%A 1417041081 SEPTA ARIO
%T PENGARUH VARIASI KONSENTRASI BERAT
LAMPUNG

FAKULTAS MATEMATIKA DAN

MINERAL
SEBAGAI MATERIAL SUBSTITUSI SEMEN
PADA PRODUK MORTAR
%X Basalt Lampung yang digunakan berupa bubuk tanpa dan dengan dikalsinasi suhu
900?C. Sampel mortar dibuat dengan metode pengadukan basah yang terdiri dari
campuran semen, pasir, air dan bubuk basalt. Hasil uji menunjukkan bahwa basalt
tanpa dan dengan dikalsinasi masing-masing memiliki kandungan SiO2, Al2O3,
dan Fe2O3 sebesar 82,175% dan 82,19%, berat tertinggal di atas ayakan 45?m
sebesar 0,66% dan 1,0% serta fasa yang terbentuk diantaranya adalah fasa
anorthite, augite, augite aluminian, forsterite, quartz dan silicon oxide. Sampel
mortar semen OPC substitusi basalt tanpa dan dengan dikalsinasi memiliki kuat
tekan tertinggi masing-masing pada konsentrasi 5% dan 20% dengan porositas
sebesar 2,4% dan 2,4%, absorbsi sebesar 1,29% dan 1,30% serta kuat tekan
masing-masing sebesar 24,97 MPa dan 24,16 MPa. Sampel mortar semen PCC
substitusi basalt tanpa dan dengan dikalsinasi memiliki kuat tekan tertinggi pada
konsentrasi yang sama yaitu 5% dengan porositas sebesar 4,8% dan 4,8%,
absorbsi sebesar 2,52% dan 2,50% serta kuat tekan masing-masing sebesar 22,55
MPa dan 21,11 MPa. Fasa yang terbentuk pada mortar semen OPC dan PCC yaitu
CSH, portlandite, calcite dan quartz. Fasa CASH juga muncul pada mortar semen
PCC. Hasil tersebut menunjukkan bahwa variasi konsentrasi berat basalt pada
semen OPC dan PCC mempengaruhi sifat dan karakteristik produk mortar.

Kata kunci: basalt, mortar, semen OPC dan PCC, struktur fasa, kuat tekan.
Lampung basalt?s used in the form of powder without and with calcined
temperature of 900?C. Mortar samples are made by wet stirring method which
consists of a mixture of cement, sand, water and basalt powder. The test results
showed that basalt without and with calcined each contained SiO2, Al2O3, and
Fe2O3 amounting to 82,175% and 82,19%, the weight left on the 45?m sieve was
0,66% and 1,0% and the phases formed included are the phases of anorthite,
augite, augite aluminian, forsterite, quartz and silicon oxide. OPC cement mortar
samples of basalt substitution without and with calcined had the highest
compressive strength at concentrations of 5% and 20% with porosity are 2,4% and
2,4%, absorption are 1,29% and 1,30% and compressive strength respectively
24,97 MPa and 24,16 MPa. PCC cement mortar samples of basalt substitution
without and with calcined had the highest compressive strength at the same
concentration of 5% with porosity are 4,8% and 4,8%, absorption are 2,52% and
2.50% and compressive strength respectively at 22,55 MPa and 21,11 MPa.
Phases are formed on OPC and PCC cement mortars are CSH, portlandite, calcite
and quartz. CASH phase also appeared on PCC cement mortar. These results
indicate that variations in basalt weight concentration on OPC and PCC cement
affect the properties and characteristics of mortar products.

Keywords: basalt, mortar, OPC and PCC cement, phase structure, compressive
strength.
%C UNIVERSITAS LAMPUNG
%D 2019
%I FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM
%L eprints57347