title: PENGARUH SUHU DAN WAKTU PEMANASAN TERHADAP ANALISIS
DAN UJI FISIS GERABAH
(Skripsi)
ispublished: pub
subjects: 370
subjects: 540
full_text_status: restricted
abstract: Penelitian ini bertujuan untuk mengetahui kakrakterisitik dan kualitas gerabah
komposisi 65% mineral lempung dan 35% mineral feldspar. Sampel gerabah
dipanaskan pada variasi suhu 800ºC, 900ºC, 950ºC dan 1000ºC dan waktu 2, 3, 4
dan 5 jam. Hasil yang diperoleh menunjukkan bahwa nilai densitas=2,28
gram/cm3
dan kuat tekan=8,96Mpa optimum pada waktu tahan 3 jam suhu
1000ºC. Nilai uji absorbsi dan porositas menurun seiring naiknya suhu
pemanasan. Berdasarkan karakterisasi XRF bahan baku gerabah mengandungan
unsur Si=56,405% dan Al=18,927%. Hasil uji XRD waktu pemanasan 3 jam
variasi suhu 800-1000ºC puncak fasa tertinggi didominasi quartz (PDF-461045)
dengan rentan puncak 2θ(26º-28,7º). Fasa lain yang terbentuk yaitu cristobalite
(PDF-391425) dan tridymite (PDF-421401). Mulai suhu 900ºC terjadi ikatan
Al2SiO5 fasa sillimanite (PDF-380471).
Kata kunci: feldspar, gerabah, sifat fisis, XRD, XRF
This study aims to know the characteristics and quality of pottery with the
composition of 65% clay and 35% feldspart mineral. Pottery samples were heated
at temperature variations of 800ºC, 900ºC, 950ºC and 1000ºC and time 2, 3, 4 and
5 hours. The results obtained showed that the density value=2,28 gram/cm3
and
compressive srength=8,96 Mpa optimum in 3 hour time heating and 1000ºC
temperature. The value of absorbtion and porosity decreases with increasing
heating temperature. Based on XRF characterization pottery containing
Si=56,405% and Al=18,927%. The XRD test at 800-1000ºC temperature and 3
hour time heating was domination with quartz phase (PDF-461045) at 2θ(26º28,7º) peak. Another phase was formed are cristobalite (PDF-391425) dan
tridymite (PDF-421401). Starting at 900ºC Al2SiO5 was bonding sillimanite
phase (PDF-380471).
Keywords: feldspart, pottery, physical properties, XRD, XRF
date: 2019
date_type: published
publisher: FAKULTAS ILMU KEGURUAN DAN ILMU PENDIDIKAN
place_of_pub: UNIVERSITAS LAMPUNG
citation:   Latifah Desti Lustikasari , 1317041021  (2019) PENGARUH SUHU DAN WAKTU PEMANASAN TERHADAP ANALISIS DAN UJI FISIS GERABAH (Skripsi).  FAKULTAS ILMU KEGURUAN DAN ILMU PENDIDIKAN, UNIVERSITAS LAMPUNG.     
document_url: http://digilib.unila.ac.id/59173/1/ABSTRAK.pdf
document_url: http://digilib.unila.ac.id/59173/2/SKRIPSI%20FULL.pdf
document_url: http://digilib.unila.ac.id/59173/3/SKRIPSI%20TANPA%20BAB%20PEMBAHASAN.pdf