?url_ver=Z39.88-2004&rft_val_fmt=info%3Aofi%2Ffmt%3Akev%3Amtx%3Adc&rft.title=UJI+AKTIVITAS+NANOKATALIS+Ni0%2C6Cu0%2C4Fe2O4+UNTUK+KONVERSI+%0D%0ANANOSELULOSA+DARI+LIMBAH+KULIT+PISANG+KEPOK+%0D%0A(Musa+paradisiaca+L.)+MENJADI+GULA+ALKOHOL%0D%0ADI+BAWAH+IRRADIASI+SINAR+UV&rft.creator=MELIANA+SARI+SIMARMATA%2C+1417011074&rft.subject=540+Kimia+dan+ilmu+yang+berhubungan&rft.description=Konversi+nanoselulosa+dari+kulit+pisang+kepok+(Musa+paradisiaca+L.)+menjadi+%0D%0Agula+alkohol+telah+dilakukan+menggunakan+nanokatalis+Ni0%2C6Cu0%2C4Fe2O4+di+bawah+%0D%0Airradiasi+sinar+UV.+Nanoselulosa+dipreparasi+dari+limbah+kulit+pisang+kepok+%0D%0Amelalui+tahap+delignifikasi%2C+pemutihan+(bleaching)%2C+dan+hidrolisis+asam+disertai+%0D%0Adengan+proses+sonikasi.+Nanoselulosa+yang+digunakan+memiliki+indeks+%0D%0Akristalinitas+sebesar+40%2C63%25+dan+ukuran+partikel+sebesar+20%2C52+nm.+Nanokatalis+%0D%0ANi0%2C6Cu0%2C4Fe2O4+dipreparasi+dengan+metode+sol-gel+menggunakan+pektin+sebagai+%0D%0Aagen+pengemulsi.+Preparasi+nanokatalis+dilakukan+melalui+langkah-langkah+%0D%0Apencampuran%2C+penguapan%2C+dan+kalsinasi+pada+temperatur+600+oC.+Hasil+%0D%0Akarakterisasi+nanokatalis+menggunakan+XRD+menunjukkan+bahwa+nanokatalis+%0D%0Amemiliki+fasa+kristalin+dominan+NiFe2O4+dan+CuFe2O4+dengan+ukuran+kristal+%0D%0A26%2C24+nm.+Nanokatalis+memiliki+situs+asam+Br%C3%B8nsted-Lowry+dan+Lewis+dengan+%0D%0Ajumlah+situs+asam+sebesar+1%2C5110+mmol+piridin%2F+gram+nanokatalis.+Berdasarkan+%0D%0Ahasil+TEM%2C+nanokatalis+memiliki+ukuran+partikel+sebesar+27%2C5+nm.+Energi+celah+%0D%0Apita+nanokatalis+sebesar+3%2C28+eV.+Hasil+konversi+nanoselulosa+kulit+pisang+kepok+%0D%0Amenggunakan+nanokatalis+Ni0%2C6Cu0%2C4Fe2O4+dengan+bantuan+irradiasi+sinar+UV+%0D%0Adilakukan+dengan+variabel+waktu+konversi%2C+yaitu+30%2C+60%2C+90%2C+dan+120+menit.+%0D%0APresentase+nanoselulosa+terkonversi+didapatkan+sebesar+16%2C+20%2C+20%2C+dan+14%25.+%0D%0AKonsentrasi+glukosa+larutan+hasil+konversi+masing-masing+sebesar+30%2C3%3B+21%2C9%3B+%0D%0A37%2C8%3B+dan+27%2C8+ppm.+Hal+ini+menunjukkan+bahwa+nanokatalis+telah+aktif+dalam+%0D%0Amengkonversi+nanoselulosa+menjadi+gula+reduksi+tetapi+belum+optimal+untuk+%0D%0Amengkonversi+nanoselulosa+menjadi+gula+alkohol.%0D%0AKata+Kunci+%3A+gula+alkohol%2C+kulit+pisang+kepok%2C+nanokatalis%2C+nanoselulosa.%0D%0A%0D%0AIn+this+research%2C+conversion+of+nanocelulose+prepared+from+banana+(Musa+%0D%0Aparadisiaca+L.)+peel+into+sugar+alcohol+has+been+studied+using+nanocatalyst+%0D%0ANi0%2C6Cu0%2C4Fe2O4+under+UV+light+irradation.+Preparation+of+nanocelulose+was+%0D%0Ainvolved+delignifation%2C+bleaching%2C+and+acid+hydrolysist+with+sonification%2C+and+%0D%0Aproduced+nanocelulose+with+crystalinity+index+of+40.63%25+and+particle+size+of+%0D%0A20.52+nm.+Nanocatalyst+Ni0%2C6Cu0%2C4Fe2O4+was+prepared+with+sol-gel+method+using+%0D%0Apectin+as+emultion+agent%2C+by+mixing%2C+evaporating%2C+and+calcination+at+600+oC+for+11+%0D%0Ahours%2C+the+nanocatalyst+was+characterized+using+XRD%2C+TEM%2C+FTIR%2C+and+UV-Vis+%0D%0Ainstruments.+Characterization+of+nanocatalyst+using+XRD+showed+that+%0D%0Ananocatalyst+are+dominated+by+crystaline+NiFe2O4+and+CuFe2O4+phase+with+%0D%0Acrystal+size+at+26.24+nm.+Then%2C+FTIR+spectra+proved+that+Nanocatalyst+has+both+%0D%0ABr%C3%B8nsted-Lowry+and+Lewis+acid+sites+of+1.5110+mmol+pyridine%2Fnanocatalyst+gram.+%0D%0AMicrograph+analysis+using+TEM+showed+nanostructure+with+a+grain+size+of+27.5+%0D%0Anm+agglomeration.+UV-Vis+spectrophotometer+analysis+of+the+nanocatalyst+also+%0D%0Aproved+that+the+band+gap+energy+of+3.28+eV.+Furthermore%2C+conversion+of+%0D%0Ananocelulose+of+kepok+banana+peels+using+Ni0%2C6Cu0%2C4Fe2O4+nanocatalyst+was+%0D%0Ahappened+with+the+best+result+of+20+%25+conversion+and+37.8+ppm+of+glucose+at+90+%0D%0Aminutes+exposure+to+UV+ray+irradiation.+%0D%0AKeywords+%3A+Banana+peels%2C+nanocelulose%2C+nanocatalyst%2C+sugar+alcohol.%0D%0A&rft.publisher=Fakultas+Matematika+dan+Ilmu+Pengetahuan+Alam&rft.date=2019&rft.type=Skripsi&rft.type=NonPeerReviewed&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F57081%2F1%2FABSTRAK.pdf&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F57081%2F2%2FSKRIPSI%2520FULL.pdf&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F57081%2F3%2FSKRIPSI%2520TANPA%2520BAB%2520PEMBAHASAN.pdf&rft.identifier=++MELIANA+SARI+SIMARMATA%2C+1417011074++(2019)+UJI+AKTIVITAS+NANOKATALIS+Ni0%2C6Cu0%2C4Fe2O4+UNTUK+KONVERSI+NANOSELULOSA+DARI+LIMBAH+KULIT+PISANG+KEPOK+(Musa+paradisiaca+L.)+MENJADI+GULA+ALKOHOL+DI+BAWAH+IRRADIASI+SINAR+UV.++Fakultas+Matematika+dan+Ilmu+Pengetahuan+Alam%2C+UNIVERSITAS+LAMPUNG.+++++&rft.relation=http%3A%2F%2Fdigilib.unila.ac.id%2F57081%2F