@misc{eprints61189,
           title = {PENGARUH SUHU KALSINASI ZEOLIT-X
TERHADAP KARAKTERISTIK LIQUID FUEL
HASIL PIROLISIS MINYAK KELAPA SAWIT},
          author = {1617011045 Yosefin Tiurma R Tampubolon},
         address = {UNIVERSITAS LAMPUNG},
       publisher = {FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM},
            year = {2021},
             url = {http://digilib.unila.ac.id/61189/},
        abstract = {Dalam penelitian ini telah dilakukan pengolahan minyak kelapa sawit
menjadi liquid fuel sebagai bahan bakar alternatif dengan metode pirolisis
menggunakan katalis zeolit-X, dengan tujuan untuk mempelajari pengaruh suhu
kalsinasi zeolit-X terhadap karakteristik liquid fuel. Zeolit-X diperoleh melalui
sintesis silika sekam padi dan aluminium foil food grade dengan metode sol-gel dan
hidrotermal pada suhu 100 ?C selama 96 jam, kemudian dikalsinasi pada suhu yang
berbeda, yakni 550, 650, 750, dan 850 ?C selama 6 jam. Zeolit-X hasil sintesis
dikaraktersiasi menggunakan XRD dan SEM yang menunjukkan bahwa zeolit-X
berhasil disintesis dan suhu kalsinasi 550 ?C merupakan kondisi terbaik.
Selanjutnya, dilakukan uji aktivitas katalitik zeolit-X dalam proses pirolisis dengan
minyak kelapa sawit.
Proses pirolisis dilakukan dengan komposisi minyak kelapa sawit dan
katalis zeolit-X masing-masing variasi suhu kalsinasi, yakni 20 : 1 (v/m). Produk
pirolisis (liquid fuel) kemudian dianalisis menggunakan GC-MS. Hasil analisis
GC-MS menunjukkan bahwa hidrokarbon merupakan komponen utama liquid fuel
dengan persentase relatif 76-87 \%. Komponen lain yang terkandung dalam liquid
fuel yaitu asam karboksilat (10-19\%), keton (0,6-1,7\%), dan alkohol (1,4-2,0).
Liquid fuel hasil pirolisis minyak kelapa sawit dengan katalis zeolit-X suhu
kalsinasi 850 ?C mengandung hidrokarbon tertinggi, yaitu 87,91\% dan mengandung
fraksi gasoline tertinggi, yaitu 54,27\%.

Kata kunci: liquid fuel, minyak kelapa sawit, pirolisis, silika sekam padi, zeolit-X
In this research, palm oil processing has been carried out into liquid fuel as
an alternative fuel by pyrolysis method using zeolite-X as the catalyst. Zeolite-X
was obtained through silica synthesis of rice husk and food-grade aluminum foil by
sol-gel and hydrothermal method at 100 ?C for 96 hours, then calcined at different
temperatures, 550, 650, 750, and 850 ?C for 6 hours. The various synthesized
zeolite-X was then characterized using both XRD and SEM instruments. The
characterization proved that zeolite-X calcined at 550?C was the best result.
Furthermore, the zeolite-X obtained is used on the pyrolysis of palm oil.
The pyrolysis of palm oil is examined with the various calcined zeolite-X
catalysts to palm oil of 20: 1 (v/m). The liquid fuel produced was analyzed using
GC-MS. The results of the GC-MS analysis showed that the main component of
liquid fuel is a hydrocarbon containing 76-87\%. Other components detected in the
liquid fuel are carboxylic acids (10-19\%), ketones (0.6-1.7\%), and alcohol (1.4-
2.0\%). Liquid fuel produced by pyrolysis using a zeolite-X catalyst calcined at 850
?C has the highest fraction of the hydrocarbon and gasoline 87.91, 54.27\%,
respectively.
Keywords: liquid fuel, palm oil, pyrolysis, rice husk silica, zeolite-X}
}