PENGARUH LAMA PEMANASAN, PENDINGINAN SECARA CEPAT DAN TEMPERING TERHADAP SIFAT TANGGUH BAJA PEGAS DAUN AISI NO. 9260
ABSTRAK Telah dilakukan penelitian mengenai pengaruh pemanasan, pendinginan secara cepat, dan tempering terhadap sifat tangguh baja pegas daun AISI No. 9260. Penelitian ini dilakukan untuk mengetahui sifat tangguh baja pegas daun yang biasanya dipakai pada kendaraan bermotor berdasarkan proses pemanasan, pendinginan secara cepat menggunakan oli, dan tempering sehingga dihasilkan data tentang ketangguhan baja pegas daun. Proses pemanasan dilakukan dengan suhu 780 oC dengan waktu tahan 40 dan 60 menit yang selanjutnya didinginkan secara cepat menggunakan oli. Proses pemanasan merubah fasa baja menjadi martensit yang bersifat keras dan dilanjutkan dengan proses tempering pada suhu 400 oC dan 600 oC dengan waktu tahan 40 menit yang membuat fasa baja berubah menjadi martensit temper dan ferit, sehingga kekerasan baja menurun dan ketangguhan meningkat. Sebelum dilakukan pemanasan, nilai ketangguhan baja 0,23 J/mm2 lebih kecil dari baja yang telah diberikan proses pemanasan, pendinginan secara cepat, dan tempering yaitu sebesar 0.803 J/mm2. Kata Kunci: Baja pegas daun, tempering, quenching, ketangguhan baja (Impact), mikro struktur. ABSTRACT We have discovered the effect of heating, quenching, and tempering of leaf spring steel AISI No. 9260. It was conducted to determine the impact value of leaf springs steel that are used on motor vehicles. The heating, quenching with oil, and tempering on the impact of leaf springs steel was obtained to produce data. The steel were heated at 780 °C for 40 and 60 minutes followed with oil cooling. Heating process was changed the steel phase to hardly martensite that obtained by tempering at a temperature of 400 oC and 600 °C for 40 minutes. It was made the steel phase transformed into tempered martensite and ferrite, so the steel has hardness decreased and impact values was increased. Before that process, the impact values of steel is 0.23 J/mm2 smaller than the steel which has been given the heating, quenching, and tempering approach equal to 0.803 J/mm2. Key words: Leaf springs steel, tempering, quenching, impact test, micro structure.
PENGARUH LAMA PEMANASAN, PENDINGINAN SECARA CEPAT DAN TEMPERING TERHADAP SIFAT TANGGUH BAJA PEGAS DAUN AISI NO. 9260 (File PDF)
PENGARUH LAMA PEMANASAN, PENDINGINAN SECARA CEPAT DAN TEMPERING TERHADAP SIFAT TANGGUH BAJA PEGAS DAUN AISI NO. 9260 (Other)
HTML Summary of #5643 PENGARUH LAMA PEMANASAN, PENDINGINAN SECARA CEPAT DAN TEMPERING TERHADAP SIFAT TANGGUH BAJA PEGAS DAUN AISI NO. 9260