%A 1517041037 ANI SETIAWATI %T PENGENDALIAN LAJU KOROSI BAJA St37 DALAM MEDIUM NaCl 3% MENGGUNAKAN INHIBITOR EKSTRAK DAUN SIDAGURI (Sida rhombifolia L.) %X Ekstrak daun sidaguri digunakan sebagai inhibitor korosi pada baja St37 yang direndam dalam medium korosif NaCl 3%. Analisis awal kandungan senyawa menggunakan uji tanin dan analisis FTIR yang menunjukkan bahwa ekstrak daun sidaguri memiliki kandungan tanin. Penelitian ini menggunakan inhibitor ekstrak daun sidaguri dan inhibitor pabrikan yang memiliki zat anti korosi. Inhibitor ekstrak daun sidaguri konsentrasi 0, 1, 2, 3, dan 4% serta inhibitor pabrikan yang direndam dalam medium NaCl 3% selama 144 jam. Pengujian laju korosi dilakukan dengan metode pengurangan massa. Hasil penelitian menunjukkan bahwa peningkatan pengurangan massa menurunkan laju korosi. Efisiensi maksimum inhibitor ekstrak daun sidaguri adalah 86,154 ? 0,0008 % pada konsentrasi 4%. Sampel dikarakterisasi dengan XRD yang menunjukkan bahwa fase yang terbentuk adalah Fe murni dengan bidang kisi 110, 200, dan 211. Hasil karakterisasi SEM pada sampel dengan inhibitor ekstrak daun sidaguri 4% terlihat produk korosi yang terbentuk lebih sedikit, dengan hasil EDS menunjukkan bahwa persentase Fe lebih besar dibandingkan dengan inhibitor ekstrak daun sidaguri dengan konsentrasi 1%. Kata kunci. Inhibitor korosi, daun sidaguri, baja karbon St37, dan NaCl Sidaguri leaves extract is used as a corrosion inhibitor in St37 steel soaked in 3% NaCl corrosive medium. Initial analysis of the compound content using tannin tests and FTIR analysis showed that sidaguri leaves extract has tannin content. This research used and commercial anti-corrosion substances as inhibitor. 0, 1, 2, 3, and 4% concentrations of and commercial inhibitor were immersed in 3% of NaCl medium for of 24 hours. Corrosion rate was analized using mass reduction method. The results showed that increasing of mass reduction decreased the corrosion rate. Maximum efficiency of sidaguri leaves extract inhibitor was 86.154 ? 0,0008 % in 4% concentration. Samples were characterized by XRD which showed that the formed phase was pure Fe with 110, 200, and 211 lattice plane. The results of SEM characterization on samples with 4% sidaguri leaves extract inhibitor has less formed of corrosion products with EDS results showed that Fe percentage was greater than 1% concentrations of sidaguri leaves extract. Key words. corrosion inhibitor, sidaguri leaves, St37 steel, and NaCl %C UNIVERSITAS LAMPUNG %D 2019 %I FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM %L eprints57556