           title = {PEMBUATAN DAN KARAKTERISASI PLASTIK BIODEGRADABLE CAMPURAN PATI DARI TEPUNG TAPIOKA DAN LDPE MENGGUNAKAN SINGLE SCREW EXTRUDER 



},
          author = {1017011037 Lailatul Hasanah},
         address = {Universitas Lampung},
       publisher = {Fakultas MIPA},
            year = {2014},
             url = {http://digilib.unila.ac.id/6011/},
        abstract = {ABSTRAK


PEMBUATAN DAN KARAKTERISASI PLASTIK BIODEGRADABLE CAMPURAN PATI DARI TEPUNG TAPIOKA DAN LDPE MENGGUNAKAN SINGLE SCREW EXTRUDER 

Oleh


LAILATUL HASANAH


Telah dilakukan penelitian pembuatan plastik dari campuran pati dari tepung tapioka dan LDPE menggunakan single screw extruder. Tujuan dari percoban ini adalah untuk membuat material yang ramah lingkungan. Untuk mendapatkan Film plastik campuran Low Density Polietilen (LDPE) dan pati termoplastik telah dilakukan dengan memvariasikan komposisi pati termoplastik 0\%, 1\%, 5\%, dan 10\% dari jumlah sampel yang digunakan sebanyak 50 gram dengan komposisi pati termoplastik terdiri dari gliserol dan aquades. Hasil penelitian menunjukan bahwa plastik yang dihasilkan bersifat sedikit kaku akibat penambahan pati termoplastik dalam LDPE.  Karakterisasi plastik dilakukan dengan menggunakan instrumen DSC dan TGA.  Data termogram DSC dan TGA menunjukan bahwa penambahan PTP pada LDPE dan ketidakhomogenan campuran PTP-LDPE tidak berpengaruh pada pergeseran titik leleh (Tm) namun berpengaruh terhadap Tg dan laju dekomposisi plastik. Hasil analisis FTIR menunjukkan bahwa sampel telah tercampur yang ditandai dengan pergeseran bilangan gelombang


Kata kunci :Pati, LDPE, Differential Scanning Calorymetry
                    (DSC), Thermal Gravimetry Analyser (TGA)


ABSTRACT


PREPARATION AND CHARACTERIZATION
OF PLASTIC MIXTURE OF FLOUR TAPIOCA STARCH AND LDPE 
USING SINGLE SCREW EXTRUDER


By


LAILATUL HASANAH

The green material plastic made from starch of tapioca flour and Low Density
Polietilen (LDPE) using a single screw extruder was conducted.The mixture of
Plastic film Low Density Polyethylene(LDPE) and thermoplastic starch(PTP) has
Been carried out by varying the composition of thermoplastic starch 0\%, 1\%, 5\%,
and10\% of thenumber of  samples used as much as 50 grams of the thermoplastic starch composition contains glycerol and distilled water. The results show that the plastic produced are slightly more rigid due to the addition of thermoplastic starch to the LDPE. Plastic characterization was performed using DSC and TGA instrument. DSC and TGA thermogram showed that the addition of the LDPE and irregularities PTP-LDPE mixture had no effecton the shift of the melting point(Tm) but the effect on the Tg and the rate of decomposition of plastics. A little shifting wavenumber in the FTIR spectrum indicates that the PTP and LDPE was mixed.


Keyword :Starch, LDPE, Differential Scanning Calorymetry
      (DSC), Thermal Gravimetry Analyser (TGA)
}
}