@misc{eprints57356,
           title = {SIFAT FISIS KOMPOSIT PE/NANOSILIKA SEBAGAI FUNGSI

KETEBALAN},
          author = {1417041092 TriaPermata Sari},
         address = {UNIVERSITAS LAMPUNG},
       publisher = {FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM},
            year = {2019},
             url = {http://digilib.unila.ac.id/57356/},
        abstract = {Polietilena (PE) telah banyak digunakan sebagai bahan insulasi kabel tegangan
tinggi karena sifat fisik, kimia, dan listriknya yang luar biasa. Dalam penelitian ini
bubuk amorf nanosilika diekstraksi dari batu apung menggunakan NaOH, H2SO4
dan HCl. PE dan nanosilika dicampur menggunakan mixer pada suhu 95 oC dan
kemudian dibuat lapisan tipis menggunakan barcoater. Presentase berat
nanosilika adalah 5 dan 10\% dengan ketebalan masing-masing 6, 12, dan 25 {\ensuremath{\mu}}m.
PE/nanosilika dikarakterisasi melalui spektroskopi Fourier Transform Infra Red
(FTIR) dan pengukuran LCR meter untuk mengetahui respon konduktivitas listrik
dan permitivitas sebagai fungsi frekuensi. Efek ketebalan pada sifat listrik
PE/nanosilika 5 dan 10\% untuk nilai konduktivitas listrik pada sampel dengan
ketebalan 25 {\ensuremath{\mu}}m memiliki nilai konduktivitas yang lebih besar. Sedangkan untuk
permitivitas dari kedua sampel dengan variasi filer menunjukkan bahwa semakin
tebal sampel, maka semakin besar nilai permitivitas.
Kata Kunci: komposit, polietilena, nanosilika, barcoater.
Polyethylene (PE) has been widely used as the insulation material of high voltage
cables because of its outstanding physical, chemical, and electrical properties. In
this research the amorph nanosilica powders were extracted from pumice using
NaOH, H2SO4 and HCl. PE and nanosilica was blended by mixer at temperature
95 OC and then made the film by using barcoater. The weight percentage of
nanosilica was 5 and 10\% with thickness of 6, 12 and 25{\ensuremath{\mu}}m respectively. The
PE/nanosilica were characterized via Fourier Transform Infra Red (FTIR)
spectroscopy and LCR measurement to abtain conductivity and permitivity respons
as a function of frequency. The effect thickness on the electrical properties of
PE/nanosilica of 5 and 10 \% for conductivity values in samples 25 {\ensuremath{\mu}}m thick has a
greater conductivity value. Whereas for the electric constant of two filer variation
shows that the thicker the sample, the greater the electric constant value. Whereas
for the dielectric constant of two filler variations shows that the ticker the sample,
the greater the electric constant value.
Key words: composite, polyethylene, nanosilica, barcoater}
}