%A 1517041044 Nur Asriyani
%T Dia Raafi Pertiwi, 1517041130 (2019) PENGARUH VARIASI KONSENTRASI MINERAL BASALT DAN SODIUM HIDROKSIDA TERHADAP SIFAT FISIS DAN KARAKTERISTIK PRODUK GEOPOLYMER. FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.
%X Elektroda kondukif transparan (TCE) berbasis AgNWs dibuat pada substrat
polikarbonat (PC) dengan variasi perulangan menggunakan teknik spray coating. AgNWs disintesis mengunakan polyvinyl pyrrolidone (PVP) dengan metode
polyol. AgNWs yang diperoleh memiliki diameter dan panjang masing-masing
176,13 nm dan 28,58 ?m. Lapisan AgNWs menghasilkan resistansi terendah pada
3 perulangan sebesar 4,98 ?.sq

-1 dengan transmitansi 23,81%. Konduktivitas

optik lapisan AgNWs diperoleh sekitar 1,8-2,32 x 105 S.m
-1
, indeks bias sekitar
1,93 hingga 2,26 dan energi gap lapisan AgNWs diperoleh sekitar 3,79 hingga
3,84 eV. Meningkatnya perulangan, mengakibatkan ketebalan dan konduktivitas
optik semakin meningkat serta resistansi dan transmitansi semakin menurun.
Kata kunci: Energi gap, Ketebalan Lapisan, Konduktivitas Optik, Lapisan

AgNWs, Transmitansi
Transparent Conductive Electrode (TCE) film based on silver nanowires
(AgNWs) were fabricated onto a polycarbonate (PC) substrate with variation
cycle using spray coating technique. AgNWs were synthesized using polyvinyl
pyrrolidone (PVP) by polyol method. AgNWs obtained has diameter and length of
17.13 nm and 28.58 ?m, respectively. The AgNWs film produces lowest sheet
resistance at 3 cycle of 4.98 ?/sq with a transmittance of 23.81 %. The optical
conductivity of AgNWs film was obtained about 1.8-2.32 x 105Sm-1

, the refractive
index obtained about 1,93 to 2.26 and the band gap energy obtained about 3.79 to
3.84 eV. Increased cycle, affect the thickness and optical conductivity increases
and resistance and transmittance decreases.
Keywords: AgNWs Film, Layers Thickness, Optical Conductivity, Sheet Resistance, Transmittance
%C UNIVERSITAS LAMPUNG
%D 2019
%I FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM
%L eprints57517