?url_ver=Z39.88-2004&rft_val_fmt=info%3Aofi%2Ffmt%3Akev%3Amtx%3Adc&rft.title=PENGARUH+LAJU+PENAMBAHAN+DOPING+FOSFOR+TERHADAP%0D%0ASTRUKTUR+KRISTAL+DAN+LUAS+PERMUKAAN+SPESIFIK%0D%0ANANOTITANIA+DENGAN+METODE+SOL+GEL&rft.creator=Vidi+Nurhidayah%2C+1517041095&rft.subject=500+ilmu+pengetahuan+alam+dan+matematika&rft.subject=530+Fisika&rft.description=Telah+dilakukan+penelitian+tentang+pengaruh+penambahan+doping+fosfor%0D%0Amenggunakan+syringe+pump+dengan+metode+sol-gel.+Penelitian+ini+bertujuan+untuk%0D%0Amengetahui+pengaruh+variasi+laju+penambahan+doping+fosfor+terhadap+struktur%0D%0Akristal+dan+luas+permukaan+spesifik+TiO2.+Laju+penambahan+doping+yang%0D%0Adigunakan+selama+0%2C4%3B+0%2C2%3B+0%2C13+dan+0%2C1ml%2Fjam+dengan+doping+yang+digunakan%0D%0Asebanyak+0%2C2+ml.+Sampel+TiO2+dikalsinasi+pad+suhu+450oC+selama+5+jam.+Serbuk%0D%0Adikarakterisasi+dengan+x-ray+diffraction+(XRD)+dan+surface+area+analyzer+(SAA)%0D%0Adengan+metode+BET.+Difraktogram+XRD+secara+umum+menunjukkan+fasa+struktur%0D%0Akristal+nanotitania+adalah+anatase+yang+merupakan+hasil+sintesis+TTIP+sebagai%0D%0Asumber+utama+TiO2.+Analisis+ukuran+partikel+menggunakan+data+XRD+pada+TiO2%0D%0Adengan+laju+yang+berbeda-beda+secara+berturut-turut+yaitu+sebesar+10%2C13%3B+9%2C98%3B%0D%0A%0D%0A9%2C25%3B+dan+10%2C33+nm.+Masing-masing+hasil+uji+BET+pada+setiap+sampel+berturut-%0D%0Aturut+yaitu+86%2C9%3B+87%2C4%3B+99%2C7%3B+96%2C3dan+96%2C2+m%0D%0A%0D%0A2%0D%0A%2Fg.+Hasil+ukuran+partikel+yaitu+sebesar%0D%0A9%2C25+nm+dan+luas+permukaan+maksimum+pada+metode+BET+yaitu+sebesar+99%2C7%0D%0Am%0D%0A2%0D%0A%2Fg+pada+laju+penetesan+0%2C2+ml%2Fjam.%0D%0AKata+kunci%3A+Luas+permukaan%2C+metode+sol-gel%2C+nanotitania%2C+syringe+pump.%0D%0AThe+effect+of+the+addition+of+phosphorus+dopingto+nanotitania+has+been+carried+out%0D%0Ausing+a+syringe+pump+by+sol-gel+method.+The+purpose+of+this+study+is+to+determine%0D%0Athe+effect+of+the+addition+rate+of+phosphorus+doping+to+thecrystal+structure+and%0D%0Aspecific+surface+area+of+TiO2.+Doping+increment+rate+used+are+0%2C4%3B+0%2C2%3B+0%2C13+and%0D%0A0%2C1+ml%2Fhours.+TiO2+samples+were+calcined+at+450oC+for+5+hours.+The+powder+was%0D%0Acharacterized+by+x-ray+diffraction+(XRD)+and+surface+area+analyzer+(SAA)+by+the%0D%0ABET+method.+XRD+diffractogram+shows+that+the+nanotitania+crystal+structure%0D%0Aphase+is+anatase+which+is+the+result+of+TTIP+synthesis+as+the+main+source+of+TiO2.+Particle+size+analysis+using+XRD+data+on+TiO2+with+different+rates+are+10.13%3B+9.98%3B%0D%0A9.25%3B+and+10.33+nm.+Respectively+BET+test+results+for+each+sample+were+86.9%3B%0D%0A87%2C4%3B+99%2C7%3B+96%2C3and+96%2C2+m%0D%0A2%0D%0A%2Fg.+The+average+particle+size+is+9%2C25+nm+and+the%0D%0A%0D%0Amaximum+surface+area+in+BET+method+was+found+99%2C7+m2%0D%0A%0D%0A%2Fg+in+the+rate+of+0%2C2%0D%0A%0D%0Aml%2Fhours.%0D%0AKeywords%3A+Nanotitania%2C+sol-gel+method%2C+surface+area%2C+syringe+pump.&rft.publisher=FAKULTAS+MATEMATIKA+DAN+ILMU+PENGETAHUAN+ALAM&rft.date=2019&rft.type=Skripsi&rft.type=NonPeerReviewed&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F57358%2F1%2FABSTRAK.pdf&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F57358%2F2%2FSKRIPSI%2520TANPA%2520BAB%2520PEMBAHASAN.pdf&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F57358%2F2%2FSKRIPSI%2520FULL.pdf&rft.identifier=++Vidi+Nurhidayah%2C+1517041095++(2019)+PENGARUH+LAJU+PENAMBAHAN+DOPING+FOSFOR+TERHADAP+STRUKTUR+KRISTAL+DAN+LUAS+PERMUKAAN+SPESIFIK+NANOTITANIA+DENGAN+METODE+SOL+GEL.++FAKULTAS+MATEMATIKA+DAN+ILMU+PENGETAHUAN+ALAM%2C+UNIVERSITAS+LAMPUNG.+++++&rft.relation=http%3A%2F%2Fdigilib.unila.ac.id%2F57358%2F