title: PENGARUH ABU SEKAM SEBAGAI BAHAN PENGGANTI SEJUMLAH
SEMEN TERHADAP KUAT TEKAN DAN KUAT LENTUR PADA
BETON REAKTIF (REACTIVE POWDER CONCRETE)
ispublished: pub
subjects: 620
subjects: 690
full_text_status: restricted
abstract: Kualitas beton dapat ditentukan dari komposisi adukan, jenis bahan, dan cara
perawatan. Beton reaktif adalah salah satu jenis beton mutu tinggi yang komposisinya
mengandung banyak semen dan bahan sangat halus lainnya serta di rawat dengan
cara pemanasan. Abu sekam padi yang mengandung senyawa silika juga berpotensi
untuk bahan adukan beton reakif.
Penelitian ini dilakukan pada variasi prosentase abu sekam sebagai pengganti
sejumlah semen (0%, 10%, 20%, 30%, dan 40%) dan cara perawatan benda uji
prisma 40 x 40 x 160 mm (pemanasan suhu pada 180o, perawatan uap air panas pada
90 o, dan perendaman dalam air). Pengujian kuat lentur pada umur 7 hari dan kuat
tekan pada umur 7 hari dan 28 hari
Hasil pengujian menunjukan bahwa kuat lentur optimum 16, 48 MPa
diperoleh dari komposisi 10% abu sekam dan perawatan uap air panas. Kuat tekan
optimum juga diperoleh dari perawatan uap air panas, namun pada komposisi 30%
abu sekam, yaitu 37,54 MPa umur 7 hari dan 54,44 MPa umur 28 hari. Dengan
demikian abu sekam dapat digunakan untuk bahan pengganti sebagian semen dalam
komposisi beton reaktif dengan perawatan uap air panas.
Kata kunci : beton mutu tinggi, beton reaktif , reactive powder concrete, abu sekam,
kuat tekan, kuat lentur.
The quality of concrete can be determined by mixture composition, type of
material, and treatment method. Reactive powder concrete is one of high quality
performance concrete containing a lot of cement and fine powders which needs a heat
treatment. Rice husk ash containing silica compounds has a potential to be used in
concrete mixtures.
This research was conducted with the percentage variation of rice husk ash
instead of cement (0%, 10%, 20%, 30%, and 40%) and the treatments method were
applied on prism samples with dimension of 40 x 40 x 160 mm (180o heating
temperature, 90 o steam treatment, and water treatment). The flexural strength test
was conducted at 7 days and the compressive strength was tested at 7 days and 28
days.
The test results show that the optimum flexural strength was 16.48 MPa,
obtained from the composition of 10% rice husk ash with steam treatment. The
optimum compressive strength was also obtained by the steam treatment, but on the
composition of 30% rice husk ash, which are 37.54 MPa at 7 days and 54.44 MPa at
28 days. It is concluded that rice husk ash can be used as a substitute for some cement
in the composition of reactive powder concrete with steam treatment.
Keywords: reactive powder concrete, rice husk ash, compressive strength, flexural
strength.
date: 2019
date_type: published
publisher: FAKULTAS TEKNIK
place_of_pub: UNIVERSITAS LAMPUNG
citation:   Mufidah Aulia Annisa, 1415011098  (2019) PENGARUH ABU SEKAM SEBAGAI BAHAN PENGGANTI SEJUMLAH SEMEN TERHADAP KUAT TEKAN DAN KUAT LENTUR PADA BETON REAKTIF (REACTIVE POWDER CONCRETE).  FAKULTAS TEKNIK, UNIVERSITAS LAMPUNG.     
document_url: http://digilib.unila.ac.id/56400/1/ABSTRAK.pdf
document_url: http://digilib.unila.ac.id/56400/2/SKRIPSI%20FULL.pdf
document_url: http://digilib.unila.ac.id/56400/3/SKRIPSI%20TANPA%20BAB%20PEMBAHASAN.pdf