%T STUDI PENAMBAHAN ASAP CAIR TEMPURUNG KELAPA GRADE 2 SEBAGAI
INHIBITOR KERAK KALSIUM SULFAT (CaSO4) MENGGUNAKAN METODE
SEEDED EXPERIMENT
%X Pembentukan kerak CaSO4 dalam pipa-pipa industri terutama pada industri minyak dan gas
dapat menimbulkan masalah yang cukup serius. Oleh karena itu,dalam penelitian ini telah
dilakukan pengujian inhibitor asap cair tempurung kelapa Grade 2 pada kerak kalsium sulfat
(CaSO4) menggunakan metode penambahan bibit kristal (seeded experiment) pada
konsentrasi larutan pertumbuhan CaSO4 sebesar 0,050; 0,075; 0,100; dan 0,125 M serta
variasi penambahan inhibitor dari 50, 150, 250 dan 350 ppm. Efektifitas tertinggi terjadi pada
konsentrasi dengan larutan pertumbuhan kristal CaSO4 0,050 M dan konsentrasi inhibitor
yang ditambahkan sebesar 350 ppm, diperoleh persen efektivitas sebesar 172,84%.
Berdasarkan analisis menggunakan scanning electronmicroscopy (SEM) dan X-Ray
Diffraction (XRD) menunjukkan bahwa kerak CaSO4 tanpa penambahan inhibitor berukuran
besar dan terdiri dari kristal fasa gypsum dan basanit sedangkan dengan penambahan
inhibitor, kerak CaSO4 menjadi berukuran kecil dan terdiri dari kristal fasa basanit, gypsum
dan sedikit anhidrit. Analisis kuantitatif menggunakan particle size analyzer (PSA)
menunjukkan bahwa distribusi ukuran partikel menjadi lebih kecil dengan adanya
penambahan inhibitor berdasarkan nilai rata-rata (mean) ukuran partikel yaitu dari 16,84
menjadi 0,353 ?m.
Kata kunci : Asap cair, CaSO4, kerak, inhibitor.

ABSTRACK

Scale formation in the industrial pipes, especially on gas and oil industry can lead to some
serious problems. Therefore in this study, it has been tested inhibitor of liquid smoke grade 2
to calcium sulfate (CaSO4) scale by using seeded experiment method in the concentration of
CaSO4 growth solutions of 0.050; 0.075; 0.100; and 0.125 M and variation of inhibitor added
from 50, 150, 250, and 350 ppm. The highest effectivity occurred at 0.05 M concentration of
CaSO4 crystal growth solution and 350 ppm inhibitor concentration added with percent
effectivity of 172.84%. Based on analysis using Scanning Electron Microscopy (SEM) and
X-Ray Diffraction (XRD) showed that without the addition of inhibitor, CaSO4 scale was
large and consisted of gypsum and basannite phase crystals while with the addition of
inhibitor, the CaSO4 scale became small and consisted of basannite, gypsum and a little
anhydrite. Quantitative analysis using Particle Size Analyzer (PSA) showed that particle size
distribution became smaller with the addition of inhibitor based on mean value from 16.84 to
0.353 ?m.
Keyword : Liquid smoke, CaSO4, scale, inhibitor.