title: SINTESIS, KARAKTERISASI, DAN APLIKASI KOMPLEKS  KOBALT(II) DENGAN LIGAN 1,10- FENANTROLIN SEBAGAI DYE  SENSITIZER PADA DYE SENSITIZED SOLAR CELL (DSSC)
creator: AURA DHAYANG FIARIZKY, 1717011064
subject: 540 Kimia dan ilmu yang berhubungan
description: ABSTRAK    SINTESIS, KARAKTERISASI, DAN APLIKASI KOMPLEKS  KOBALT(II) DENGAN LIGAN 1,10- FENANTROLIN SEBAGAI DYE  SENSITIZER PADA DYE SENSITIZED SOLAR CELL (DSSC)    Oleh    AURA DHAYANG FIARIZKY    Telah dilakukan sintesis senyawa kompleks dengan ion logam Co(II) dan ligan  1,10- Fenantrolin dengan perbandingan konsentrasi 1:3. Senyawa kompleks Co(II)  Fenantrolin hasil sintesis dikarakterisasi menggunakan MSB untuk mengetahui  nilai momen magnet, spektrofotometer UV-Vis untuk mengetahui pergeseran  panjang gelombang, spektrofotometer FTIR untuk mengetahui gugus fungsi khas,  analisis DTA-TGA untuk mengetahui formula dan dekomposisi senyawa, dan  analisis SEM untuk mengetahui bentuk morfologi kristal senyawa kompleks.  Senyawa kompleks Co(II) Fenantrolin hasil sintesis diaplikasikan sebagai dye  sensitizer pada DSSC. Dari hasil sintesis diperoleh kristal kompleks Co(II)  Fenantrolin berwarna oranye dengan berat 0,552 gram dan rendemen 72,6%.  Analisis menggunakan MSB menunjukkan momen magnet kompleks Co(II)  Fenantrolin sebesar 4,720 BM. Data spektrum spektrofotometer UV-Vis  menunjukkan senyawa kompleks Co(II) Fenantrolin mengalami pergeseran  batokromik yang ditandai dengan bergesernya senyawa pembentuknya 228 nm ke  panjang gelombang 267 nm dengan transisi n→π*. Data Spektrum FTIR senyawa  kompleks Co(II) Fenantrolin menunjukkan adanya serapan khas senyawa kompleks  (M-N) pada bilangan gelombang 420,48 cm-1    . Analisis dekomposisi termal  menunjukkan terjadi dekomposisi massa 5 molekul H2O pada rentang suhu 50-  100°C sebanyak 12,11%; pada rentang suhu 120-405°C terjadi dekomposisi massa  ligan fen sebanyak 45,38%. Analisis morfologi menunjukkan senyawa kompleks  Co(II) Fenantrolin memiliki bentuk tongkat seperti poros dengan tambahan bentuk  prisma (prism-like). Hasil pengujian DSSC diperoleh nilai efisiensi sebesar 0,398%  dengan tegangan 398,7 mV dan kuat arus sebesar 1,0 mA.    Kata Kunci :Kobalt, Fenantrolin, 1,10- Fenantrolin, sensitizer, Dye Sensitizer Solar  Cell(DSSC)    ABSTRACT    SYNTHESIS, CHARACTERIZATION, AND APLICATION OF  COBALT(II) COMPLEX WITH 1,10- PHENANTROLINE LIGAND AS A  DYE SENSITIZER IN DYE SENSITIZED SOLAR CELL (DSSC)    By    AURA DHAYANG FIARIZKY    Synthesis of complex compound with metal ion Co(II) and ligand 1,10-  Phenanthroline has been carried out with a concentration ratio of 1:3. The  synthesized Co(II) phenanthroline complex compound was characterized using  MSB to determine the value of the magnetic moment, UV-Vis spectrophotometer  to determine the wavelength shift, FTIR spectrophotometer to determine typical  functional groups, DTA-TGA analysis to determine the formula and decomposition  of the compound, and SEM analysis to determine the crystal morphology of  complex compounds. The synthesized Co(II) Phenanthroline complex was applied  as a dye sensitizer in DSSC. From the results of the synthesis, it was obtained that  the crystal complex of Co(II) Fenanthroline was orange with a weight of 0.552  grams and a yield of 72.6%. Analysis using MSB showed that the magnetic moment  of the phenanthroline Co(II) complex was 4.720 BM. Spectrophotometer UV-Vis  spectrophotometer data showed that the complex compound Co(II) phenanthroline  underwent a bathochromic shift which was indicated by the shift of its constituent  compound from 228 nm to a wavelength of 267 nm with a transition of n→π*. Data  on the FTIR spectrum of the phenanthroline Co(II) complex compound showed a    typical absorption of the complex compound (MN) at a wave number of 420.48 cm-  1    . Thermal decomposition analysis showed that there was a mass decomposition of  5 Hmolecules2Oin the temperature range of 50-100°C as much as 12.11%; in the  temperature range of 120-405°C the fen ligand mass decomposition was 45.38%.    Morphological analysis showed that the Co(II) phenanthroline complex had a rod-  like shape with an additionalshapeprism-like. DSSC test results obtained an    efficiency value of 0.398% with a voltage of 398.7 mV and a current of 1.0 mA.    Key Words :Cobalt, Phenantroline, 1,10- Phenantroline, sensitizer, Dye Sensitizer  Solar Cell(DSSC)
publisher: FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM
date: 2021
type: Skripsi
type: NonPeerReviewed
format: text
identifier: http://digilib.unila.ac.id/60966/1/ABSTRAK%20-%20Aura%20Dhayang%20Fiarizky.pdf
format: text
identifier: http://digilib.unila.ac.id/60966/2/SKRIPSI%20FULL%20-%20Aura%20Dhayang%20Fiarizky.pdf
format: text
identifier: http://digilib.unila.ac.id/60966/3/SKRIPSI%20TANPA%20BAB%20PEMBAHASAN%20-%20Aura%20Dhayang%20Fiarizky.pdf
identifier:   AURA DHAYANG FIARIZKY, 1717011064  (2021) SINTESIS, KARAKTERISASI, DAN APLIKASI KOMPLEKS KOBALT(II) DENGAN LIGAN 1,10- FENANTROLIN SEBAGAI DYE SENSITIZER PADA DYE SENSITIZED SOLAR CELL (DSSC).  FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.     
relation: http://digilib.unila.ac.id/60966/