        abstract = {Pada penelitian ini telah dilakukan sintesis dan karakterisasi karbon aktif dari
tempurung kelapa sawit secara aktivasi fisika (CAF) dan aktivasi kimia (CAK)
serta dilanjutkan dengan pelapisan magnetit pada CAF dan CAK sehingga
didapatkan masing-masing karbon aktif fisika magnet (CAFM) dan karbon aktif
kimia magnet (CAKM) yang bertujuan untuk mengetahui karakterisasi dan
kemampuan adsorpsinya terhadap zat warna metilen biru. Proses aktivasi fisika
dilakukan pada suhu 700 oC dan aktivasi kimia dilakukan dengan menggunakan
aktivator H3PO4, serta penambahan senyawa FeSO4.7H2O dalam proses pelapisan
magnetit. Karakterisasi pada karbon aktif dilakukan dengan menggunakan XRD
untuk mengidentifikasi kristalinitas, SEM-EDX untuk mengetahui morfologi
permukaan dan mengidentifikasi komposisi unsur, serta BET surface area untuk
mengetahui pola isoterm adsorpsi-desorpsi dan mengetahui luas permukaan
adsorben. Uji adsorpsi karbon aktif terhadap metilen biru bertujuan untuk
mengetahui volume dan pH optimum, serta model kinetika dan pola isoterm
adsorpsinya. Adsorpsi metilen biru 10 mg L-1 dengan dosis adsorben sebanyak
0,05 g optimum pada rentang volume 20-30 mL. Hasil pH optimum pada
adsorben diperoleh pada pH 8 dan waktu kontak optimum diperoleh selama 120
menit. Data kinetika adsorpsi metilen biru pada CAF, CAK, CAFM, dan CAKM
cenderung mengikuti model kinetika pseudo orde dua dengan nilai k2 masingmasing
191,104; 361,637; 325,150; dan 106,510 g mmol-1 menit-1. Isoterm
adsorpsi metilen biru pada CAF, CAK, CAFM, dan CAKM cenderung mengikuti
model isoterm Freundlich dengan nilai koefisien korelasi sebesar 0,995.
Kata kunci: Adsorpsi, karbon aktif, tempurung kelapa sawit, pelapisan magnetit,
metilen biru.

ABSTRACT

In this study, activated carbon form palm oil shell has been synthesized and
characterized by physical activation (CAF) and chemical activation (CAK) and
then continued with magnetite coating on CAF and CAK so that magnetite
physical activated carbon (CAFM) and magnetite chemical activated carbon
(CAKM) were produced which aims to know the characterization and the
adsorption capability of methylene blue. The physical activation process is done
at temperature of 700 oC and chemical activation is done by using H3PO4
activator, also by addition FeSO4.7H2O compound on magnetite coating process.
The characterization of activated carbon has been characterized using XRD to
identify the crystallinity, SEM-EDX to determine the surface morphology and to
identify element, also BET surface area to determine adsorption-desorption
isotherm pattern and to determine the adsorbent surface area. The adsorption test
of activated carbon in adsorbing 10 mg L-1 methylene blue with an adsorben dose
of 0,05 g was optimum in the volume range 20-30 mL. The result of the optimum
pH on adsorben was obtained at pH 8 and the optimum contact time was obtained
at 120 minutes. The adsorption kinetics data of methylene blue on CAF, CAK,
CAFM, and CAKM tend to follow the model of pseudo second order with k2
values repeally 191,104; 361,637; 325,150; and 106,510 g mmol-1 min-1. The
adsorption isotherm of methylene blue on CAF, CAK, CAFM, and CAKM tend to
follow the model of Freundlich isotherms with correlation coefficient was 0,995.
Keywords: Adsorption, activated carbon, palm oil shell, magnetite coating,
methylene blue.}
}