        abstract = {ABSTRAK

SINTESIS, KARAKTERISASI, DAN APLIKASI SENYAWA KOMPLEKS
BASA SCHIFF DARI 4-(DIMETILAMINO)BENZALDEHIDA DAN
ANILINA DENGAN KOMPLEKS Mn(II) SEBAGAI SENSITIZER PADA

DYE SENSITIZED SOLAR CELL (DSSC)

Oleh
MITA SEPTIANI

Telah dilakukan sintesis senyawa kompleks Mn(II) basa Schiff dari anilina dan
4-(dimetilamino)benzaldehida. Senyawa kompleks Mn(II) basa Schiff yang
diperoleh dikarakterisasi menggunakan spektrofotometer UV-Vis,
spektrofotometer IR, DTA-TG, SEM, dan MSB. Kompleks Mn(II) basa Schiff
hasil sintesis diaplikasikan sebagai sensitizer pada Dye Sensitized Solar Cell
(DSSC). Hasil sintesis diperoleh padatan kristalin berwarna coklat sebanyak
0,4681 gram dengan rendemen 76,7\%. Hasil karakterisasi menggunakan
spektrofotometer UV-Vis menunjukkan bahwa kompleks Mn(II) basa Schiff
mengalami pergeseran hipsokromik dari gugus azometina pada ligan basa Schiff
349 nm ke panjang gelombang 337 nm dengan transisi n{$\rightarrow$}{\ensuremath{\pi}}* dan munculnya
peak pada daerah 432 nm merupakan transisi orbital d pada logam Mn. Data
spektrum IR kompleks Mn(II) basa Schiff menunjukkan serapan ikatan koordinasi
(Mn-N) pada daerah bilangan gelombang 514 cm-1

. Analisis DTA-TG
menunjukkan adanya pengurangan massa sebanyak 6,621\% pada suhu 75-100?C
yang menunjukkan adanya pengotor dari pelarut (etanol), pada Suhu sekitar 120-
375?C dekomposisi ligan basa Schiff terjadi secara tiga tahap sebanyak 58,09\%,
dan pada suhu 375-430?C daerah ini sampel kehilangan air (ligan) sebanyak
5,059\%. Karakterisasi menggunakan SEM menunjukkan bahwa Kompleks Mn(II)
basa Schiff memiliki bentuk seperti bongkahan batu yang tersebar ukuran partikel
sekitar 10-30 {\ensuremath{\mu}}m. Karakterisasi MSB menunjukkan kompleks Mn(II) basa Schiff
memiliki momen magnet sebesar 5,24 BM. Pengujian DSSC menghasilkan
efisiensi (?) 0,1\% dengan tegangan 143,6 mV dan kuat arus 0,7 mA.
Kata Kunci: Kompleks Mn(II) basa Schiff, sensitizer, Dye Sensitized Solar Cell

(DSSC)

ABSTRACT

SYNTHESIS, CHARACTERIZATION, AND APPLICATION OF THE
SCHIFF BASE COMPLEX OF 4-(DIMETHYLAMINO)BENZALDEHYDE
AND ANYLINE WITH Mn(II) COMPLEX AS A DYE SENSITIZED

SOLAR CELL (DSSC)

By
MITA SEPTIANI

Synthesis of the Mn(II) complex of Schiff base compound from aniline and
4-(dimethylamino)benzaldehyde. The obtained Mn(II) complex of Schiff base
compounds were characterized using UV-Vis spectrophotometer, IR
spectrophotometer, DTA-TG, SEM, and MSB. The synthesized Mn(II) complex
of Schiff base was applied as a sensitizer in Dye Sensitized Solar Cell (DSSC).
The results of the synthesis obtained brown crystalline solids as much as 0.4681
grams with a yield of 76.7\%. The results of characterization using UV-Vis
spectrophotometer showed that the Mn(II) complex of Schiff base experienced a
hypochromic shift from the azomethine group on the Schiff base ligand at 349 nm
to a wavelength of 337 nm with transition n{$\rightarrow$}{\ensuremath{\pi}}* and the appearance of a peak in
the 432 nm region was a d orbital transition on Mn metal. The IR spectrum data
for the Mn(II) complex of Schiff base showed the absorption of the coordination
bond (Mn-N) in the wave number region of 514 cm-1. DTA-TG analysis showed
a mass reduction of 6.621\% at a temperature of 75-100?C which indicated the
presence of impurities from the solvent (ethanol), at a temperature of around 120-
375?C the decomposition of the Schiff base ligand occurred in three stages as
much as 58.09\%, and at a temperature of 375-430?C in this area the sample loses
water (ligand) as much as 5.059\%. Characterization using SEM showed that the
basic Mn(II) Complex of Schiff base had a rock-like shape with a particle size of
about 10-30 {\ensuremath{\mu}}m. MSB characterization showed that the Mn(II) complex of Schiff
base had a magnetic moment of 5.24 BM. The DSSC test resulted in an efficiency
(?) of 0.1\% with a voltage of 143.6 mV and a current of 0.7 mA.
Keywords: Mn(II) complex of Schiff base, sensitizer, Dye Sensitized Solar Cell
(DSSC)}
}