title: ANALISIS GLASS-CERAMICS DARI BATUAN BASALT
LAMPUNG TIMUR SEBAGAI MATERIAL FILLER KOMPOSIT
HIDROKSIAPATIT (HAp)
ispublished: pub
subjects: 620
subjects: 670
full_text_status: restricted
abstract: Glass-ceramics merupakan material polikristalin berbutir halus yang
dihasilkan oleh kristalisasi terkontrol pada fasa glass. Memiliki
karaktesitik sebagai material biokeramik yang tahan terhadap bahan kimia
maupun cairan tubuh, tidak terkorosi, dan sifat mekanik unggul. Material
yang terus dikembangkan menjadi glass-ceramics adalah basalt.
Pembuatan glass-ceramics diawali pembentukan glass melalui proses
melting temperatur 1.200
o
C selama 1 jam dilanjutkan pembentukan
nukleasi temperatur 600
o
C selama 2 jam, dan proses kristalisasi pada
temperatur 850, 950, 1.050
o
C selama 3 dan 8 Jam. Pembuatan komposit
HAp – glass-ceramics dilakukan dengan komposisi 5, 10, 15%
glass-ceramics berukuran < 44 μm. Sebagai binder ditambahkan 25%
Polilatic acid (PLA) dengan pelarut Methilene Chloride (MC).
Hasil analisis thermal menunjukkan bahwa basalt memungkinkan
pembentukan glass secara homogen yang ditandai dengan prameter Trg
kurang dari 2/3. Selain itu, parameter penting terdiri dari temperatur
transisi glass (Tg) 425
o
C, temperatur awal kristalisasi (Tx) 725
o
C, dan
titik lebur basalt ( Tm) 1.200
o
C. Komposisi kimia basalt dominan
48,418% SiO2, 18,82% Al2O3, 12,593% Fe2O3, 9,761% CaO, 4,561%
MgO, dan 3,356% Na2O. Digram TAS (Na2O+K2O - SiO2) menunjukkan
bahwa basalt merupakan tipe basalt subalkaline. Tekstur kristalin
glass-ceramics yang halus dan seragam dipengaruhi oleh rasio FeO/Fe3O4
kurang dari 0,85. Rasio CaO/MgO dan CaO/NaO (2,5 dan 10)
mengindikasikan bahwa kristalisasi terjadi pada temperatur rendah. Fasa
yang terbentuk yaitu anorthite, olivine dominan fayalite, dan pyroxene.
Kekerasan sebesar 637 hingga 837 HV1N dengan densitas antara 1,9
hingga 2,9 g/cm
3
. Sebagai filler penguat komposit, glass-ceramics
memberikan kenaikan kekerasan 125% dari material HAp dan 57% dari
komposit HAp - PLA.
Kata kunci: basalt, glass-ceramics, kristalisasi, biokeramik, komposit
ABSTRACT

Glass-ceramics were fine-grained polycrystalline material produced
by controlled crystallization in the glass phase. It has characteristics as a
bioceramic such as resistant to chemicals and body fluids,
corrosion-resistant, and superior mechanical properties. Material that
continues to be developed into glass-ceramics is basalt.
The glass-ceramic manufacturing begins with ordering the glass
through a melting process at 1,200
o
C for 1hrs. Nucleation at 600
o
C for
2hrs, and a crystallization process at 850, 950, 1,050
o
C for 3 and 8 hrs.
HAp-glass-ceramics composites were prepared with composition of 5, 10,
15% glass-ceramics. As a binder, 25% Polylactic acid (PLA) was added
with Methylene Chloride (MC) as a solvent.
The analysis results show the basalt supports a glass homogeneously,
indicated the Trg less than 2/3. The essential parameters include glass
transition temperature (Tg) 425
o
C, initial crystallization temperature (Tx)
725
o
C, and basalt melting point (Tm) 1,200
o
C. The chemical
composition of the dominant basalt is 48.418% SiO2, 18.82% Al2O3,
12.593% Fe2O3, 9.761% CaO, 4.561% MgO, and 3.356% Na2O. TAS
diagrams (Na2O + K2O - SiO2) showed that basalt is a sub alkaline type
of basalt. The crystalline texture of glass-ceramics is smooth and uniform
with a FeO / Fe3O4 ratio of less than 0.85. The CaO / MgO and CaO /
NaO ratios (2.5 and 10) indicate that crystallization occurs at low
temperatures. The phases formed are anorthite, olivine, and pyroxene.
The hardness are 637 - 837 HV1N with density between 1.9 to 2.9 g/cm
3
.
As a reinforcing composite filler, glass ceramics provide a 125% increase
in hardness over HAp materials and 57% over HAp - PLA composites.
Keywords: basalt, glass-ceramics, crystallization, bioceramics,
composites
date: 2021
date_type: published
institution: Universitas Lampung
department: FAKULTAS TEKNIK
thesis_type: masters
citation:   YUSUP HENDRONURSITO, 1925021004  (2021) ANALISIS GLASS-CERAMICS DARI BATUAN BASALT LAMPUNG TIMUR SEBAGAI MATERIAL FILLER KOMPOSIT HIDROKSIAPATIT (HAp).  Masters thesis, Universitas Lampung.   
document_url: http://digilib.unila.ac.id/61223/1/ABSTRAK2%20-%20Yusup%20Hendronursito.pdf
document_url: http://digilib.unila.ac.id/61223/3/TESIS%20FULL-dikompresi%20-%20Yusup%20Hendronursito.pdf
document_url: http://digilib.unila.ac.id/61223/2/TESIS%20TANPA%20BAB%20PEMBAHASAN-dikompresi%20-%20Yusup%20Hendronursito.pdf