@misc{eprints60545,
           month = {Nopember},
           title = {EKSTRAKSI DAN KARAKTERISASI TiO2 DARI PASIR BESI
LAMPUNG MENGGUNAKAN METODE LEACHING HCl DENGAN
VARIASI WAKTU
},
          author = {1717041006 YUDHISTIRA NOVITA HANDAYANI},
         address = {UNIVERSITAS LAMPUNG},
       publisher = {Fakultas Teknik},
            year = {2021},
             url = {http://digilib.unila.ac.id/60545/},
        abstract = {Telah dilakukan penelitian ekstraksi dan karakterisasi TiO2 dari pasir besi
Lampung menggunakan metode leaching HCl dengan variasi waktu. Pasir besi
yang digunakan dalam penelitian ini berasal dari Pesisir Barat. Penelitian ini
bertujuan untuk mengetahui bagaimana komposisi, dan struktur fasa yang
terbentuk sebelum dan setelah proses leaching, serta mengetahui morfologi dan
kandungan elementer pada pasir besi setelah proses leaching. Variasi waktu
leaching yang digunakan yaitu 2, 3, 4, 5, dan 6 jam dengan konsentrasi larutan
HCl 12 M dan suhu leaching 110?C. Serbuk TiO2 dikalsinasi pada suhu 480?C
dengan waktu tahan 2 jam. Karakterisasi yang dilakukan yaitu X-Ray Flouresence
(XRF), X-Ray Diffraction (XRD), dan Scanning Electron Microscopy-Energy
Dispersive Spectroscopy (SEM-EDS). Hasil yang diperoleh pada analisis XRF
yaitu komposisi TiO2 terbesar diperoleh pada sampel dengan waktu leaching 2
jam yaitu sebesar 60,701\%. Difraktogram XRD menunjukkan bahwa fasa TiO2
yang terbentuk yaitu fasa rutil dan brukit. Morfologi permukaan yang terbentuk
yaitu berbentuk kumpulan butir dengan kandungan elementer Ti sebesar 0,03\%.
Berdasarkan hasil di atas, maka proses leaching dapat meningkatkan persentase
kadar kemurnian TiO2 pada pasir besi.
Kata kunci : Brukit, HCl, leaching, pasir besi, rutil, TiO2.

Research has been carried out on the extraction and characterization of TiO2
from Lampung iron sands using the HCl leaching method with time variations.
The iron sand used in this study obtained from the Pesisir Barat, Lampung
Province. This study aims to determine the composition and structure of the
phases formed before and after the leaching process, as well as to determine the
morphology and elementary content of iron sand after the leaching process. The
leaching time variations used are 2, 3, 4, 5, and 6 hours with HCl concentration
12 M and leaching temperature 110?C. TiO2 powder was calcined at 480?C with
a holding time of 2 hours. The characterizations carried out were X-Ray
Fluorescence (XRF), X-Ray Diffraction (XRD), and Scanning Electron
Microscopy-Energy Dispersive Spectroscopy (SEM-EDS). The results obtained in
XRF analysis that is the composition of the largest TiO2 obtained in samples with
a leaching time of 2 hours, i.e. 60.701\%. The XRD diffractogram shows that the
formed TiO2 phases are Rutile and Brookite phases. The surface morphology
formed is in the form of a collection of grains with an elementary content of Ti is
0.03\%. Based on the results, the leaching process by HCl can increase the purity
percentage of TiO2 in iron sand.
Keywords: Brookite, HCl, iron sand, leaching, rutile, TiO2.}
}