N2  - Penelitian dilakukan untuk mengetahui pengaruh penambahan aspal terhadap
karakteristik termal, struktur fasa, daya serap air, dan kuat tekan silika yang
diekstraksi dari sekam padi menggunakan metode alkalis. Pembuatan paduan
silika aspal dilakukan dengan menggunakan perbandingan massa silika dan aspal
yaitu 1:0; 1:0,4; 1:0,5; dan 1:0,6 pada suhu pencampuran 160 ?C dan dipanaskan
pada suhu 150 ?C selama 3 jam. Karakteristik termal dan struktur fasa dianalisis
menggunakan Differential Thermal Analysis/Thermo Gravimetrical Analysis
(DTA/TGA) dan X-Ray Diffraction (XRD). Hasil analisis DTA/TGA
menunjukkan bahwa penambahan aspal mengakibatkan terjadinya penurunan
massa, suhu awal (on set), suhu maksimal dan suhu lembah endotermik. Selain
itu, terjadi peningkatan suhu puncak eksotermik. Hasil analisis XRD
menunjukkan bahwa penambahan aspal mengakibatkan munculnya karbon amorf,
terjadi pergeseran 2? rentang dan intensitas tertinggi dari silika amorf.
Penambahan aspal mengakibatkan terjadinya penurunan nilai daya serap air dan
kuat tekan.
Kata kunci: aspal, karakteristik termal, silika sekam padi, struktur fasa.
This research was carried out to investigate the effect of asphalt addition to
thermal characteristics, phase structure, water absorption and compressive
strength of extracted silica from rice husk using alkaline method. The mass ratio
of silica and asphalt alloys were 1:0; 1:0,4; 1:0,5; and 1:0,6. Silica and asphalt
were mixed at 160 ?C followed by calcination at 150 ?C for 3 hours. Thermal
characteristics and phase structures were analyzed using Differential Thermal
Analysis/Thermo Gravimetrical Analysis (DTA/TGA) and X-Ray Diffraction
(XRD). DTA/TGA analysis results show that the addition of asphalt causes a
decreasing in mass, on set temperature, maximum temperature, endothermic
temperature, and an increasing in exothermic temperature. The results of XRD
analysis show that the addition of asphalt resulted in the appearance of
amorphous carbon, shifting the range and the highest intensity of 2? amorphous
silica. The addition of asphalt causes a decrease in the value of water absorption
and compressive strength.
Keywords: asphalt, phase structure, rice husk silica, thermal characteristics.