title: UJI AKTIVITAS NANOKATALIS Ni0,65Cu0,35Fe2O4 UNTUK KONVERSI
NANOSELULOSA KULIT PISANG KEPOK (Musa paradisiaca L.)
MENJADI GULA ALKOHOL DI BAWAH IRRADIASI SINAR UV
ispublished: pub
subjects: Q
subjects: QD
full_text_status: restricted
abstract: Pada penelitian ini, katalis Ni0,65Cu0,35Fe2O4 telah dipreparasi menggunakan
metode sol-gel dan pektin sebagai agen pengemulsi, dilanjutkan dengan kalsinasi
pada temperatur 600 °C. Katalis ini digunakan untuk uji konversi selulosa
menjadi gula alkohol menggunakan sinar UV serta aliran gas H2 10 ml/menit
dengan waktu konversi 15, 30, 45, dan 60 menit. Analisis keasaman dengan
metode gravimetri, menunjukkan bahwa katalis Ni0,65Cu0,35Fe2O4 memiliki
keasaman 1,34 mmol piridin/gram. Berdasarkan metode Fourier Transform Infra
Red (FTIR) situs asam Lewis lebih dominan. Hasil analisis difraksi sinar-X
(XRD) katalis terdiri dari beberapa fasa kristal yakni fasa NiFe2O4, CuFe2O4,
CuO, dan NiO. Hasil analisis morfologi katalis dengan metode Transmission
Electron Microscop (TEM) menunjukkan morfologi permukaan yang heterogen.
Hasil analisis energi senjang dengan metode Diffuse Reflectance Spectroscopy
(DRS) menunjukkan nilai energi senjang sebesar 1,5 eV. Uji Fehling
mengindikasikan bahwa hasil terbaik diperoleh menggunakan aliran gas H2 10
ml/menit dengan waktu konversi 60 menit. Analisis menggunakan High
Performance Liquid Chromatography (HPLC) menunjukkan bahwa katalis
Ni0,65Cu0,35Fe2O4 hanya mampu mengkonversi nanoselulosa menjadi gula
reduksi.
Kata Kunci : nanoselulosa, nanokatalis, gula alkohol.

ABSTRACT

On this research, catalyst of Ni0.65Cu0,35Fe2O4 had been prepared with using solgel
method and pectin as an emulsifying agent, followed by calcination at
temperature 600 °C. The catalyst is used for converting nanocellulose into sugar
alcohols under UV rays with the exposure time of 15, 30, 45, and 60 minutes.
Analysis of acidity with gravimetric method, showed that the catalyst
Ni0.65Cu0,35Fe2O4 have the acidity 1,34 mmol piridin/gram. Method based on
Fourier Transform Infra Red (FTIR) lewis acid site is more dominant. The results
of the analysis of the X-ray difraction (XRD) catalyst consists of several crystal
phase i.e. phase NiFe2O4, CuFe2O4, CuO, and NiO. The results of catalyst
morphology analysis with transmission electron microscope (TEM) method
showed heterogeneous surface morphology. The results of the analysis of gap
energy using the Diffuse Reflectance Spectroscopy (DRS) method show the value
of the gap energy of 1,5 eV. The fehling test indicated that the best results were
obtained using a 10 mL H2 gas flow per minute with a convertion time of 60
minutes. Analysis using high performance liquid chromatography (HPLC)
showed that the Ni0.65Cu0,35Fe2O4 catalyst was only able to convert nanocellulose
into reducing sugar.
Keywords : nanocelulose, nanocatalyst, sugar alcholol.
date: 2018-10-09
date_type: published
publisher: FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM UNIVERSITAS LAMPUNG BANDAR LAMPUNG 2018
place_of_pub: UNIVERSITAS LAMPUNG
citation:    ERWIN SIMARMATA , 1417011035  (2018) UJI AKTIVITAS NANOKATALIS Ni0,65Cu0,35Fe2O4 UNTUK KONVERSI NANOSELULOSA KULIT PISANG KEPOK (Musa paradisiaca L.) MENJADI GULA ALKOHOL DI BAWAH IRRADIASI SINAR UV.  FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM UNIVERSITAS LAMPUNG BANDAR LAMPUNG 2018, UNIVERSITAS LAMPUNG.     
document_url: http://digilib.unila.ac.id/33829/1/ABSTRAK.pdf
document_url: http://digilib.unila.ac.id/33829/2/SKRIPSI%20FULL.pdf
document_url: http://digilib.unila.ac.id/33829/3/SKRIPSI%20TANPA%20BAB%20PEMBAHASAN.pdf