?url_ver=Z39.88-2004&rft_val_fmt=info%3Aofi%2Ffmt%3Akev%3Amtx%3Adc&rft.title=PEMBUATAN+LAPISAN+TIPIS+TiO2+BERBASIS+ILMENIT+LAMPUNG%0D%0AMENGGUNAKAN+METODE+CHEMICAL+BATH+DEPOSITION+(CBD)&rft.creator=NADIA+FEBRIYANTI%2C+1717041008&rft.subject=500+ilmu+pengetahuan+alam+dan+matematika&rft.subject=530+Fisika&rft.description=Telah+dilakukan+penelitian+pembuatan+lapisan+tipis+TiO2+berbasis+ilmenit+Lampung%0D%0Adengan+menggunakan+metode+Chemical+Bath+Deposition+(CBD).+Prekursor+yang%0D%0Adigunakan+dalam+pembuatan+lapisan+tipis+TiO2+pada+penelitian+ini+berupa+serbuk%0D%0Ahasil+ekstraksi+TiO2+dari+ilmenit+Lampung+dengan+kemurnian+sebesar+60%2C701%25.%0D%0ALapisan+tipis+TiO2+ditumbuhkan+pada+media+berupa+substrat+kaca.+Variasi+yang%0D%0Adigunakan+dalam+penumbuhan+lapisan+tipis+pada+penelitian+ini+berupa+waktu%0D%0Apelapisan+yaitu+2%2C+3%2C+4+dan+5+jam.+Setelah+proses+pelapisan%2C+substrat+kaca%0D%0Adikeringkan+dan+dikalsinasi+pada+suhu+500%EF%82%B0C+selama+4+jam.+Kemudian+dilakukan%0D%0Akarakterisasi+menggunakan+XRD+dan+SEM%2C+serta+dilakukan+pengukuran+nilai%0D%0Aresistivitas+dari+lapisan+tipis+dengan+menggunakan+metode+empat+titik.+Hasil+XRD%0D%0Amenunjukkan+bahwa+serbuk+hasil+ekstraksi+TiO2+dari+ilmenit+Lampung+didominasi%0D%0Aoleh+fasa+rutil+dan+brukit.+Sedangkan+untuk+lapisan+tipis+TiO2+yang+dihasilkan%0D%0Aberstruktur+amorf.+Morfologi+pada+semua+sampel+menunjukkan+bahwa+telah%0D%0Aterbentuk+struktur+berpori.+Berdasarkan+hasil+SEM+penampang+melintang%2C+pada%0D%0Asampel+dengan+waktu+pelapisan+3+jam+memiliki+ketebalan+lapisan+sebesar+7%2C28+%CE%BCm.%0D%0ABerdasarkan+pengukuran+resistivitas+didapatkan+hasil+bahwa+semakin+lama+waktu%0D%0Apelapisan+maka+semakin+besar+nilai+resistivitas+rata-ratanya.%0D%0AKata+Kunci%3A+Chemical+Bath+Deposition%2C+ilmenit%2C+lapisan+tipis%2C+TiO2%0D%0A%0D%0AResearch+has+been+carried+out+on+the+fabrication+of+thin+film+TiO2+based+on+ilmenite%0D%0Ain+Lampung+using+the+chemical+bath+deposition+(CBD)+method.+The+precursor+used%0D%0Ain+the+manufacture+of+TiO2+thin+films+in+this+study+was+a+powder+extracted+from%0D%0ATiO2+from+Lampung+ilmenite+with+a+purity+of+60.701%25.+A+thin+layer+of+TiO2+was%0D%0Agrown+on+a+medium+in+the+form+of+a+glass+substrate.+The+variation+used+in+the%0D%0Agrowth+of+the+thin+layer+in+this+study+were+2%2C+3%2C+4%2C+and+5+hours+coating+time.+After%0D%0Athe+coating+process%2C+the+glass+substrate+was+dried+and+calcined+at+500%0D%0A%EF%82%B0C+for+4%0D%0Ahours.+Then+the+characterization+was+carried+out+using+XRD%2C+SEM+and+the%0D%0Aresistivity+value+of+the+thin+layer+was+measured+using+the+four-point+method.+The%0D%0AXRD+results+showed+that+the+TiO2+powder+extracted+from+Lampung+ilmenite+was%0D%0Adominated+by+the+rutile+and+brookite+phases.+As+for+the+resulting+thin+layer+of+TiO2%2C%0D%0Athe+structure+is+amorphous.+The+morphology+of+all+samples+showed+that+a+porous%0D%0Astructure+had+been+formed.+Based+on+the+cross-sectional+SEM+results%2C+the+sample%0D%0Awith+a+coating+time+of+3+hours+had+a+layer+thickness+of+7%2C28+%CE%BCm.+Based+on+the%0D%0Aresistivity+measurement%2C+it+was+found+that+the+longer+the+coating+time%2C+the+greater%0D%0Athe+average+resistivity+value.%0D%0AKeywords%3A+chemical+bath+deposition%2C+ilmenite%2C+thin+film%2C+TiO2.&rft.publisher=Fakultas+Teknik&rft.date=2021-11-24&rft.type=Skripsi&rft.type=NonPeerReviewed&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F60551%2F1%2F1.%2520ABSTRAK%2520-%2520ALLIF%2520Printing%2520%25281%2529.pdf&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F60551%2F2%2F2.%2520SKRIPSI%2520FULL%2520-%2520ALLIF%2520Printing%2520%25281%2529.pdf&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F60551%2F3%2F3.%2520SKRIPSI%2520FULL%2520TANPA%2520BAB%2520PEMBAHASAN%2520-%2520ALLIF%2520Printing%2520%25281%2529.pdf&rft.identifier=++NADIA+FEBRIYANTI%2C+1717041008++(2021)+PEMBUATAN+LAPISAN+TIPIS+TiO2+BERBASIS+ILMENIT+LAMPUNG+MENGGUNAKAN+METODE+CHEMICAL+BATH+DEPOSITION+(CBD).++Fakultas+Teknik%2C+UNIVERSITAS+LAMPUNG.+++++&rft.relation=http%3A%2F%2Fdigilib.unila.ac.id%2F60551%2F