<> "The repository administrator has not yet configured an RDF license."^^ . <> . . "UJI AKTIVITAS NANOKATALIS 3%V/LaCrO3 PADA KONVERSI \r\nNANOSELULOSA DARI KULIT PISANG KEPOK (Musa paradisiaca L.) \r\nMENJADI GULA ALKOHOL DI BAWAH IRRADIASI SINAR UV "^^ . "Productions of alcohol sugar an increasingly being developed until now. This is because \r\nalcohol sugar can be used as an alternative sweetener for diabetics. Alcohol sugar is \r\nproduced from cellulose through catalytic conversion. In this research, alcohol sugar was\r\nproduced from cellulose that extracted from banana peels. This production was carried \r\nout using 3%V/LaCrO3 nanocatalyst under UV irradiation. Nanocatalyst was\r\ncharacterized through XRD, TEM, SEM-EDX, FTIR and DRS UV-Vis. XRD analysis \r\nshowed that crystallite size of nanocatalyst is around 80.48 nm. TEM analysis showed\r\nthat particles size of nanocatalyst is 75 nm. SEM analysis showed that nanocatalyst \r\nagglomeration occurs and the particle size is not homogeneous, while EDX analysis \r\nshowed that nanocatalyst has a ratio of La, Cr, and V elements that is accordance with the \r\nLaCr1-xVxO3 formula. Then, FTIR analysis showed that the wavenumber of 600-900 cm-1\r\nindicated that the La-O-Cr bond was formed. In addition, UV-Vis Diffuse-reflectance \r\nSpectroscopy analysis showed that the band gap energy of the nanocatalyst is 2,6 eV. \r\nThe result of nanocellulose conversion was then analyzed through Fehling test, DNS, and \r\nHPLC. Both Fehling and DNS tests showed that reducing sugar was formed. However, \r\nHPLC analysis showed the result of alcohol sugar were not completely identified.\r\nKeywords : Nanocatalyst, Nanocellulose, Alcohol sugar.\r\n\r\nProduksi gula alkohol semakin terus dikembangkan sampai saat ini. Hal ini dikarenakan \r\ngula alkohol dapat digunakan sebagai pemanis alternative bagi penderita diabetes. Gula \r\nalkohol diperoleh dari selulosa melalui konversi katalitik. Dalam penelitian ini, produksi \r\ngula alkohol berasal dari selulosa yang diekstrak dari kulit pisang. Produksi ini dilakukan \r\nmenggunakan nanokatalis 3%V/LaCrO3 dibawah irradiasi sinar UV. Nanokatalis \r\ndikarakterisasi menggunakan XRD, TEM, SEM-EDX, FTIR, dan DRS UV-Vis. Hasil \r\nanalisis XRD menunjukkan bahwa ukuran kristalin nanokatalis sekitar 80,48 nm. \r\nAnalisis TEM menunjukkan bahwa ukuran partikel nanokatalis adalah 75 nm. Hasil \r\nanalisis SEM menunjukkan bahwa terjadi aglomerasi dan ukuran partikel nanokatalis \r\nyang tidak homogen, sedangkan hasil analisis EDX menunjukkan bahwa pada nanokatalis \r\nterdapat unsur La, Cr, dan V, hal itu merupakan perbedaan formula dari LaCr1-xVxO3. \r\nKemudian, hasil analisis FTIR menunjukkan bahwa pada bilangan gelombang 600-900 \r\ncm-1 menandakan bahwa terbentuknya ikatan La-O-Cr. Tambahan hasil dari analisis \r\nDRS UV-Vis mennjukkan bahwa energi celah pita dari nanokatalis adalah 2,6 eV. \r\nNanoselulosa yang telah dikonversi dengan nanokatalis selanjutnya dikarakterisasi \r\ndengan Uji Fehling, DNS dan HPLC. Kedua uji fehling dan DNS menunjukkan bahwa \r\ntelah terbentuknya gula pereduksi. Namun demikian, pada hasil analisis HPLC \r\nmenunjukkan terbentuknya gula alkohol yang tidak teridentifikasi secara sempurna.\r\nKata Kunci : Nanokatalis, Nanoselulosa, Gula alkohol.\r\n"^^ . "2019" . . . . . "Fakultas Matematika dan Ilmu Pengetahuan Alam"^^ . . . . . . . "1517011093"^^ . "Elsina ‘Azmi"^^ . "1517011093 Elsina ‘Azmi"^^ . . . . . . "UJI AKTIVITAS NANOKATALIS 3%V/LaCrO3 PADA KONVERSI \r\nNANOSELULOSA DARI KULIT PISANG KEPOK (Musa paradisiaca L.) \r\nMENJADI GULA ALKOHOL DI BAWAH IRRADIASI SINAR UV (File PDF)"^^ . . . "3. SKRIPSI FULL TANPA BAB PEMBAHASAN.pdf"^^ . . . "UJI AKTIVITAS NANOKATALIS 3%V/LaCrO3 PADA KONVERSI \r\nNANOSELULOSA DARI KULIT PISANG KEPOK (Musa paradisiaca L.) \r\nMENJADI GULA ALKOHOL DI BAWAH IRRADIASI SINAR UV (File PDF)"^^ . . . "UJI AKTIVITAS NANOKATALIS 3%V/LaCrO3 PADA KONVERSI \r\nNANOSELULOSA DARI KULIT PISANG KEPOK (Musa paradisiaca L.) \r\nMENJADI GULA ALKOHOL DI BAWAH IRRADIASI SINAR UV (File PDF)"^^ . . . "1. ABSTRAK.pdf"^^ . . . "UJI AKTIVITAS NANOKATALIS 3%V/LaCrO3 PADA KONVERSI \r\nNANOSELULOSA DARI KULIT PISANG KEPOK (Musa paradisiaca L.) \r\nMENJADI GULA ALKOHOL DI BAWAH IRRADIASI SINAR UV (Other)"^^ . . . . . . "indexcodes.txt"^^ . . . "UJI AKTIVITAS NANOKATALIS 3%V/LaCrO3 PADA KONVERSI \r\nNANOSELULOSA DARI KULIT PISANG KEPOK (Musa paradisiaca L.) \r\nMENJADI GULA ALKOHOL DI BAWAH IRRADIASI SINAR UV (Other)"^^ . . . . . . "UJI AKTIVITAS NANOKATALIS 3%V/LaCrO3 PADA KONVERSI \r\nNANOSELULOSA DARI KULIT PISANG KEPOK (Musa paradisiaca L.) \r\nMENJADI GULA ALKOHOL DI BAWAH IRRADIASI SINAR UV (Other)"^^ . . . . . . "indexcodes.txt"^^ . . . "UJI AKTIVITAS NANOKATALIS 3%V/LaCrO3 PADA KONVERSI \r\nNANOSELULOSA DARI KULIT PISANG KEPOK (Musa paradisiaca L.) \r\nMENJADI GULA ALKOHOL DI BAWAH IRRADIASI SINAR UV (Other)"^^ . . . . . . "lightbox.jpg"^^ . . . "UJI AKTIVITAS NANOKATALIS 3%V/LaCrO3 PADA KONVERSI \r\nNANOSELULOSA DARI KULIT PISANG KEPOK (Musa paradisiaca L.) \r\nMENJADI GULA ALKOHOL DI BAWAH IRRADIASI SINAR UV (Other)"^^ . . . . . . "preview.jpg"^^ . . . "UJI AKTIVITAS NANOKATALIS 3%V/LaCrO3 PADA KONVERSI \r\nNANOSELULOSA DARI KULIT PISANG KEPOK (Musa paradisiaca L.) \r\nMENJADI GULA ALKOHOL DI BAWAH IRRADIASI SINAR UV (Other)"^^ . . . . . . "medium.jpg"^^ . . . "UJI AKTIVITAS NANOKATALIS 3%V/LaCrO3 PADA KONVERSI \r\nNANOSELULOSA DARI KULIT PISANG KEPOK (Musa paradisiaca L.) \r\nMENJADI GULA ALKOHOL DI BAWAH IRRADIASI SINAR UV (Other)"^^ . . . . . . "small.jpg"^^ . . . "UJI AKTIVITAS NANOKATALIS 3%V/LaCrO3 PADA KONVERSI \r\nNANOSELULOSA DARI KULIT PISANG KEPOK (Musa paradisiaca L.) \r\nMENJADI GULA ALKOHOL DI BAWAH IRRADIASI SINAR UV (Other)"^^ . . . . . . "UJI AKTIVITAS NANOKATALIS 3%V/LaCrO3 PADA KONVERSI \r\nNANOSELULOSA DARI KULIT PISANG KEPOK (Musa paradisiaca L.) \r\nMENJADI GULA ALKOHOL DI BAWAH IRRADIASI SINAR UV (Other)"^^ . . . . . . "UJI AKTIVITAS NANOKATALIS 3%V/LaCrO3 PADA KONVERSI \r\nNANOSELULOSA DARI KULIT PISANG KEPOK (Musa paradisiaca L.) \r\nMENJADI GULA ALKOHOL DI BAWAH IRRADIASI SINAR UV (Other)"^^ . . . . . . "UJI AKTIVITAS NANOKATALIS 3%V/LaCrO3 PADA KONVERSI \r\nNANOSELULOSA DARI KULIT PISANG KEPOK (Musa paradisiaca L.) \r\nMENJADI GULA ALKOHOL DI BAWAH IRRADIASI SINAR UV (Other)"^^ . . . . . . "lightbox.jpg"^^ . . . "UJI AKTIVITAS NANOKATALIS 3%V/LaCrO3 PADA KONVERSI \r\nNANOSELULOSA DARI KULIT PISANG KEPOK (Musa paradisiaca L.) \r\nMENJADI GULA ALKOHOL DI BAWAH IRRADIASI SINAR UV (Other)"^^ . . . . . . "UJI AKTIVITAS NANOKATALIS 3%V/LaCrO3 PADA KONVERSI \r\nNANOSELULOSA DARI KULIT PISANG KEPOK (Musa paradisiaca L.) \r\nMENJADI GULA ALKOHOL DI BAWAH IRRADIASI SINAR UV (Other)"^^ . . . . . . "preview.jpg"^^ . . . "UJI AKTIVITAS NANOKATALIS 3%V/LaCrO3 PADA KONVERSI \r\nNANOSELULOSA DARI KULIT PISANG KEPOK (Musa paradisiaca L.) \r\nMENJADI GULA ALKOHOL DI BAWAH IRRADIASI SINAR UV (Other)"^^ . . . . . . "medium.jpg"^^ . . . "UJI AKTIVITAS NANOKATALIS 3%V/LaCrO3 PADA KONVERSI \r\nNANOSELULOSA DARI KULIT PISANG KEPOK (Musa paradisiaca L.) \r\nMENJADI GULA ALKOHOL DI BAWAH IRRADIASI SINAR UV (Other)"^^ . . . . . . "small.jpg"^^ . . "HTML Summary of #55673 \n\nUJI AKTIVITAS NANOKATALIS 3%V/LaCrO3 PADA KONVERSI \nNANOSELULOSA DARI KULIT PISANG KEPOK (Musa paradisiaca L.) \nMENJADI GULA ALKOHOL DI BAWAH IRRADIASI SINAR UV \n\n" . "text/html" . . . " " . .