%0 Generic
%A Oleh  MITA SEPTIANI, 1717011070
%C UNIVERSITAS LAMPUNG
%D 2021
%F eprints:60959
%I FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM
%T SINTESIS, KARAKTERISASI, DAN APLIKASI SENYAWA KOMPLEKS  BASA SCHIFF DARI 4-(DIMETILAMINO)BENZALDEHIDA DAN  ANILINA DENGAN KOMPLEKS Mn(II) SEBAGAI SENSITIZER PADA    DYE SENSITIZED SOLAR CELL (DSSC)    (Skripsi)    
%U http://digilib.unila.ac.id/60959/
%X ABSTRAK    SINTESIS, KARAKTERISASI, DAN APLIKASI SENYAWA KOMPLEKS  BASA SCHIFF DARI 4-(DIMETILAMINO)BENZALDEHIDA DAN  ANILINA DENGAN KOMPLEKS Mn(II) SEBAGAI SENSITIZER PADA    DYE SENSITIZED SOLAR CELL (DSSC)    Oleh  MITA SEPTIANI    Telah dilakukan sintesis senyawa kompleks Mn(II) basa Schiff dari anilina dan  4-(dimetilamino)benzaldehida. Senyawa kompleks Mn(II) basa Schiff yang  diperoleh dikarakterisasi menggunakan spektrofotometer UV-Vis,  spektrofotometer IR, DTA-TG, SEM, dan MSB. Kompleks Mn(II) basa Schiff  hasil sintesis diaplikasikan sebagai sensitizer pada Dye Sensitized Solar Cell  (DSSC). Hasil sintesis diperoleh padatan kristalin berwarna coklat sebanyak  0,4681 gram dengan rendemen 76,7%. Hasil karakterisasi menggunakan  spektrofotometer UV-Vis menunjukkan bahwa kompleks Mn(II) basa Schiff  mengalami pergeseran hipsokromik dari gugus azometina pada ligan basa Schiff  349 nm ke panjang gelombang 337 nm dengan transisi n→π* dan munculnya  peak pada daerah 432 nm merupakan transisi orbital d pada logam Mn. Data  spektrum IR kompleks Mn(II) basa Schiff menunjukkan serapan ikatan koordinasi  (Mn-N) pada daerah bilangan gelombang 514 cm-1    . Analisis DTA-TG  menunjukkan adanya pengurangan massa sebanyak 6,621% pada suhu 75-100°C  yang menunjukkan adanya pengotor dari pelarut (etanol), pada Suhu sekitar 120-  375°C dekomposisi ligan basa Schiff terjadi secara tiga tahap sebanyak 58,09%,  dan pada suhu 375-430°C daerah ini sampel kehilangan air (ligan) sebanyak  5,059%. Karakterisasi menggunakan SEM menunjukkan bahwa Kompleks Mn(II)  basa Schiff memiliki bentuk seperti bongkahan batu yang tersebar ukuran partikel  sekitar 10-30 μm. Karakterisasi MSB menunjukkan kompleks Mn(II) basa Schiff  memiliki momen magnet sebesar 5,24 BM. Pengujian DSSC menghasilkan  efisiensi (ƞ) 0,1% dengan tegangan 143,6 mV dan kuat arus 0,7 mA.  Kata Kunci: Kompleks Mn(II) basa Schiff, sensitizer, Dye Sensitized Solar Cell    (DSSC)    ABSTRACT    SYNTHESIS, CHARACTERIZATION, AND APPLICATION OF THE  SCHIFF BASE COMPLEX OF 4-(DIMETHYLAMINO)BENZALDEHYDE  AND ANYLINE WITH Mn(II) COMPLEX AS A DYE SENSITIZED    SOLAR CELL (DSSC)    By  MITA SEPTIANI    Synthesis of the Mn(II) complex of Schiff base compound from aniline and  4-(dimethylamino)benzaldehyde. The obtained Mn(II) complex of Schiff base  compounds were characterized using UV-Vis spectrophotometer, IR  spectrophotometer, DTA-TG, SEM, and MSB. The synthesized Mn(II) complex  of Schiff base was applied as a sensitizer in Dye Sensitized Solar Cell (DSSC).  The results of the synthesis obtained brown crystalline solids as much as 0.4681  grams with a yield of 76.7%. The results of characterization using UV-Vis  spectrophotometer showed that the Mn(II) complex of Schiff base experienced a  hypochromic shift from the azomethine group on the Schiff base ligand at 349 nm  to a wavelength of 337 nm with transition n→π* and the appearance of a peak in  the 432 nm region was a d orbital transition on Mn metal. The IR spectrum data  for the Mn(II) complex of Schiff base showed the absorption of the coordination  bond (Mn-N) in the wave number region of 514 cm-1. DTA-TG analysis showed  a mass reduction of 6.621% at a temperature of 75-100°C which indicated the  presence of impurities from the solvent (ethanol), at a temperature of around 120-  375°C the decomposition of the Schiff base ligand occurred in three stages as  much as 58.09%, and at a temperature of 375-430°C in this area the sample loses  water (ligand) as much as 5.059%. Characterization using SEM showed that the  basic Mn(II) Complex of Schiff base had a rock-like shape with a particle size of  about 10-30 μm. MSB characterization showed that the Mn(II) complex of Schiff  base had a magnetic moment of 5.24 BM. The DSSC test resulted in an efficiency  (ƞ) of 0.1% with a voltage of 143.6 mV and a current of 0.7 mA.  Keywords: Mn(II) complex of Schiff base, sensitizer, Dye Sensitized Solar Cell  (DSSC)