N2  - Pembuatan paving block dilakukan dengan proses pencetakan, perawatan,
pengujian fisik meliputi kuat tekan, berat jenis, absorpsi, porositas, dan susut
bakar, serta karakterisasi meliputi XRF dan XRD. Paving block ini dibuat dengan
tanpa penambahan mineral slag dan dengan penambahan mineral slag 5%, 15%,
25%, dan 35% dengan tingkat kehalusan mesh 60 dan 80. Bahan baku yang
digunakan yaitu semen, pasir, batuan andesit dan air. Proses ini menunjukkan
hasil bahwa semakin besar variasi konsentrasi mineral slag maka kuat tekan, berat
jenis, dan susut bakar yang dihasilkan semakin kecil, serta absorpsi dan porositas
semakin besar. Paving block tanpa penambahan mineral slag memiliki kuat tekan
sebesar 8,612 MPa dan absorpsi sebesar 8,89%, sedangkan dengan penambahan
mineral slag 5% pada mesh 60 dan mesh 80 memiliki kuat tekan secara berurutan
sebesar 9,115 MPa dan 9,652 MPa, serta nilai absorpsi sebesar 6,61% dan 5,88%.
Sehingga paving block pada penelitian ini termasuk ke dalam paving block tipe D
yang biasa digunakan untuk taman. Karakterisasi XRF menunjukkan bahwa
semakin banyak konsentrasi slag maka CaO yang terkandung dalam paving block
semakin berkurang sedangkan SiO2 semakin bertambah. Hasil karakterisasi XRD
menunjukkan bahwa fasa yang terbentuk yaitu fasa Gismondine, Calcite, C-S-H
dan Quartz. Kata kunci. Paving block, mineral slag, kuat tekan, berat jenis, absorpsi,

porositas, susut bakar, XRF, dan XRD.
Paving Block making process is done with the process of making test objects,
printing, maintenance, physical testing includes strong press, density, absorption,
porosity, and grilled shrink , as well as characterization including XRF and XRD.
Paving Block is made with no addition of slag minerals and with the addition of
the mineral slag 5%, 15%, 25%, and 35% with the smoothness level of mesh 60
and 80. The raw materials used are cement, sand, andesite rocks and water. This
process shows that the greater variation in the concentration of slag minerals then
strong press, type weight, and grilled shrink become smaller, and the absorption
and porosity are getting bigger. Paving Block without additions of slag mineral
has a strong press of 8.612 MPa and absorption of 8.89%, while with the addition
of slag mineral 5% on mesh No. 60 and mesh No. 80 has strong press of 9.115
MPa and 9.652 MPa, as well as absorption value of 6.61% and 5.88%. So Paving
Block in this study included in type D Paving Block that commonly used for
parks. XRF characterization shows that the more concentration of slag then the
CaO contained in the paving block is decrease while SiO2 is increase . XRD
characterization results shows that the phases formed are the gismondine, calcite, C-S-H and Quartz phases. Keywords. Paving Block, Slag Mineral, Strong press, density, Absorption,

porosity, grilled shrink , XRF, and XRD.