%A 1317041021 Latifah Desti Lustikasari 
%T PENGARUH SUHU DAN WAKTU PEMANASAN TERHADAP ANALISIS
DAN UJI FISIS GERABAH
(Skripsi)
%X Penelitian ini bertujuan untuk mengetahui kakrakterisitik dan kualitas gerabah
komposisi 65% mineral lempung dan 35% mineral feldspar. Sampel gerabah
dipanaskan pada variasi suhu 800?C, 900?C, 950?C dan 1000?C dan waktu 2, 3, 4
dan 5 jam. Hasil yang diperoleh menunjukkan bahwa nilai densitas=2,28
gram/cm3
dan kuat tekan=8,96Mpa optimum pada waktu tahan 3 jam suhu
1000?C. Nilai uji absorbsi dan porositas menurun seiring naiknya suhu
pemanasan. Berdasarkan karakterisasi XRF bahan baku gerabah mengandungan
unsur Si=56,405% dan Al=18,927%. Hasil uji XRD waktu pemanasan 3 jam
variasi suhu 800-1000?C puncak fasa tertinggi didominasi quartz (PDF-461045)
dengan rentan puncak 2?(26?-28,7?). Fasa lain yang terbentuk yaitu cristobalite
(PDF-391425) dan tridymite (PDF-421401). Mulai suhu 900?C terjadi ikatan
Al2SiO5 fasa sillimanite (PDF-380471).
Kata kunci: feldspar, gerabah, sifat fisis, XRD, XRF
This study aims to know the characteristics and quality of pottery with the
composition of 65% clay and 35% feldspart mineral. Pottery samples were heated
at temperature variations of 800?C, 900?C, 950?C and 1000?C and time 2, 3, 4 and
5 hours. The results obtained showed that the density value=2,28 gram/cm3
and
compressive srength=8,96 Mpa optimum in 3 hour time heating and 1000?C
temperature. The value of absorbtion and porosity decreases with increasing
heating temperature. Based on XRF characterization pottery containing
Si=56,405% and Al=18,927%. The XRD test at 800-1000?C temperature and 3
hour time heating was domination with quartz phase (PDF-461045) at 2?(26?28,7?) peak. Another phase was formed are cristobalite (PDF-391425) dan
tridymite (PDF-421401). Starting at 900?C Al2SiO5 was bonding sillimanite
phase (PDF-380471).
Keywords: feldspart, pottery, physical properties, XRD, XRF
%C UNIVERSITAS LAMPUNG
%D 2019
%I FAKULTAS ILMU KEGURUAN DAN ILMU PENDIDIKAN
%L eprints59173