title: VARIASI KADAR CaCO3 TERHADAP PEMBENTUKAN FASA
SUPERKONDUKTOR BSCCO-2223 MENGGUNAKAN
METODE PENCAMPURAN BASAH
ispublished: pub
subjects: 530
full_text_status: restricted
abstract: Penelitian ini dilakukan untuk mengetahui pengaruh kadar CaCO3 terhadap
pembentukan fasa superkonduktor BSCCO-2223 dengan menghitung tingkat
kemurnian fasa yang terbentuk, melihat stuktur mikro dan efek Meissnernya.
Variasi CaCO3 yang dilakukan sebesar 1,95; 2,00; 2,05 dan 2,10 mol menggunakan
metode pencampuran basah dengan suhu kalsinasi 800 °C selama 10 jam dan suhu
sintering 865 °C selama 30 jam. Hasil karakterisasi XRD menunjukkan tingkat
kemurnian fasa yang terbentuk meningkat seiring dengan bertambahnya kadar Ca
dan optimum pada BSCCO/Ca 2,05 mol dan menurun pada BSCCO/Ca 2,10. Fraksi
volume tertinggi didapatkan sebesar 74,48 % pada sampel BSCCO/Ca 2,05.
Sedangkan fraksi volume terendah sebesar 48,17 % pada sampel BSCCO/Ca 1,95.
Sementara, derajat orientasi tertinggi 11,61 % pada BSCCO/Ca 2,05. Derajat
orientasi terendah 6,63 % pada BSCCO/Ca 1,95. Hasil karakterisasi SEM
menunjukkan semua sampel telah terorientasi serta memiliki ruang kosong antar
lempengan (void) yang relatif sedikit. Hasil uji efek Meissner menunnjukkan hanya
pada sampel BSCCO/Ca 2,05 yang mengalami efek Meissner lemah berupa
penolakan medan magnet.

Kata kunci: Superkonduktor BSCCO-2223, CaCO3, fraksi volume, derajat
orientasi, dan efek Meissner.
This research was conducted to determine the effect of CaCO3 levels on the
formation of the superconducting phase BSCCO-2223 by calculating the level of
purity of the phases formed, looking at the microstructure and its Meissner effect.
The variation of CaCO3 was 1.95; 2.00; 2.05 and 2.10 mole using the wet mixing
method with a calcination’s temperature is 800 °C for 10 hours and a sintering’s
temperature of 865 °C for 30 hours. The XRD’s chacterization results show that the
level of purity of the formed phases increases with increasing Ca levels and its
optimum at BSCCO/Ca 2.05 mole and then decreases at BSCCO/Ca 2.10. The
highest volume fraction was 74,48 % in the BSCCO/Ca 2.05 sample. While the
lowest volume fraction was 48.17 % in the BSCCO/Ca 1.95 sample. Meanwhile,
the highest degree of orientation was 11.61 % at BSCCO/Ca 2.05. The lowest
degree of orientation was 6.63 % at BSCCO/Ca 1.95. SEM’s chacterization results
show of all samples have been oriented and have relatively little space between
slabs (voids). The results of the Meissner effect show that only in the BSCCO/Ca
2.05 sample which showed a weak Meissner effect as the rejection of magnetic
fields.

Keywords: Superconductors BSCCO-2223, CaCO3, volume fraction, degree of
orientation, and Meissner effect.
date: 2019
date_type: published
publisher: FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM
place_of_pub: UNIVERSITAS LAMPUNG
citation:   Prastiana Tiara Pratiwi, 151704101115  (2019) VARIASI KADAR CaCO3 TERHADAP PEMBENTUKAN FASA SUPERKONDUKTOR BSCCO-2223 MENGGUNAKAN METODE PENCAMPURAN BASAH.  FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.     
document_url: http://digilib.unila.ac.id/57337/1/ABSTRAK.pdf
document_url: http://digilib.unila.ac.id/57337/2/SKRIPSI%20FULL.pdf
document_url: http://digilib.unila.ac.id/57337/3/SKRIPSI%20TANPA%20BAB%20PEMBAHASAN.pdf