%A 1417011025 Dhia Hawari
%T SINTESIS DAN KARAKTERISASI POLIPADUAN POLI ASAM LAKTAT 
(PLA) DAN POLI ?-KAPROLAKTON (PCL) SEBAGAI BAHAN BAKU 
PEMBUATAN BENANG BEDAH OPERASI
DENGAN EMULSIFIER GELATIN
%X Pada penelitian ini telah dilakukan sintesis Poli Asam Laktat (PLA) dan Poli ??kaprolakton (PCL) yang banyak digunakan dalam aplikasi biomedis karena rentan 
terhadap pembelahan rantai hidrolitik maupun enzimatik sehingga mudah 
dimetabolisme dalam tubuh manusia. Hal ini sangat berguna untuk aplikasi biomedis, 
terutama benang operasi. Untuk meningkatkan fleksibilitas bahan, maka ditambahkan 
emulsifier berupa gelatin. Metode sintesis dilakukan dengan memadukan polimer PLA 
dan PCL sehingga menghasilkan lembaran film polipaduan. Uji degradasi memberikan 
hasil terbaik pada perbandingan komposisi PLA/PCL 4:1 yang memiliki persentase 
sebesar 3,06% dalam NaCl 0,9%; 1,98% dalam buffer fosfat pH 6; 2,83% dalam buffer 
fosfat pH 7 dan 4,8% dalam buffer fosfat pH 8. Nilai kekuatan mekanik terbesar 
dimiliki polipaduan dengan perbandingan komposisi PLA/PCL 1:1 sebesar 13,06 
N/mm2
belum memenuhi standar benang operasi komersil. Hasil analisis FTIR 
menunjukkan adanya interaksi fisika antara PLA dan PCL, dibuktikan dengan 
munculnya spektrum yang sama antara PLA dan PCL sebelum dan sesudah dipadukan. 
Analisis TGA menunjukkan polipaduan mengalami penurunan stabilitas termal 
dibandingkan dengan polimer penyusunnya akibat interaksi antarpolimer yang rendah. 
Analisis SEM menunjukkan polipaduan memiliki morfologi yang acak dan cenderung 
berongga.
Kata kunci: Polimer, Poli Asam Laktat (PLA), Poli ?-kaprolakton (PCL), gelatin, 
benang operasi.

In this research the synthesis of Poly Lactic Acid (PLA) and Poly ?-caprolactone 
(PCL) are widely used in biomedical applications because they are susceptible to 
hydrolytic and enzymatic chain cleavages so that they are easily metabolized in the 
human body. This is very useful for biomedical applications, especially operating 
sutures. To increase the flexibility of the material, an emulsifier in the form of gelatin 
is added. The synthesis method is carried out by blending PLA and PCL polymers to 
produce polyblend film fibers. The degradation test gives the best results on the 
composition ratio of PLA/PCL 4:1 which has a percentage of 3.06% in 0.9% NaCl; 
1.98% in phosphate buffer pH 6; 2.83% in phosphate buffer pH 7 and 4.8% in 
phosphate buffer pH 8. The greatest value of mechanical strength was obtained by 
polyblend with the ratio of the composition of PLA / PCL 1:1 at 13.06 N/mm2
. But 
this value does not meet the standards of commercial sutures. The results of FTIR 
analysis showed that there was a physical interaction between PLA and PCL, as 
evidenced by the appearance of the same spectrum, between PLA and PCL before 
and after blending. TGA analysis shows that polyblend has decreased its thermal 
stability compared to its constituent polymers due to low interaction between 
polymers. SEM analysis shows that polyblends have random morphology and tend to 
be hollow.
Keywords: Polymer, Poly Lactic Acid (PLA), Poly ?-caprolactone (PCL), gelatin, 
suture.