title: PENGARUH SUHU SINTERING TERHADAP PEMBENTUKAN FASE  SUPERKONDUKTOR BSCCO-2223 DENGAN KADAR Ca = 2,10  MENGGUNAKAN METODE PENCAMPURAN BASAH
creator: KOMALA DEWI, 1417041044
subject: 500 ilmu pengetahuan alam dan matematika
description: Penelitian ini dilakukan untuk mengetahui pengaruh suhu sintering terhadap  pembentukan fase superkonduktor BSCCO-2223 dengan kadar Ca = 2,10  menggunakan metode pencampuran basah. Bahan yang digunakan yaitu Bi2O3,  SrCO3, CaCO3, CuO, HNO3 dan aquades. Sintesis dilakukan dengan melarutkan  bahan menggunakan HNO3 dan aquades secara perlahan kemudian larutan  dikeringkan selama 40 jam dengan suhu 300, 400 dan 600 °C secara bertahap.  Sampel dikalsinasi pada suhu 800 °C selama 10 jam dan disintering dengan variasi  suhu 850, 855, 860 dan 865 °C selama 20 jam. Hasil XRD menunjukkan bahwa    suhu sintering berpengaruh terhadap pembentukan fase superkonduktor BSCCO-  2223, dengan nilai fraksi volume yang cenderung meningkat seiring meningkatnya    suhu sintering. Fraksi volume tertinggi diperoleh pada sampel BSCCO-2223-865  yaitu 79,49 %. Hasil SEM menunjukkan bahwa semua sampel telah memiliki  lapisan-lapisan yang tersusun (terorientasi) dengan ruang kosong antara lempengan    (void) relatif kecil. Derajat orientasi yang tertinggi diperoleh pada sampel BSCCO-  2223-860 yaitu 23,77 %.    Kata kunci: Superkonduktor, BSCCO-2223, sintering, fraksi volume dan derajat    orientasi.  This study was conducted to determine the effect of sintering temperature on the  formation of BSCCO-2223 superconductor phase with levels of Ca = 2,10 using the  wet mixing method. The materials used were Bi2O3, SrCO3, CaCO3, CuO, HNO3  and aquades. Synthesis is carried out by dissolving the materials using HNO3 and  aquades slowly then the solution is dried for 40 hours at a temperature of 300, 400  and 600 °C gradually. The samples were calcined at 800 ° C for 10 hours and each  was sintered with temperature variations of 850, 855, 860 and 865 ° C for 20 hours.  The XRD result shows that the sintering temperature has an effect on the formation  of BSCCO-2223 superconductor phase, with volume fraction value which tends to  increase with increasing sintering temperature. The highest volume fraction was  obtained in the BSCCO-2223-865 sample which is 79,49%. SEM result shows that  all samples have arranged layers (oriented) with relatively small empty space  between the plaques (void). The highest orientation degree is in the BSCCO-2223-  860 sample which is 23,77%.    Keywords: Superconductor, BSCCO-22223, sintering, volume fraction and    orientation degree.
publisher: FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM
date: 2019
type: Skripsi
type: NonPeerReviewed
format: text
identifier: http://digilib.unila.ac.id/57381/1/ABSTRAK-ABSTRACT.pdf
format: text
identifier: http://digilib.unila.ac.id/57381/2/SKRIPSI%20FULL.pdf
format: text
identifier: http://digilib.unila.ac.id/57381/3/SKRIPSI%20TANPA%20BAB%20PEMBAHASAN.pdf
identifier:   KOMALA DEWI, 1417041044  (2019) PENGARUH SUHU SINTERING TERHADAP PEMBENTUKAN FASE SUPERKONDUKTOR BSCCO-2223 DENGAN KADAR Ca = 2,10 MENGGUNAKAN METODE PENCAMPURAN BASAH.  FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.     
relation: http://digilib.unila.ac.id/57381/