title: MEKANISME ADSORPSI INHIBITOR KOROSI OLIGOMER  4-VINILPIRIDIN PADA PERMUKAAN BAJA LUNAK    DALAM MEDIUM KOROSIF CO2
creator: TB. SOFI SUDIRMANO, 1617011014
subject: 500 ilmu pengetahuan alam dan matematika
subject: 540 Kimia dan ilmu yang berhubungan
description:     Oligomer 4-vinilpiridin yang digunakan pada penelitian ini telah difraksinasi  dengan menggunakan Sephadex LH-20 sebagai fase diam dan metanol sebagai  fase gerak. Fraksi-fraksi oligomer 4-vinilpiridin diuji aktivitasnya menggunakan  metode Electrochemical Impedance Spectroscopy (EIS) dengan konsentrasi  bervariasi (0, 25, 50, 100 dan 150 mg L-1    ) dan suhu bervariasi (30, 50 dan 70oC)  sebagai inhibitor korosi pada baja lunak dalam medium korosif CO2. Data persen  proteksi EIS digunakan untuk menentukan mekanisme adsorpsi menggunakan  empat model adsorpsi, yaitu: Temkin, Langmuir, Frumkin dan Flory-Huggins.    Permukaan baja lunak dianalisis menggunakan Scanning Electron Microscope-  Energy Dispersive X-Ray Spectroscopy (SEM-EDS). Hasil uji EIS menunjukkan    fraksi yang memiliki kemampuan sebagai inhibitor korosi terbaik pada suhu 30oC  yaitu F5, pada suhu 50 dan 70oC yaitu F1. Hasil mekanisme adsorpsi yang paling  baik yaitu menggunakan model Langmuir dengan reaksi berlangsung secara  spontan, adsorpsi terjadi secara kimia dan endotermik, serta entropi pada suhu  paling tinggi menunjukkan adsorpsi paling baik. Hasil analisis permukaan  menunjukkan F1 dan F2 paling baik dalam memproteksi baja lunak.    Kata kunci: Baja lunak, korosi CO2, inhibitor korosi, fraksi-fraksi oligomer 4-    vinilpiridin, mekanisme adsorpsi.        The 4-vinylpyridine oligomer used in this study was fractionated using Sephadex  LH-20 as the stationary phase and methanol as the mobile phase. The 4-  vinylpyridine oligomeric fractions were tested for their activities using the  Electrochemical Impedance Spectroscopy (EIS) method with varying  concentrations (0. 25, 50, 100 and 150 mg L-1    ) and varying temperatures (30, 50  and 70oC) as corrosion inhibitors on mild steel in CO2 corrosive medium. EIS  protection percent data was used to determine the adsorption mechanism using  four adsorption models, namely: Temkin, Langmuir, Frumkin and Flory-Huggins.  Mild steel surfaces were analyzed using Scanning Electron Microscope-Energy  Dispersive X-Ray Spectroscopy (SEM-EDS). The results of the fractionation  obtained 5 fractions. The EIS test results show the fraction that has ability as the  best corrosion inhibitor at temperature of 30oC, namely F5, at temperature of 50  and 70oC, namely F1. The best result of the adsorption mechanism is using the  Langmuir model with the reaction taking place spontaneously, adsorption occurs  chemically and endothermically, and the entropy at the highest temperature shows  the best adsorption. The result of surface analysis shows that F1 and F2 are the  best in protecting mild steel.    Kata kunci: Mild steel, CO2 corrosion, corrosion inhibitor, 4-vinylpyridine    oligomeric fractions, adsorption mechanism.
publisher: FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM
date: 2021
type: Skripsi
type: NonPeerReviewed
format: text
identifier: http://digilib.unila.ac.id/60652/1/ABSTRAK%20-%20tubagus%20sudirmano.pdf
format: text
identifier: http://digilib.unila.ac.id/60652/2/FULL%20SKRIPSI%20TANPA%20LAMPIRAN%20-%20tubagus%20sudirmano.pdf
format: text
identifier: http://digilib.unila.ac.id/60652/3/FULL%20SKRIPSI%20TANPA%20PEMBAHSAN%20DAN%20LAMPIRAN%20-%20tubagus%20sudirmano.pdf
identifier:   TB. SOFI SUDIRMANO, 1617011014  (2021) MEKANISME ADSORPSI INHIBITOR KOROSI OLIGOMER 4-VINILPIRIDIN PADA PERMUKAAN BAJA LUNAK DALAM MEDIUM KOROSIF CO2.  FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.     
relation: http://digilib.unila.ac.id/60652/