<> "The repository administrator has not yet configured an RDF license."^^ . <> . . "EFEK KANDUNGAN Ce2O3 TERHADAP STRUKTUR DAN SERAPAN\r\nGELOMBANG MIKRO MATERIAL Ni0,5Zn0,5CeXFe(2-X)O4"^^ . "Synthesis of Ni0,5Zn0,5CexFe(2-x)O4 (x = 0,010; 0,015; 0,020; 0,025; and 0,030)\r\nmicrowave wave absorbers was carried out using a solid reaction method with\r\nsintering 1.2000C for 5 hours. This research was conducted to determine the effect\r\nion substitution of Ce3+ on the morphologi structure and absorption properties of\r\nNi0,5Zn0,5CexFe(2-x)O4 material. The existence of a single phase was found in all\r\nsamples with a value of x = 0,010; 0,015; 0,020; 0,025; and 0,030 and have been\r\nidentified by using XRD. The phase lattice parameter of Ni0,5Zn0,5Fe2O4 was\r\ndecreases by increasing levels of Ce3 + ions. Observation of morphology using SEM\r\nshows the formation of particles which tend to be homogeneous and the results of\r\nEDS show that the levels of Ce3 + ions increase as x values are added.Whereas the\r\nabsorption ability of microwaves as measured by VNA shows a maximum\r\nreflection loss (RL) value of -16.43 dB obtained in samples with a value of x =\r\n0.030. Which means that Ni0,5Zn0,5CexFe(2-x)O4 material is able to absorb\r\nmicrowaves at 97.73% at a frequency of 10.80 GHz.\r\n\r\nKeywords: Cerium oxide, Nicel zinc ferrite, and Microwave absorption.\r\nTelah dilakukan sintesis penyerap gelombang mikro Ni0,5Zn0,5CeXFe(2-X)O4 (x =\r\n0,010; 0,015; 0,020; 0,025; dan 0,030) menggunakan metode reaksi padatan\r\ndengan pemanasan pada suhu 1.2000C selama 5 jam. Penelitian ini dilakukan untuk\r\nmengetahui pengaruh subtitusi ion Ce3+ terhadap struktur morfologi dan sifat\r\npenyerapan bahan Ni0,5Zn0,5CeXFe(2-X)O4. Keberadaan fasa tunggal terdapat pada\r\nsemua sampel dengan nilai x = 0,010; 0,015; 0,020; 0,025; dan 0,030 dan telah\r\ndiidentifikasi dengan menggunakan XRD. Parameter kisi fasa Ni0,5Zn0,5Fe2O4\r\nmenurun seiring dengan peningkatan kadar ion Ce3+. Pengamatan morfologi\r\ndengan menggunakan SEM menunjukan terbentuknya partikel yang cenderung\r\nhomogen dan hasil EDS menunjukan bahwa kadar ion Ce3+ meningkat seiring\r\nditambahkan nilai x . Sedangkan kemampuan penyerapan gelombang mikro yang\r\ndiukur dengan alat VNA menunjukan nilai reflection loss (RL) maksimum sebesar\r\n-16,43 dB diperoleh pada sampel dengan nilai x = 0,030. Yang mengartikan\r\nbahwa material Ni0,5Zn0,5CeXFe(2-X)O4 mampu menyerap gelombang mikro sebesar\r\n97,73% pada frekuensi 10,80 GHz.\r\n\r\nKata kunci: Cerium oksida, Nicel zinc ferrit, dan Penyerapan gelombang mikro."^^ . "2019" . . . . . "FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM"^^ . . . . . . . "1517041056"^^ . "Dinda Rizki Amelia"^^ . "1517041056 Dinda Rizki Amelia"^^ . . . . . . "EFEK KANDUNGAN Ce2O3 TERHADAP STRUKTUR DAN SERAPAN\r\nGELOMBANG MIKRO MATERIAL Ni0,5Zn0,5CeXFe(2-X)O4 (File PDF)"^^ . . . "1. ABSTRAK.pdf"^^ . . . "EFEK KANDUNGAN Ce2O3 TERHADAP STRUKTUR DAN SERAPAN\r\nGELOMBANG MIKRO MATERIAL Ni0,5Zn0,5CeXFe(2-X)O4 (File PDF)"^^ . . . "EFEK KANDUNGAN Ce2O3 TERHADAP STRUKTUR DAN SERAPAN\r\nGELOMBANG MIKRO MATERIAL Ni0,5Zn0,5CeXFe(2-X)O4 (File PDF)"^^ . . . "3. SKRIPSI FULL TANPA BAB PEMBAHASAN.pdf"^^ . . . "EFEK KANDUNGAN Ce2O3 TERHADAP STRUKTUR DAN SERAPAN\r\nGELOMBANG MIKRO MATERIAL Ni0,5Zn0,5CeXFe(2-X)O4 (Other)"^^ . . . . . . "indexcodes.txt"^^ . . . "EFEK KANDUNGAN Ce2O3 TERHADAP STRUKTUR DAN SERAPAN\r\nGELOMBANG MIKRO MATERIAL Ni0,5Zn0,5CeXFe(2-X)O4 (Other)"^^ . . . . . . "EFEK KANDUNGAN Ce2O3 TERHADAP STRUKTUR DAN SERAPAN\r\nGELOMBANG MIKRO MATERIAL Ni0,5Zn0,5CeXFe(2-X)O4 (Other)"^^ . . . . . . "indexcodes.txt"^^ . . . "EFEK KANDUNGAN Ce2O3 TERHADAP STRUKTUR DAN SERAPAN\r\nGELOMBANG MIKRO MATERIAL Ni0,5Zn0,5CeXFe(2-X)O4 (Other)"^^ . . . . . . "lightbox.jpg"^^ . . . "EFEK KANDUNGAN Ce2O3 TERHADAP STRUKTUR DAN SERAPAN\r\nGELOMBANG MIKRO MATERIAL Ni0,5Zn0,5CeXFe(2-X)O4 (Other)"^^ . . . . . . "preview.jpg"^^ . . . "EFEK KANDUNGAN Ce2O3 TERHADAP STRUKTUR DAN SERAPAN\r\nGELOMBANG MIKRO MATERIAL Ni0,5Zn0,5CeXFe(2-X)O4 (Other)"^^ . . . . . . "medium.jpg"^^ . . . "EFEK KANDUNGAN Ce2O3 TERHADAP STRUKTUR DAN SERAPAN\r\nGELOMBANG MIKRO MATERIAL Ni0,5Zn0,5CeXFe(2-X)O4 (Other)"^^ . . . . . . "small.jpg"^^ . . . "EFEK KANDUNGAN Ce2O3 TERHADAP STRUKTUR DAN SERAPAN\r\nGELOMBANG MIKRO MATERIAL Ni0,5Zn0,5CeXFe(2-X)O4 (Other)"^^ . . . . . . "EFEK KANDUNGAN Ce2O3 TERHADAP STRUKTUR DAN SERAPAN\r\nGELOMBANG MIKRO MATERIAL Ni0,5Zn0,5CeXFe(2-X)O4 (Other)"^^ . . . . . . "EFEK KANDUNGAN Ce2O3 TERHADAP STRUKTUR DAN SERAPAN\r\nGELOMBANG MIKRO MATERIAL Ni0,5Zn0,5CeXFe(2-X)O4 (Other)"^^ . . . . . . "EFEK KANDUNGAN Ce2O3 TERHADAP STRUKTUR DAN SERAPAN\r\nGELOMBANG MIKRO MATERIAL Ni0,5Zn0,5CeXFe(2-X)O4 (Other)"^^ . . . . . . "EFEK KANDUNGAN Ce2O3 TERHADAP STRUKTUR DAN SERAPAN\r\nGELOMBANG MIKRO MATERIAL Ni0,5Zn0,5CeXFe(2-X)O4 (Other)"^^ . . . . . . "lightbox.jpg"^^ . . . "EFEK KANDUNGAN Ce2O3 TERHADAP STRUKTUR DAN SERAPAN\r\nGELOMBANG MIKRO MATERIAL Ni0,5Zn0,5CeXFe(2-X)O4 (Other)"^^ . . . . . . "preview.jpg"^^ . . . "EFEK KANDUNGAN Ce2O3 TERHADAP STRUKTUR DAN SERAPAN\r\nGELOMBANG MIKRO MATERIAL Ni0,5Zn0,5CeXFe(2-X)O4 (Other)"^^ . . . . . . "medium.jpg"^^ . . . "EFEK KANDUNGAN Ce2O3 TERHADAP STRUKTUR DAN SERAPAN\r\nGELOMBANG MIKRO MATERIAL Ni0,5Zn0,5CeXFe(2-X)O4 (Other)"^^ . . . . . . "small.jpg"^^ . . "HTML Summary of #57520 \n\nEFEK KANDUNGAN Ce2O3 TERHADAP STRUKTUR DAN SERAPAN \nGELOMBANG MIKRO MATERIAL Ni0,5Zn0,5CeXFe(2-X)O4\n\n" . "text/html" . . . "500 ilmu pengetahuan alam dan matematika" . . . "530 Fisika" . .