?url_ver=Z39.88-2004&rft_id=1317041027&rft_val_fmt=info%3Aofi%2Ffmt%3Akev%3Amtx%3Adc&rft.title=PREPARASI+DAN+KARAKTERISASI+KALSIUM+SILIKAT+BERBAHAN+DASAR+CANGKANG+KERANG+DARAH+PADA+SUHU%0D%0A+KALSINASI+1100+oC%0D%0A&rft.creator=Neta+Oktavia%2C+1317041027&rft.subject=QC+Physics&rft.description=Kalsium+silikat+dapat+di+sintesis+dengan+menggunakan+metode+konvensional+yaitu+metode+reaksi+padatan+dengan+menggunakan+bahan+dasar+sekam+padi+sebagai+sumber+silika+dan+cangkang+kerang+darah+sebagai+sumber+CaCO3+serta+dengan+menggunakan+CaCO3+komersil+yang+kemudian+di+kalsinasi+pada+suhu+1100+oC.+Hasil+DTA%2FTGA+memperlihatkan+adanya+dekomposisi+fasa+CaCO3+dan+masih+adanya+puncak-puncak+eksotermik+yang+menandai+adanya+proses+kristalisasi+pada+sampel%2C+hal+ini+dapat+dilihat+pula+pada+pola+XRD+bahwa+adanya+trnasformasi+dari+fasa+%CE%B2-CaSiO3+menjadi+%CE%B1-CaSiO3+serta+mulai+munculnya+fasa+CaSiO3+sebagai+fasa+minor.+Spektrum+FTIR+pada+kedua+sampel+memperlihatkan+bahwa+terdapat+puncak+karakteristik+dari+gugus+fungsi+kalsium+silikat+yaitu+adanya+puncak+Si-O-Ca.+Selain+itu%2C+morfologi+SEM+memperlihatkan+partikel+berbentuk+acicular+dengan+ukuran+partikel+kalsium+silikat+cangkang+kerang+darah+lebih+kecil+yaitu+0%2C29+%C2%B5m+dibandingkan+dengan+kalsium+silikat+CaCO3+yaitu+0%2C33+%C2%B5m.%0D%0A%0D%0A%0D%0AKata+kunci%3A+Cangkang+kerang+darah%2C+kalsium+silikat%2C+%CE%B2-CaSiO3%2C+%CE%B1-CaSiO3%2C+kalsinasi.%0D%0A%0D%0A%0D%0AABSTRACT%0D%0A%0D%0A%0D%0ACalcium+silicate+can+be+synthesized+using+conventional+method+that+is+solid+state+reaction+method+by+using+rice+husk+as+source+of+silica+and+blood+cockle+shell+as+source+of+CaCO3+and+by+using+commercial+CaCO3+as+raw+materials+then+calcined+at+1100+oC.+The+DTA%2FTGA+results+show+there+are+decomposition+phase+of+CaCO3+and+exothermic+peaks+that+remarked+crystallization+process+to+the+samples%2C+it+is+considerably+noticed+on+the+X-Ray+Diffraction+there+was+a++transformation+from+%CE%B2-CaSiO3+to+%CE%B1-CaSiO3+phase+and+emergence+of++CaSiO3+phase+as+minor+phase.+The+FTIR+spectrum+of+both+samples+show+that+there+was+a+characteristic+peaks+of+the+functional+group+present+in+the+calcium+silicate+that+is+Si-O-Ca+peak.+Afterward%2C+SEM+morphology+shows+particle+of+acicular+shaped+and+that+size+particle+of+blood+cockle+shells+calcium+silicate+is+smaller+that+is+0.29+%CE%BCm+compared+with+CaCO3+calcium+silicate++size+is+0.33+%CE%BCm.%0D%0A%0D%0AKeywords%3A+Blood+cockle+shells%2C+calcium+silicate%2C+%CE%B2-CaSiO3%2C+%CE%B1-CaSiO3%2C+calcination.%0D%0A%0D%0A&rft.publisher=FAKULTAS+MATEMATIKA+DAN+ILMU+PENGETAHUAN+ALAM+&rft.date=2018-06-26&rft.type=Skripsi&rft.type=NonPeerReviewed&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F32046%2F1%2FABSTRAK.pdf&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F32046%2F2%2FSKRIPSI%2520TANPA%2520BAB%2520PEMBAHASAN.pdf&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F32046%2F3%2FSKRIPSI%2520FULL.pdf&rft.identifier=++Neta+Oktavia%2C+1317041027++(2018)+PREPARASI+DAN+KARAKTERISASI+KALSIUM+SILIKAT+BERBAHAN+DASAR+CANGKANG+KERANG+DARAH+PADA+SUHU+KALSINASI+1100+oC.++FAKULTAS+MATEMATIKA+DAN+ILMU+PENGETAHUAN+ALAM+%2C++UNIVERSITAS+LAMPUNG.+++++&rft.relation=http%3A%2F%2Fdigilib.unila.ac.id%2F32046%2F