%A 1517011066 FATRY SINJIA
%T STUDI TRANSPOR FENOL MENGGUNAKAN SENYAWA CARRIER
Co-EDAF(Copoli Eugenol-Dialil Ftalat) 8% DENGAN METODE Polymer 
Inclusion Membrane (PIM)
%X Telah dilakukan Sintesis kopoli eugenol-dialil ftalat (Co-EDAF) 8% yang 
berfungsi sebagai senyawa carrier. Co-EDAF 8% merupakan salah satu 
komponen dalam pembuatan polymer inclusion membrane (PIM). Selanjutnya 
senyawa Co-EDAF 8% dikarakterisasi menggunakan Fourier-Transform Infrared 
Spectroscopy (FTIR) serta dilakukan uji transpor fenol menggunakan metode PIM 
dengan beberapa parameter diantaranya pH fasa sumber, konsentrasi fasa 
penerima, ketebalan membran yang digunakan, waktu transpor serta uji transpor 
pada limbah buatan. Karakterisasi membran dilakukan dengan menggunakan 
Scanning Electron Microscopy (SEM) untuk mengetahui morfologi permukaan 
membran dan FTIR untuk mengetahui gugus fungsi. Senyawa hasil sintesis 
berbentuk serbuk, berwarna orange dan larut terhadap kloroform, dietil eter dan 
tetrahidrofuran. Hasil FTIR menunjukkan hilangnya gugus vinil pada bilangan
gelombang 995,27 cm-1
dan gugus alil pada bilangan gelombang 1636 cm-1
. Hasil 
uji transpor fenol menunjukkan bahwa PIM menggunakan senyawa carrier Co?EDAF 8% mampu mentranspor fenol sebesar 82,42 % pada pH 5,5 di fasa 
sumber, konsentrasi NaOH 0,1 M di fasa penerima, ketebalan membran 0,27 mm 
(tipe membran t54) dengan waktu transpor selama 48 jam. Uji transpor fenol pada 
limbah buatan dihasilkan bahwa membran PIM selektif terhadap recovery fenol, 
Kata kunci : Co-EDAF, Dialil Ftalat, Fenol, PIM

Synthesis of copoly eugenol-diallyl phthalate (Co-EDAF) 8% has been carried out 
as a carrier compound. Co-EDAF 8% is one component in the creation of 
polymer inclusion membranes (PIMs). Furthermore Co-EDAF 8 % compounds 
were characterized using the Fourier-Transform Infrared Spectroscopy (FTIR) and 
phenol transport tests were carried out using the PIM method with some 
parameter among them are source phase pH, receiving phase concentration, the 
thickness of membrane that used in this research, time transport, and test metal 
transport. Membrane characterization is carried out using Scanning Electron 
Microscopy (SEM) to know the membrane surface morphology and FTIR to know 
functional groups. The synthesis product result was an orange powder which 
dissolves with chloroform, diethyl ether and tetrahydrofuran. The results by FTIR
showed the loss of vinyl and allyl groups at wave number 995.27 cm-1
and 1636 
cm-1
respectively. Transport phenol study showed that the PIM using an Co?EDAF 8% as a carrier compound was able to transport phenols up to 82.42% at 
pH 5.5 in the source, the concentration of 0.1 M NaOH in the receiver with a 
membrane thickness 0,27 (type membrane t54) with time transport until 48 hours. 
Transport phenol test in synthetic wastes showed that PIM membrane was 
selective for the recovery of phenol. 
Keywords: Co-EDAF, Dialyl Phthalate, Phenol, PIM