%T PENGARUH SUHU DAN WAKTU PEMANASAN TERHADAP ANALISIS  DAN UJI FISIS GERABAH  (Skripsi)
%U http://digilib.unila.ac.id/59173/
%X Penelitian ini bertujuan untuk mengetahui kakrakterisitik dan kualitas gerabah  komposisi 65% mineral lempung dan 35% mineral feldspar. Sampel gerabah  dipanaskan pada variasi suhu 800ºC, 900ºC, 950ºC dan 1000ºC dan waktu 2, 3, 4  dan 5 jam. Hasil yang diperoleh menunjukkan bahwa nilai densitas=2,28  gram/cm3  dan kuat tekan=8,96Mpa optimum pada waktu tahan 3 jam suhu  1000ºC. Nilai uji absorbsi dan porositas menurun seiring naiknya suhu  pemanasan. Berdasarkan karakterisasi XRF bahan baku gerabah mengandungan  unsur Si=56,405% dan Al=18,927%. Hasil uji XRD waktu pemanasan 3 jam  variasi suhu 800-1000ºC puncak fasa tertinggi didominasi quartz (PDF-461045)  dengan rentan puncak 2θ(26º-28,7º). Fasa lain yang terbentuk yaitu cristobalite  (PDF-391425) dan tridymite (PDF-421401). Mulai suhu 900ºC terjadi ikatan  Al2SiO5 fasa sillimanite (PDF-380471).  Kata kunci: feldspar, gerabah, sifat fisis, XRD, XRF  This study aims to know the characteristics and quality of pottery with the  composition of 65% clay and 35% feldspart mineral. Pottery samples were heated  at temperature variations of 800ºC, 900ºC, 950ºC and 1000ºC and time 2, 3, 4 and  5 hours. The results obtained showed that the density value=2,28 gram/cm3  and  compressive srength=8,96 Mpa optimum in 3 hour time heating and 1000ºC  temperature. The value of absorbtion and porosity decreases with increasing  heating temperature. Based on XRF characterization pottery containing  Si=56,405% and Al=18,927%. The XRD test at 800-1000ºC temperature and 3  hour time heating was domination with quartz phase (PDF-461045) at 2θ(26º28,7º) peak. Another phase was formed are cristobalite (PDF-391425) dan  tridymite (PDF-421401). Starting at 900ºC Al2SiO5 was bonding sillimanite  phase (PDF-380471).  Keywords: feldspart, pottery, physical properties, XRD, XRF