?url_ver=Z39.88-2004&rft_val_fmt=info%3Aofi%2Ffmt%3Akev%3Amtx%3Adc&rft.title=ANALISIS+KETAHANAN+LELAH+BAJA+KARBON+AISI+1045+YANG+DITEMPERING&rft.creator=Hendra+Prawira%2C+0815021033&rft.subject=+&rft.subject=Karya+Karya+Umum+%3D+000&rft.description=ABSTRAK+(In)%0D%0A%0D%0ABaja+karbon+sedang+merupakan+material+yang+banyak+diproduksi+dan+digunakan+dalam+dunia+industri.+Baja+karbon+AISI+1045+adalah++salah+satu+jenis+baja+karbon+yang+banyak++digunakan+sebagai+bahan+pembuat+poros+untuk+komponen+mesin.+%0D%0APada+penggunaannya%2C+poros+beroperasi+menerima+beban+dinamik+dalam+waktu+yang+lama%2C+sehingga+rentan+mengalami+kegagalan++saat+digunakan+akibat+mengalami+kegagalan+lelah.+Ketahanan++lelah+suatu+baja+dipengaruhi+sifat+mekanis+dan+struktur+mikro+baja+tersebut.%0D%0APerlakuan+panas+merupakan+salah+satu+cara+yang+dilakukan+untuk+merubah+sifat+mekanis+dan+struktur+mikro+suatu+baja+dan+salah+satu+jenis+perlakuan+panas+yang+dapat+diberikan+pada+baja+AISI+1045+adalah+metode+tempering+yang+dapat+%0D%0Ameningkatkan+keuletan+baja+tersebut.+Untuk+mengetahui+nilai+ketahanan+lelah+baja+AISI+1045+yang+telah+diberikan+perlakuan+panas+tempering%2C+dilakukan+dengan+melakukan+pengujian+ketahanan+lelah+menggunakan+alat+rotary+%0D%0Abending.+Adapun+metode+pengujian+yang+dilakukan+adalah+memberikan+variasi+pembebanan+sebesar+20%25%2C+30%25%2C+40%25%2C+50%25+dan+60%25+dari+nilai+tegangan+tarik+maksimum+dari+baja++tersebut%2C+serta+melakukan+pengamatan+makroskopik+tehadap+pola+perpatahan+yang+terjadi+pada+spesimen+pengujian.%0D%0AHasil+pengujian+menunjukkan+nilai+ketahanan+lelah+maksimum+yang+dicapai+adalah+1.107.150+siklus+pada+pembebanan+30%25%2C++disertai+patah+getas+pada+pembebanan+50%25+dan+60%25%2C+patah+ulet-getas+pada+pembebanan%2C+40%25%2C+dan+patah+ulet+pada+pembebanan+30%25.%0D%0A%0D%0AABSTRACT+(En)%0D%0A%0D%0ASteel+is+a+material+that+is+widely+used+in+the+industrial+world.+One+of+the+widely+%0D%0Aused++type++of++steel++is++AISI++1045++steel++as++the++material++of++the++shaft++for++the++engine+%0D%0Acomponents++maker.++On++its++use%2C++the++axis++of++operation++receive++dynamic++load++in++a+%0D%0Along++time%2C++so+++that++the++vulnerable++experienced++a++failure++when++used++due++to+%0D%0Aexperiencing++fatigue++failure.++A++weary++resilience++steel++affected++by++mechanical+%0D%0Aproperties+and+microstructure+of+the+steel.+%0D%0AHeat+treatment+is+one+way+that+can+be+done+to+change+the+mechanical+properties+%0D%0Aand+microstructure+of+steel+and+one+of+a+kind+of+heat+treatment+that+can+be+given+%0D%0Aon+the+steel+AISI+1045+is+tempering++method+which+can+improve+the+steel+ductility.+%0D%0ATo++find++out+the++fatigue++strength++value++of++AISI++1045++steel++that++has++been++granted+%0D%0Atempering++heat++treatment%2C++can++be++done++by++performing++testing++using++the++rotary+%0D%0Abending+testing+machine.+As+for+the+testing+method+is+done+by+giving+the+variation+%0D%0Aof+load+by+20%25%2C+30%25%2C+40%25%2C+50%25+and+60%25+of+the+ultimate+tensile+strength+value%2C+%0D%0Aas+well+as+do+macroscopic+observations+by+taking+action+against+the+pattern+of+the+%0D%0Afracture+that+occurs+in+the+test+specimens.+%0D%0AThe++test++results++show++that+the++value++of++the++maximum++fatigue++strength++is++able++to+%0D%0Aaccomplish++is++1.107.150++cycle++on++the++30%25++loading%2C++accompanied++by++brittle+%0D%0Afracture+on+the+50%25+and+60%25+loading%2C+ductile-brittle+fracture+on+the+40%25+loading+%0D%0Aand+ductile+fracture+on+the+30%25+loading.&rft.publisher=Fakultas+Teknik&rft.date=2014-10-02&rft.type=Skripsi&rft.type=NonPeerReviewed&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F3759%2F1%2FABSTRAK.pdf&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F3759%2F2%2FABSTRACT%2520english.pdf&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F3759%2F3%2FCOVER%2520dalam.pdf&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F3759%2F4%2FHalaman%2520Persetujuan.pdf&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F3759%2F5%2FHalaman%2520Pengesahan.pdf&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F3759%2F6%2FPERNYATAAN%2520PENULIS.pdf&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F3759%2F7%2FRIWAYAT%2520HIDUP.pdf&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F3759%2F8%2FPersembahan.pdf&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F3759%2F9%2FMOTTO.pdf&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F3759%2F10%2FSanwacana.pdf&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F3759%2F11%2FDAFTAR%2520ISI.pdf&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F3759%2F12%2FDAFTAR%2520TABEL.pdf&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F3759%2F13%2FDAFTAR%2520Lampiran.pdf&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F3759%2F14%2FDAFTAR%2520Gambar.pdf&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F3759%2F15%2FBAB%2520I.pdf&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F3759%2F16%2FBAB%2520II.pdf&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F3759%2F17%2FBAB%2520III.pdf&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F3759%2F18%2FBab%2520IV.pdf&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F3759%2F19%2FBAB%2520V.pdf&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F3759%2F20%2FDaftar%2520Pustaka.pdf&rft.identifier=++Hendra+Prawira%2C+0815021033++(2014)+ANALISIS+KETAHANAN+LELAH+BAJA+KARBON+AISI+1045+YANG+DITEMPERING.++Fakultas+Teknik%2C+Universitas+Lampung.+++++&rft.relation=http%3A%2F%2Fdigilib.unila.ac.id%2F3759%2F