title: PENGARUH TEMPERATUR DAN WAKTU REDUKSI TERHADAP  PERUBAHAN FASA BIJIH MANGAN DARI NUSA TENGGARA TIMUR  MENGGUNAKAN ARANG KAYU SEBAGAI REDUKTOR
creator: SOFHIA CHAIRUNNISYA, 1417041087
subject: 500 ilmu pengetahuan alam dan matematika
subject: 530 Fisika
description: Telah dilakukan penelitian mengenai pengaruh temperatur dan waktu reduksi  terhadap perubahan fasa bijih mangan dari Nusa Tenggara Timur menggunakan  arang kayu sebagai reduktor. Reduksi bijih mangan dilakukan dengan metode  pirometalurgi. Pada tahap pertama dilakukan reduksi dengan variabel temperatur  900, 1000, dan 1100 °C dengan waktu reduksi dibuat tetap yaitu 15 menit. Setelah  itu dilakukan proses reduksi dengan variabel waktu reduksi 30, 45, 60, dan 75  menit menggunakan temperatur terbaik yang diketahui dari tahap sebelumnya.  Hasil analisis XRF menunjukkan bahwa temperatur dan waktu reduksi  berpengaruh pada peningkatan kadar Mn pada bijih Mangan. Kadar Mn tertinggi  mencapai 77,985 % didapatkan menggunakan temperatur 1100 °C dan waktu  reduksi 45 menit. Hasil karakterisasi XRD menunjukkan bahwa raw material  bijih mangan setelah direduksi mengalami perubahan fasa dan struktur mineral.  Perubahan fasa yang terjadi adalah fasa pyrolusite (MnO2) menjadi fasa bixbyite  (Mn2O3), braunite (Mn2SiO4) dan Hausmannite (Mn3O4). Perubahan struktur  mineral yang terjadi adalah pyrolusite dan bixbyite berbentuk kubik menjadi  bixbyite, braunite, dan hausmannite berbentuk tetragonal. Model kinetika yang  sesuai merepresentasikan reduksi bijih Mn pada penelitian ini adalah model  kinetika Ginstling-Brounshtein dengan energi aktivasi (Ea) yang didapat sebesar  9,573 kkal/mol, sehingga laju reduksi dikendalikan oleh reaksi kimia dan difusi  gas.  Kata Kunci : Bijih Mangan, Perubahan Fasa, Reduksi, Struktur Mineral.  Effect of temperature and reduction time to phase transformation on east nusa  tenggara manganese ore using charcoal as reductant has been researched.  Reduction of manganese ore was carried out by pyometallurgy method. In the first  step, reduction was carried out with temperature variables of 900, 1000, and  1100 °C with the reduction time being fixed at 15 minutes. After that the reduction  process is carried out with the reduction time variables 30, 45, 60, and 75 minutes  using the best temperature known from the previous stage. The X-Ray  Fluorescence (XRF) characterization result showed that the temperature and the  reduction time influeced increasing Mn content on manganese ore. The highest  Mn content reaching 77.985% was obtained using a temperature 1100 ° C and a  45 minute reduction time. The X-Ray Diffraction (XRD) characterization result  showed that raw material of manganese ore reduced after being reduced had  transformation of phase and structure mineral. The transformation phase that  occur were the pyrolusite (MnO2) phase became the bixbyite (Mn2O3), braunite  (Mn2SiO4) and Hausmannite (Mn3O4) phases. The transformation in mineral  structures that occur were pyrolusite and bixbyite in the form of cubic to bixbyite,  braunite, and Hausmannite in the form of tetragonal.The suitable kinetic model  with activation energy (Ea) obtained at 9,573 kcal / mol. The rate of reduction  was controlled by chemical reaction and gas diffusion.  Keywords: Manganese Ore, Phase Transformation, Reduction, Mineral Structure.
publisher: FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM
date: 2019
type: Skripsi
type: NonPeerReviewed
format: text
identifier: http://digilib.unila.ac.id/57534/1/1.%20ABSTRAK.pdf
format: text
identifier: http://digilib.unila.ac.id/57534/2/2.%20SKRIPSI%20FULL.pdf
format: text
identifier: http://digilib.unila.ac.id/57534/3/3.%20SKRIPSI%20FULL%20TANPA%20BAB%20PEMBAHASAN.pdf
identifier:   SOFHIA CHAIRUNNISYA, 1417041087  (2019) PENGARUH TEMPERATUR DAN WAKTU REDUKSI TERHADAP PERUBAHAN FASA BIJIH MANGAN DARI NUSA TENGGARA TIMUR MENGGUNAKAN ARANG KAYU SEBAGAI REDUKTOR.  FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.     
relation: http://digilib.unila.ac.id/57534/