title: PENGARUH VARIASI PERBANDINGAN MASSA ASPAL DENGAN
SILIKA TERHADAP STRUKTUR, SIFAT TERMAL,
FISIS, DAN MEKANIK SILIKA ASPAL
ispublished: pub
subjects: 500
subjects: 530
full_text_status: restricted
abstract: Penelitian ini bertujuan untuk mengetahui pengaruh variasi perbandingan massa
aspal dengan silika terhadap struktur, sifat termal, fisis (daya serap air), dan
mekanik (kuat tekan) silika aspal. Silika sekam padi diperoleh dari hasil ekstraksi
alkalis menggunakan larutan NaOH 1,5 % dan HNO3 10 % . Pembuatan paduan
silika aspal dilakukan dengan perbandingan massa silika dan aspal yaitu 1:0;
1:0,7; 1:0,8; dan 1:0,9 pada suhu pencampuran 160 oC dan dipanaskan pada suhu
150 oC selama 3 jam. Hasil analisis XRD memperlihatkan struktur amorf yang
sama. Penambahan aspal mengakibatkan teridentifikasi adanya karbon pada 2θ =
20,04o
dan terjadi pergeseran 2θ intensitas tertinggi silika amorf dari 22,45
menjadi 22,56o

. Hasil analisis TGA/DTA memperlihatkan bahwa penambahan
aspal mengakibatkan penyusutan massa meningkat hingga 32 % serta peningkatan
suhu endotermik dan eksotermik. Penambahan aspal juga mengakibatkan
terjadinya penurunan nilai daya serap air dan kuat tekan.
Kata kunci: aspal, sifat termal, sifat fisis, silika sekam padi, struktur.
This study aims to determine the effect of variations in mass ratio asphalt with
silica on the structure, thermal properties, physical (water absorption), and
mechanical (compressive strength) asphalt silica. Rice husk silica was obtained
from the alkaline extraction using NaOH 1,5% solution and HNO3 10 %. The
mass ratio of silica and asphalt alloys were 1:0; 1:0,7; 1:0,8; and 1:0,9. Silica
and asphalt were mixed at 160 oC followed by calcinations at 150 oC for 3 hours.
The XRD analysis results show the same amorphous structure. The addition of
asphalt resulted in the identification of carbon around 2θ = 20,04o

and a shift of

2θ the highest intensity of silica from 22,45 to 22,56o

. TGA/DTA analysis result
show that the addition of asphalt causes the mass loss increasing up to 32 % and
an increasing in endothermic and exothermic temperatures. The addition of
asphalt also causes the value of water absorption and compressive strength to
decreases.
Keywords: asphalt, physical properties, silica rice husk, structure, thermal

properties.
date: 2019
date_type: published
publisher: FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM
place_of_pub: UNIVERSITAS LAMPUNG
citation:   Reka Puspitasari, 1517041082  (2019) PENGARUH VARIASI PERBANDINGAN MASSA ASPAL DENGAN SILIKA TERHADAP STRUKTUR, SIFAT TERMAL, FISIS, DAN MEKANIK SILIKA ASPAL.  FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.     
document_url: http://digilib.unila.ac.id/57529/1/1.%20ABSTRAK.pdf
document_url: http://digilib.unila.ac.id/57529/2/3.%20SKRIPSI%20FULL%20TANPA%20BAB%20PEMBAHASAN.pdf
document_url: http://digilib.unila.ac.id/57529/3/2.%20SKRIPSI%20FULL.pdf