Oligomer 4-vinilpiridin yang digunakan pada penelitian ini telah difraksinasi
dengan menggunakan Sephadex LH-20 sebagai fase diam dan metanol sebagai
fase gerak. Fraksi-fraksi oligomer 4-vinilpiridin diuji aktivitasnya menggunakan
metode Electrochemical Impedance Spectroscopy (EIS) dengan konsentrasi
bervariasi (0, 25, 50, 100 dan 150 mg L-1

) dan suhu bervariasi (30, 50 dan 70oC)
sebagai inhibitor korosi pada baja lunak dalam medium korosif CO2. Data persen
proteksi EIS digunakan untuk menentukan mekanisme adsorpsi menggunakan
empat model adsorpsi, yaitu: Temkin, Langmuir, Frumkin dan Flory-Huggins.

Permukaan baja lunak dianalisis menggunakan Scanning Electron Microscope-
Energy Dispersive X-Ray Spectroscopy (SEM-EDS). Hasil uji EIS menunjukkan

fraksi yang memiliki kemampuan sebagai inhibitor korosi terbaik pada suhu 30oC
yaitu F5, pada suhu 50 dan 70oC yaitu F1. Hasil mekanisme adsorpsi yang paling
baik yaitu menggunakan model Langmuir dengan reaksi berlangsung secara
spontan, adsorpsi terjadi secara kimia dan endotermik, serta entropi pada suhu
paling tinggi menunjukkan adsorpsi paling baik. Hasil analisis permukaan
menunjukkan F1 dan F2 paling baik dalam memproteksi baja lunak.

Kata kunci: Baja lunak, korosi CO2, inhibitor korosi, fraksi-fraksi oligomer 4-

vinilpiridin, mekanisme adsorpsi.



The 4-vinylpyridine oligomer used in this study was fractionated using Sephadex
LH-20 as the stationary phase and methanol as the mobile phase. The 4-
vinylpyridine oligomeric fractions were tested for their activities using the
Electrochemical Impedance Spectroscopy (EIS) method with varying
concentrations (0. 25, 50, 100 and 150 mg L-1

) and varying temperatures (30, 50
and 70oC) as corrosion inhibitors on mild steel in CO2 corrosive medium. EIS
protection percent data was used to determine the adsorption mechanism using
four adsorption models, namely: Temkin, Langmuir, Frumkin and Flory-Huggins.
Mild steel surfaces were analyzed using Scanning Electron Microscope-Energy
Dispersive X-Ray Spectroscopy (SEM-EDS). The results of the fractionation
obtained 5 fractions. The EIS test results show the fraction that has ability as the
best corrosion inhibitor at temperature of 30oC, namely F5, at temperature of 50
and 70oC, namely F1. The best result of the adsorption mechanism is using the
Langmuir model with the reaction taking place spontaneously, adsorption occurs
chemically and endothermically, and the entropy at the highest temperature shows
the best adsorption. The result of surface analysis shows that F1 and F2 are the
best in protecting mild steel.

Kata kunci: Mild steel, CO2 corrosion, corrosion inhibitor, 4-vinylpyridine

oligomeric fractions, adsorption mechanism.