@misc{eprints57185,
           title = {SINTESIS DAN KARAKTERISASI POLIPADUAN POLI ASAM LAKTAT 
(PAL) DAN POLI {\ensuremath{\epsilon}}-KAPROLAKTON (PCL) DENGAN EMULSIFIER 
TWEEN 80 SEBAGAI BAHAN BAKU BENANG BEDAH OPERASI},
          author = {13177011078 Yolanda Larasati},
         address = {UNIVERSITAS LAMPUNG},
       publisher = {Fakultas Matematika dan Ilmu Pengetahuan Alam},
            year = {2019},
             url = {http://digilib.unila.ac.id/57185/},
        abstract = {Pada penelitian ini telah dilakukan polipaduan antara PAL dan PCL dengan 
penambahan emulsifier Tween 80. Proses polipaduan tersebut dilakukan dengan cara 
mekanik selanjutnya dibuat lembaran film. Penelitian ini dilakukan dengan 
perbandingan 3 variasi yang berbeda yaitu PAL : PCL/ tween 80 (1:1), PAL : 
PCL/tween 80 (4:1), dan PAL : PCL/tween 80 (1:4). Polipaduan yang telah dibuat di 
uji degradasi, mekanik, karakterisasi dengan FTIR, SEM, dan TGA. Hasil penelitian 
menunjukan bahwa uji degradasi dengan menggunakan larutan NaCl 0,9\% , buffer 
fosfat, dan uji mekanik memberikan hasil terbaik pada perbandingan PAL : 
PCL/tween 80 dengan perbandingan 4:1. Hasil uji degradasi pada larutan NaCl 0,9\% 
kehilangan berat sebesar 2,61\%. Hasil uji degradasi menggunakan buffer fosfat pH 6 
yaitu kehilangan berat sebesar 1,72\%, pH 7 sebesar 3,06\% dan pada pH 8 yaitu 
sebesar 4,53\%. Hasil uji mekanik memiliki nilai kuat tarik sebesar 14,11 N/mm2
. 
Hasil FTIR pada sampel polipaduan PAL+PCL (4:1) yaitu memiliki vibrasi ulur C-H, 
C=O dan C-O ester jenuh dengan bilangan gelombang sebesar 2922,2 cm-1 ,1744,4 
cm-1
, dan 1177,8 cm-1
. Pada vibrasi ulur C-H tekuk dan C-O-H tekuk yaitu pada 
bilangan gelombang 1453 cm-1 dan 1073 cm-1
. Hasil TGA menunjukkan polipaduan 
PAL : PCL (4:1) mengalami 2 fase dekomposisi yaitu pada suhu 273 oC dan 428 oC. 
Hasil SEM menunjukan polipaduan PAL : PCL (4:1) memiliki morfologi permukaan 
dengan struktur yang berongga dibandingkan dengan struktur asli permukaan dari 
PAL dan PCL. 
Kata kunci : Polipaduan, Poli Asam Laktat (PAL), Poli {\ensuremath{\epsilon}}-kaprolakton (PCL), 
Tween 80.

In this research a polyblend of PAL and PCL has been carried out with the addition 
of emulsifier Tween 80. The process of the polyblend is carried out by a mechanical 
way and then is made sheet of film. This research was conducted with a comparison 
of 3 different variations, namely PAL: PCL / tween 80 (1:1), PAL: PCL /tween 80 
(4:1), and PAL : PCL /tween 80 (1:4). Polyblend that had been made is tested 
degradation, mechanical, characterization with FTIR, SEM, and TGA. The result 
showed that the degradation test using 0,9\% NaCl solution, phosphate buffer, and 
mechanical test gave the best result on the ratio of 
PAL: PCL /tween 80 with a ratio of 4:1. The result of degradation test in 0,9\% NaCl 
solution of weight loss of 2,61\%. The result of the degradation test using phosphate 
buffer pH 6 which is weight loss of 1,72\%, pH 7 of 3,06\% and at pH 8 which is 
4,53\%. The mechanical test result have tensile strength values of 
14,11 N / mm2
. FTIR result in polyblend samples PAL + PCL (4:1) which have C-H 
stretching vibrations, C = O and saturated C-O ester with wave numbers of 2922,2 
cm-1
, 1744,4 cm-1
, and 1177,8 cm-1
. At stretching vibrations C-H buckling and 
bending C-O-H are at wave numbers 1453 cm-1
and 1073 cm-1
. The TGA result show 
a polyblend of PAL : PCL (4:1) experiencing 2 phases of decomposition which is at 
a temperature of 273 oC and 428 oC. The SEM result show that the PAL : PCL (4:1) 
polyblend has a surface morphology with a hollow structure compared to the original 
surface structure of PAL and PCL.
Kata kunci : Polyblend, Poli Lactic Acid (PLA), Poli {\ensuremath{\epsilon}}-Caprolactone (PCL), Tween 
80.
}
}