N2  - Abstrak. Telah dilakukan penelitian tentang efektivitas ekstrak kulit buah maja
sebagai inhibitor pada baja karbon AISI 1020 dalam medium korosif NaCl 3%
dengan variasi waktu perendaman. Sampel baja karbon AISI 1020 direndam
dalam medium korosif NaCl 3% tanpa diberi dan dengan diberi inhibitor ekstrak
kulit buah maja dengan konsentrasi 0,8% selama 5, 15, 25, 35, dan 45 hari.
Perhitungan penurunan laju korosi dilakukan dengan metode kehilangan berat.
Hasil penelitian menunjukkan bahwa penambahan inhibitor ekstrak kulit buah
maja efektif dalam menurunkan laju korosi sampel dengan efisiensi terbesar pada
perendaman selama 35 hari, yaitu sebesar 72,6%. Hasil karakterisasi XRD
memperlihatkan bahwa fasa yang terbentuk adalah Fe murni dan pada sampel
yang direndam tanpa inhibitor muncul juga fasa Fe3O4 yang merupakan produk
korosi. Hasil karakterisasi SEM menunjukkan mikro struktur permukaan sampel
setelah direndam yaitu terdapat retakan, lubang, dan gumpalan yang
mengindikasikan bahwa sampel telah mengalami korosi. Hasil karakterisasi EDS
menunjukkan bahwa pada sampel yang telah direndam terdapat produk korosi
berbentuk senyawa Fe dan O yang besarnya semakin meningkat ditiap waktu
perendaman.
Kata kunci: Baja karbon AISI 1020, inhibitor korosi, ekstrak kulit buah maja,

NaCl, XRD, dan SEM-EDS.
Abstract. Research has been conducted on the effectiveness of maja fruit skin
extract as an inhibitor of carbon steel AISI 1020 in a corrosive medium NaCl 3%
with variations in immersion time. The samples carbon steel AISI 1020 were
immersed in corrosive medium NaCl 3% without being given and given the
inhibitor of maja skin extract with a concentration of 0.8% for 5, 15, 25, 35, and
45 days. Calculation of reduction in corrosion rate is carried out by the method of
weight loss. The results showed that the addition of the maja fruit skin extract
inhibitor was effective in reducing the corrosion rate of the sample with the
greatest efficiency at 35 days immersion, which was equal to 72.6%. The results
of XRD characterization show that the phase formed is pure Fe and Fe3O4 phase
which is a corrosion product is immersed without inhibitor. The results of SEM
characterization showed that the microstructure of the surface of the sample after
immersion was there were cracks, holes, and lumps which indicated that the
sample had been corroded. The results of EDS characterization show that in the
soaked sample there were corrosion products in the form of Fe and O compounds
whose magnitude increased every time immersion.
Key words. Low carbon AISI 1020, corrosion inhibition, the exract of maja skin,

NaCl, XRD, and SEM-EDS.
PB  - FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM
TI  - EFEKTIVITAS EKSTRAK KULIT BUAH MAJA SEBAGAI INHIBITOR
PADA BAJA KARBON AISI 1020 DALAM MEDIUM KOROSIF
NaCl 3% DENGAN VARIASI WAKTU PERENDAMAN
AV  - restricted
ER  -