%T ANALISIS PERAMBATAN RETAK FATIK BAJA AISI 1020  YANG DICELUP PANAS ALUMINIUM DAN DIBERI    PERLAKUAN PANAS ANIL
%U http://digilib.unila.ac.id/58830/
%X American Institute and Steel Iron (AISI) 1020 has a carbon content of 0.20wt% with  elemental alloys : 0.175 C, 99.23 Fe, 0.42 Mn, 0.055 P and 0.060 S (Matweb,2018).  This steel has a high ductility and can be treated according to the desire neds, such as  annealing and quenching prosesses. AISI 1020 stell can also be dipped in aluminium  and given heat treatment, then tensile testing is carried out to get its mechanical  strength value, after which a faigue crack propagation test and microstructure testing  are performed to determined the phenomena that occur.    Keywords : tensile testing, fatigue crack propagation testing, AISI 1020 Steel,  annealing, quenching  Baja standard American Institute and Steel Iron (AISI) 1020 memiliki kandungan  karbon 0.20wt% dengan elemen-elemen paduannya : 0.175 C, 99.23 Fe, 0.42 Mn,  0.055 P dan 0.060 S (Matweb, 2018). Baja ini memiliki keuletan yang tinggi dan  dapat diberi perlakuan sesuai dengan kebutuhan yang diinginkan, seperti proses  annealing dan quenching. Baja AISI 1020 juga bias dicelup aluminium dan diberi  perlakuan panas, lalu dilakukan pengujian tarik untuk mendapatkan nilai kekuatan  mekaniknya, setelah itu dilakukan pengujian perambatan retak fatik dan pengujian  struktur mikro untuk mengetahui fenomena yan terjadi.  Kata Kunci: uji tarik, uji fatik, baja AISI 1020, annealing, quenching.