N2  - Telah dilakukan penelitian reduksi selektif bijih nikel laterit dengan variasi
temperatur sebesar 950oC, 1050°C dan 1150oC, waktu tahan 60, 90 dan 120 menit
dan konsentrasi reduktor batubara antrasit 5, 10 dan 15% wt. terhadap produk
reduksi nikel laterit menggunakan bahan aditif magnesium sulfat 10% dan dilanjut
dengan proses separasi magnetik. Karakterisasi X-ray Diffraction (XRD)
menunjukkan fasa yang dominan adalah Magnesioferrite (Fe2MgO4), Magnetite
(Fe3O4), Fayalite (Fe2SiO4), Iron Nickel (FeNi), Iron Sulfide (FeS) dan Wuestite
(FeO).Karakterisasi X-ray Fluororescene (XRF) menunjukkan bahwa kadar nikel
optimum didapatkan pada temperatur reduksi 1150°C selama 90 menit dengan
penambahan reduktor 5% diperoleh nilai 2,086% dan recovey 80,68%.
Karakterisasi Scanning Electron Microscope (SEM) yang dilengkapi Energy
Dispersive X-ray Spectroscopy (EDS) menunjukkan bahwa ukuran butir terbesar
adalah 10,31 m.

Kata kunci: nikel laterit, batubara antrasit, magnesium sulfat, reduksi selektif,
separasi magnetik.
Has conducted research laterite selective reduction of nickel ore with variations
temperature of 950oC, 1050°C and 1150oC, The holding time 60, 90 and 120
minutes and the concentration of anthracite coal reductant5, 10 and 15% wt. to the
reduction of laterite nickel product using magnesium sulfate additive is 10% and
continued with the process of magnetic separation, Characterization X-ray
Diffraction (XRD) showed that the dominant phase is Magnesioferrite (Fe2MgO4),
Magnetite (Fe3O4), Fayalite (Fe2SiO4), Iron Nickel (FeNi), Iron Sulfide (FeS) and
Wuestite (FeO). Karakterisasi X-ray Fluororescene (XRF) showed that the
optimum nickel grade obtained at temperatures of 1150°C reduction for 90
minutes with the addition of 5% reductant obtained recovey value of 2,086% and
80.68%. Characterization Scanning Electron Microscope (SEM) equipped with
Energy Dispersive X-ray Spectroscopy (EDS) showed that the largest grain size is
10,31 m.
Keywords: nickel laterite, anthracite coal, magnesium sulfate, selective reduction,
magnetic separation.
PB  - FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM
TI  - PENGARUH VARIASI TEMPERATUR, WAKTU TAHAN DAN
KONSENTRASI REDUKTOR TERHADAP PRODUK
REDUKSI KARBOTERMIK BIJIH NIKEL KADAR
RENDAH DENGAN REDUKTOR ANTRASIT DAN
BAHAN ADITIF MAGNESIUM SULFAT