?url_ver=Z39.88-2004&rft_val_fmt=info%3Aofi%2Ffmt%3Akev%3Amtx%3Adc&rft.title=STUDI+TRANSPOR+FENOL+MENGGUNAKAN+METODE+POLYMER+%0D%0AINCLUSION+MEMBRANE+(PIM)+DENGAN+KOPOLI(EUGENOL-DIVINIL+%0D%0ABENZENA)+SEBAGAI+SENYAWA+CARRIER&rft.creator=DESSY+TIARA+ELVIA+NITA+SARI%2C+1417011022&rft.subject=540+Kimia+dan+ilmu+yang+berhubungan&rft.description=Fenol+merupakan+senyawa+organik+beracun%2C+berbahaya+dan+sulit+didegradasi+yang+%0D%0Abanyak+ditemukan+sebagai+polutan+di+perairan.+Penelitian+mengenai+studi+transpor+%0D%0Afenol+menggunakan+metode+Polymer+Inclusion+Membrane+(PIM)+dengan+%0D%0Akopoli(eugenol-DVB)+sebagai+senyawa+carrier+dilakukan+untuk+mengatasi+%0D%0Amasalah+tersebut.+Beberapa+parameter+yang+berpengaruh+terhadap+transpor+fenol+%0D%0Atelah+dilakukan+diantaranya+yaitu+pH+fenol+fasa+sumber%2C+konsentrasi+NaOH+fasa+%0D%0Apenerima%2C+ketebalan+membran+PIM+dan+waktu+transpor.+Sintesis+kopoli(eugenol%EF%BF%BDDVB)+dilakukan+melalui+reaksi+kopolimerisasi+antara+eugenol+dengan+divinil+%0D%0Abenzena+(DVB)+10+%25+menggunakan+katalis+BF3O(C2H5)2.+Serbuk+kopolimer+%0D%0Ayang+dihasilkan+dikarakterisasi+menggunakan+FT-IR.+Konsentrasi+fenol+setelah+%0D%0Atranspor+ditentukan+dengan+metode+spektrofotometri+UV-Vis+menggunakan+%0D%0Areagen+4-aminoantipirin+dan+absorbansinya+diukur+pada+panjang+gelombang+%0D%0A%CE%BB%3D456+nm.+Hasil+penelitian+menunjukkan+bahwa+membran+PIM+dengan+senyawa+%0D%0Acarrier+kopoli(eugenol-DVB)+mampu+mentranspor+fenol+secara+efektif+sebesar+%0D%0A89%2C40+%25+pada+kondisi+optimum%3A+pH+fenol+fasa+sumber+5%2C5%2C+konsentrasi+NaOH+0%2C1+%0D%0AM%2C+ketebalan+membran+PIM+tipe+T27+dan+waktu+transpor+selama+24+jam.+%0D%0AMembran+PIM+yang+telah+digunakan+untuk+transpor+selama+24+jam+dikarakterisasi+%0D%0Amenggunakan+SEM+dan+FT-IR+Transpor+fenol+dengan+logam+kompetitor+Cu(II)%0D%0Adan+Pb(II)+menghasilkan+konsentrasi+fenol+yang+tertranspor+lebih+kecil+%0D%0Adibandingkan+transpor+tanpa+logam+yaitu+sebesar+27%2C25+%25.+Keberadaan+logam+%0D%0Akompetitor+ini+diasumsikan+telah+menghambat+proses+fenol+untuk+tertranspor+ke+%0D%0Afasa+penerima.%0D%0AKata+kunci%3A+Kopoli(eugenol-DVB)%2C+Polymer+Inclusion+Membrane+(PIM)%2C+%0D%0Atranspor+fenol%0D%0A%0D%0A%0D%0APhenol+is+a+toxic+organic+compound%2C+dangerous+and+hardly+degradable+which+is+%0D%0Acommonly+found+as+the+waters+pollutants.+The+study+of+phenol+transport+using+the+%0D%0APolymer+Inclusion+Membrane+(PIM)+method+with+copoly(eugenol-DVB)+as+the+%0D%0Acarrier+compound+was+carried+out+to+resolve+this+problems.+Some+parameters+that+%0D%0Ainfluence+phenol+transport+have+been+investigated%2C+including+the+pH+of+the+source+%0D%0Aphase+phenol%2C+receiver+phase+NaOH+concentration%2C+PIM+membrane+thickness+and+%0D%0Atransport+time.+Synthesis+of+copoly(eugenol-DVB)+was+carried+out+using+a+%0D%0Acopolymerization+reaction+between+eugenol+with+10%25+divinylbenzene+(DVB)%2C+and%0D%0ABF3O(C2H5)2+as+the+catalyst.+The+copolymer+powder+produced+was+characterized+%0D%0Ausing+FT-IR.+The+concentration+of+phenol+after+transport+was+determined+by+UV%EF%BF%BDVis+spectrophotometry+using+4-amino+antipyrine+reagents+and+the+absorbance+was+%0D%0Ameasured+at+wavelength+%CE%BB+%3D+456+nm.+The+results+showed+that+PIM+membranes+%0D%0Awith+copoly(eugenol-DVB)+as+carrier+compounds+were+able+to+transport+phenol+%0D%0Aeffectively+by+89.40%25+at+optimum+conditions%3A+pH+of+the+source+phase+phenol+5.5%2C+%0D%0A0.1+M+NaOH+concentration%2C+T27+type+PIM+membrane+thickness+and+transport+time+%0D%0Afor+24+hours.+PIM+membranes+that+have+been+used+for+transport+for+24+hours+were+%0D%0Acharacterized+using+SEM+and+FT-IR.+Phenol+transport+with+metal+competitor+Cu+%0D%0A(II)+and+Pb+(II)+resulted+in+a+smaller+concentration+of+transported+phenol+compared+%0D%0Ato+metalless+transport+of+27.25%25.+The+existence+of+metal+as+the+competitor+is+%0D%0Aassumed+to+have+inhibited+the+phenol+process+to+be+transported+to+the+receiving+%0D%0Aphase.%0D%0AKeywords+%3A+Copoly(eugenol-DVB)%2C+Phenol+transport%2C+Polymer+Inclusion+%0D%0AMembrane+(PIM)%0D%0A&rft.publisher=Fakultas+Matematika+dan+Ilmu+Pengetahuan+Alam&rft.date=2019&rft.type=Skripsi&rft.type=NonPeerReviewed&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F56692%2F1%2FABSTRAK.pdf&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F56692%2F2%2FSKRIPSI%2520FULL.pdf&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F56692%2F3%2FSKRIPSI%2520TANPA%2520BAB%2520PEMBAHASAN.pdf&rft.identifier=++DESSY+TIARA+ELVIA+NITA+SARI%2C+1417011022++(2019)+STUDI+TRANSPOR+FENOL+MENGGUNAKAN+METODE+POLYMER+INCLUSION+MEMBRANE+(PIM)+DENGAN+KOPOLI(EUGENOL-DIVINIL+BENZENA)+SEBAGAI+SENYAWA+CARRIER.++Fakultas+Matematika+dan+Ilmu+Pengetahuan+Alam%2C+UNIVERSITAS+LAMPUNG.+++++&rft.relation=http%3A%2F%2Fdigilib.unila.ac.id%2F56692%2F