<> "The repository administrator has not yet configured an RDF license."^^ . <> . . "PEMBUATAN SERTA PENGUJIAN KEKERASAN DAN\r\nKOMPOSISI KIMIA PRODUK CINDERAMATA BERLOGO\r\nSOLIDARITY M FOREVER DENGAN METODE\r\nPENGECORAN LOGAM MENGGUNAKAN BAHAN\r\nALUMUNIUM 6063"^^ . "In this study the making of souvenirs with the casting process and raw materials from\r\naluminum 6063. Aluminum 6063 is an aluminum alloy that has heat-treated\r\nproperties and has good properties in corrosion resistance and high strength which are\r\nwidely used for architectural frames. Aluminum 6063 series is included in the 6xxx\r\nseries aluminum alloy, namely Al-Mg-Si [3].\r\nIn this study aluminum products are produced by casting using sand molds where the\r\nequipment is simple and low cost. After conducting the casting process, the finished\r\nproduct will undergo testing including hardness test, material content test, etc. to\r\ndetermine the value of Rockwell hardness and composition content before and after\r\nthe smelting process. The test results of aluminum composition 5052 before smelting\r\nare; Si 0.532%, Fe 0.317%, Cu 0.046%, Mn 0.018%, Mg 0.562%, Cr 0.013%, Zn\r\n0.070%. And the test results of aluminum 6063 composition after smelting are; Si\r\n0.791%, Fe 0.351%, Cu 0.0583%, Mn 0.0148%, Mg 0.502%, Cr 0.0102%, Ni\r\n0.0152%, Zn 0.0658% and Ti 0.0161%. The hardness test results with the Rockwell\r\nmethod on aluminum 6063 before smelting averaged 85.5 HRB and after smelting\r\naveraged 77 HRB. Decrease in hardness test against aluminum 6063 before smelting\r\nand after smelting that is equal to 8.5 HRB. The results of the chemical composition\r\ntest were the most influences on the decrease in the level of hardness against the ratio\r\nof aluminum 6063 before smelting and after smelting namely the reduction of Mg\r\ncontent by 0.06% and increasing Si content by 0.259%.\r\nKeywords:Aluminium 6063, casting, hardness test, chemical compotition test\r\nPada penelitian kali ini pembuatan cenderamata dengan proses pengecoran dan bahan\r\nbaku dari alumunium 6063. Alumunium 6063 merupakan paduan alumunium yang\r\nmemiliki sifat dapat diperlakukan-panas dan memiliki sifat baik dalam daya tahan\r\nkorosi dan kekuatan tinggi yang banyak dipakai untuk bingkai arsitektur. Alumunium\r\nseri 6063 termasuk dalam golongan paduan alumunium seri 6xxx, yaitu Al-Mg-Si[3].\r\nPada penelitian ini produk alumunium dihasilkan melalui proses pengecoran (casting)\r\nmenggunakan cetakan pasir dimana pada proses ini peralatannya sederhana dan biaya\r\nrendah. Setelah melakukan proses pengecoran, produk cor yang telah jadi akan\r\nmengalami pengujian diantaranya uji kekerasan, uji kandungan material dan lain\r\nsebagainya untuk mengetahui nilai kekerasan Rockwell dan kandungan komposisi\r\nsebelum dan setelah proses peleburan. Hasil uji komposisi aluminium 6063 sebelum\r\npeleburan yaitu; Si 0.532%, Fe 0.31%, Cu 0.046%, Mn 0.018%, Mg 0.562%, Cr\r\n\r\n0.013%, Zn 0.07%. Dan hasil uji komposisi aluminium 6063 setelah peleburan yaitu;\r\nSi 0.791%, Fe 0.351%, Cu 0.0583%, Mn 0.0148%, Mg 0.502%, Cr 0.102%, Ni\r\n0.0152%, Zn 0.658% dan Ti 0.0161%. Hasil uji kekerasan dengan metode Rockwell\r\nterhadap aluminium 6063 sebelum peleburan rata-rata 85.5 HRB dan setelah\r\npeleburan rata-rata 77 HRB. Penurunan uji kekerasan terhadap aluminium 6063\r\nsebelum peleburan dan setelah peleburanya itu sebesar 8.5 HRB. Hasil uji komposisi\r\nkimia merupakan hal yang paling mempengaruhi turunnya tingkat kekerasan terhadap\r\nperbandingan aluminium 6063 sebelum peleburan dan setelah peleburanya\r\nberkurangnya kandungan Mg sebesar 0.06% dan bertambahnya kandungan Si sebesar 0.259 %.\r\nKeywords: Alumunium 6063, Pengecoran, Uji kekerasan, Uji komposisi Kimia"^^ . "2019" . . . . . "FAKULTAS TEKNIK"^^ . . . . . . . "1215021069"^^ . "RYAN HERMAWAN"^^ . "1215021069 RYAN HERMAWAN"^^ . . . . . . "PEMBUATAN SERTA PENGUJIAN KEKERASAN DAN\r\nKOMPOSISI KIMIA PRODUK CINDERAMATA BERLOGO\r\nSOLIDARITY M FOREVER DENGAN METODE\r\nPENGECORAN LOGAM MENGGUNAKAN BAHAN\r\nALUMUNIUM 6063 (File PDF)"^^ . . . "ABSTRAK.pdf"^^ . . . "PEMBUATAN SERTA PENGUJIAN KEKERASAN DAN\r\nKOMPOSISI KIMIA PRODUK CINDERAMATA BERLOGO\r\nSOLIDARITY M FOREVER DENGAN METODE\r\nPENGECORAN LOGAM MENGGUNAKAN BAHAN\r\nALUMUNIUM 6063 (File PDF)"^^ . . . "PEMBUATAN SERTA PENGUJIAN KEKERASAN DAN\r\nKOMPOSISI KIMIA PRODUK CINDERAMATA BERLOGO\r\nSOLIDARITY M FOREVER DENGAN METODE\r\nPENGECORAN LOGAM MENGGUNAKAN BAHAN\r\nALUMUNIUM 6063 (File PDF)"^^ . . . "SKRIPSI TANPA BAB PEMBAHASAN.pdf"^^ . . . "PEMBUATAN SERTA PENGUJIAN KEKERASAN DAN\r\nKOMPOSISI KIMIA PRODUK CINDERAMATA BERLOGO\r\nSOLIDARITY M FOREVER DENGAN METODE\r\nPENGECORAN LOGAM MENGGUNAKAN BAHAN\r\nALUMUNIUM 6063 (Other)"^^ . . . . . . "indexcodes.txt"^^ . . . "PEMBUATAN SERTA PENGUJIAN KEKERASAN DAN\r\nKOMPOSISI KIMIA PRODUK CINDERAMATA BERLOGO\r\nSOLIDARITY M FOREVER DENGAN METODE\r\nPENGECORAN LOGAM MENGGUNAKAN BAHAN\r\nALUMUNIUM 6063 (Other)"^^ . . . . . . "PEMBUATAN SERTA PENGUJIAN KEKERASAN DAN\r\nKOMPOSISI KIMIA PRODUK CINDERAMATA BERLOGO\r\nSOLIDARITY M FOREVER DENGAN METODE\r\nPENGECORAN LOGAM MENGGUNAKAN BAHAN\r\nALUMUNIUM 6063 (Other)"^^ . . . . . . "indexcodes.txt"^^ . . . "PEMBUATAN SERTA PENGUJIAN KEKERASAN DAN\r\nKOMPOSISI KIMIA PRODUK CINDERAMATA BERLOGO\r\nSOLIDARITY M FOREVER DENGAN METODE\r\nPENGECORAN LOGAM MENGGUNAKAN BAHAN\r\nALUMUNIUM 6063 (Other)"^^ . . . . . . "PEMBUATAN SERTA PENGUJIAN KEKERASAN DAN\r\nKOMPOSISI KIMIA PRODUK CINDERAMATA BERLOGO\r\nSOLIDARITY M FOREVER DENGAN METODE\r\nPENGECORAN LOGAM MENGGUNAKAN BAHAN\r\nALUMUNIUM 6063 (Other)"^^ . . . . . . "PEMBUATAN SERTA PENGUJIAN KEKERASAN DAN\r\nKOMPOSISI KIMIA PRODUK CINDERAMATA BERLOGO\r\nSOLIDARITY M FOREVER DENGAN METODE\r\nPENGECORAN LOGAM MENGGUNAKAN BAHAN\r\nALUMUNIUM 6063 (Other)"^^ . . . . . . "PEMBUATAN SERTA PENGUJIAN KEKERASAN DAN\r\nKOMPOSISI KIMIA PRODUK CINDERAMATA BERLOGO\r\nSOLIDARITY M FOREVER DENGAN METODE\r\nPENGECORAN LOGAM MENGGUNAKAN BAHAN\r\nALUMUNIUM 6063 (Other)"^^ . . . . . . "PEMBUATAN SERTA PENGUJIAN KEKERASAN DAN\r\nKOMPOSISI KIMIA PRODUK CINDERAMATA BERLOGO\r\nSOLIDARITY M FOREVER DENGAN METODE\r\nPENGECORAN LOGAM MENGGUNAKAN BAHAN\r\nALUMUNIUM 6063 (Other)"^^ . . . . . . "lightbox.jpg"^^ . . . "PEMBUATAN SERTA PENGUJIAN KEKERASAN DAN\r\nKOMPOSISI KIMIA PRODUK CINDERAMATA BERLOGO\r\nSOLIDARITY M FOREVER DENGAN METODE\r\nPENGECORAN LOGAM MENGGUNAKAN BAHAN\r\nALUMUNIUM 6063 (Other)"^^ . . . . . . "preview.jpg"^^ . . . "PEMBUATAN SERTA PENGUJIAN KEKERASAN DAN\r\nKOMPOSISI KIMIA PRODUK CINDERAMATA BERLOGO\r\nSOLIDARITY M FOREVER DENGAN METODE\r\nPENGECORAN LOGAM MENGGUNAKAN BAHAN\r\nALUMUNIUM 6063 (Other)"^^ . . . . . . "medium.jpg"^^ . . . "PEMBUATAN SERTA PENGUJIAN KEKERASAN DAN\r\nKOMPOSISI KIMIA PRODUK CINDERAMATA BERLOGO\r\nSOLIDARITY M FOREVER DENGAN METODE\r\nPENGECORAN LOGAM MENGGUNAKAN BAHAN\r\nALUMUNIUM 6063 (Other)"^^ . . . . . . "small.jpg"^^ . . . "PEMBUATAN SERTA PENGUJIAN KEKERASAN DAN\r\nKOMPOSISI KIMIA PRODUK CINDERAMATA BERLOGO\r\nSOLIDARITY M FOREVER DENGAN METODE\r\nPENGECORAN LOGAM MENGGUNAKAN BAHAN\r\nALUMUNIUM 6063 (Other)"^^ . . . . . . "lightbox.jpg"^^ . . . "PEMBUATAN SERTA PENGUJIAN KEKERASAN DAN\r\nKOMPOSISI KIMIA PRODUK CINDERAMATA BERLOGO\r\nSOLIDARITY M FOREVER DENGAN METODE\r\nPENGECORAN LOGAM MENGGUNAKAN BAHAN\r\nALUMUNIUM 6063 (Other)"^^ . . . . . . "preview.jpg"^^ . . . "PEMBUATAN SERTA PENGUJIAN KEKERASAN DAN\r\nKOMPOSISI KIMIA PRODUK CINDERAMATA BERLOGO\r\nSOLIDARITY M FOREVER DENGAN METODE\r\nPENGECORAN LOGAM MENGGUNAKAN BAHAN\r\nALUMUNIUM 6063 (Other)"^^ . . . . . . "medium.jpg"^^ . . . "PEMBUATAN SERTA PENGUJIAN KEKERASAN DAN\r\nKOMPOSISI KIMIA PRODUK CINDERAMATA BERLOGO\r\nSOLIDARITY M FOREVER DENGAN METODE\r\nPENGECORAN LOGAM MENGGUNAKAN BAHAN\r\nALUMUNIUM 6063 (Other)"^^ . . . . . . "small.jpg"^^ . . "HTML Summary of #57088 \n\nPEMBUATAN SERTA PENGUJIAN KEKERASAN DAN \nKOMPOSISI KIMIA PRODUK CINDERAMATA BERLOGO \nSOLIDARITY M FOREVER DENGAN METODE \nPENGECORAN LOGAM MENGGUNAKAN BAHAN \nALUMUNIUM 6063\n\n" . "text/html" . . . "600 Teknologi (ilmu terapan)" . . . "620 Ilmu teknik dan ilmu yang berkaitan" . .