creators_name: Ganjar Widyatmoko, 0715021046 creators_id: anjar_n46@yahoo.com type: other datestamp: 2014-12-29 04:38:09 lastmod: 2014-12-29 04:38:09 metadata_visibility: show title: PENGARUH VARIASI VOLTASE PROSES ANODISASI PADA PADUAN ALUMINIUM ADC12 TERHADAP KEKASARAN PERMUKAAN DAN KANDUNGAN FASA ispublished: pub subjects: General full_text_status: restricted abstract: Dalam pembuatan berbagai bentuk komponen mesin saat ini sudah bukan merupakan suatu hal yang sulit, namun untuk menyempurnakan performa dari suatu material terutama ketahanan terhadap korosi dan memperindah tampilan tanpa mengesampingkan performa dari suatu material diperlukan proses yang sesuai sehingga diperoleh komponen yang tahan lama. Dalam perbaikan performa material, khususnya aluminium dan paduannya, anodisasi adalah salah satu proses yang banyak digunakan untuk mencapai tujuan tersebut.. Anodisasi itu sendiri adalah proses pembentukan lapisan oksida pada logam dengan cara mereaksikan logam terutama aluminium dengan oksigen (O2) dari larutan elektolit. Penelitian ini menggunakan paduan aluminium ADC12 sebagai logam induk yang akan dilapisi dan asam phospat (H3PO4) sebagai elektrolitnya. Pada logam induk dilakukan anodisasi dengan menggunakan variasi tegangan yaitu 9 volt, 12 volt dan 15 volt dengan kuat arus listrik sebesar 0,2 ampere dan waktu proses anodisasi dilakukan selama 25 menit. Pengujian yang dilakukan meliputi pengujian kekasaran dan kandungan fasa lapisan. Dari hasil pengujian diperoleh bahwa nilai rata- rata tertinggi untuk pengujian kekasaran diperoleh pada tegangan 12 volt yaitu sebesar 0,6756 µm dan untuk nilai rata-rata terendah untuk pengujian kekasaran diperoleh pada tegangan 15 volt yaitu sebesar 0,4044 µm. Anodisasi menyebabkan terjadinya perubahan fasa pada permukaan paduan aluminium ADC12. Persentase kandungan fasa yang dihasilkan dalam proses anodisasi paduan aluminium yang menggunakan tegangan masing-masing 9 volt, 12 volt dan 15 volt yang dianodisasi selama 25 menit yaitu Al (76,868 %, 71,223 % dan 88,03 %), AlP (19,678 %, 22,9746 % dan 11,551 %) dan AlN (3,454 %, 5,802 % dan 0,419 %). Kata kunci : Variasi Voltase, Anodisasi, Paduan Aluminium ADC12, Kekasaran, Kandungan Fasa It is not a difficult thing to make all machinery components today. However but to perfect performance from a particular material, especially corrosion proof, and to beautify appearance without sacrificing its performance, a particular proper process is required to produce durable components. In improving performance, especially aluminum and its alloy, anodizing is a process to obtain the aforementioned objectives. Anodizing is a process to form oxide coating at metal by making reaction of the metal, especially the aluminum, with oxygen (O2) with electrolyte solution. This research used aluminum alloy ADC12 as the main metal to coat and phosphate acid (H3PO4) as its electrolyte. Anodizing was applied to the main metal by using varying voltages of 9 volt, 12 volt, and 25 volt with 0.2 Ampere currency strength and 25 minutes duration of anodizing procces. Anodized metal were tested with surface roughness test and phase content coating test. The research results showed that average higher value for surface roughness test obtained at 12 volt was 0.6756 µm and average lowest value obtained at 15 volt was 0.4044 µm. Anodizing caused phase changes at surface of aluminum alloy ADC12. Percentage of phase content produced in anodizing process at aluminum alloy by using 9 volt, 12 volt, and 15 volt during 25 minute were respectively A1 (76.868%, 71.223% and 88.03%), AlP (19.678%, 22.9746% and 11.551%) and AlN (3.454%, 5.802% and 0.419%). Keywords : voltage variation, anodizing, aluminum alloy ADC12, roughness, content phase. date: 2014-12-18 date_type: published publisher: FA TEKNIK place_of_pub: UNIVERSITAS LAMPUNG institution: Universitas Lampung department: FT thesis_type: other citation: Ganjar Widyatmoko, 0715021046 (2014) PENGARUH VARIASI VOLTASE PROSES ANODISASI PADA PADUAN ALUMINIUM ADC12 TERHADAP KEKASARAN PERMUKAAN DAN KANDUNGAN FASA. FA TEKNIK , UNIVERSITAS LAMPUNG. document_url: http://digilib.unila.ac.id/6189/1/1.%20ABSTRAK.pdf document_url: http://digilib.unila.ac.id/6189/2/2.%20ABSTRACT%20INGGRIS.pdf document_url: http://digilib.unila.ac.id/6189/3/3.%20COVER%20DALAM.pdf document_url: http://digilib.unila.ac.id/6189/4/4.%20HLM.%20PERSETUJUAN.pdf document_url: http://digilib.unila.ac.id/6189/5/5.%20HLM.%20PENGESAHAN.pdf document_url: http://digilib.unila.ac.id/6189/6/6.%20PERNYATAAN.pdf document_url: http://digilib.unila.ac.id/6189/7/7.%20RIWAYAT%20HIDUP.pdf document_url: http://digilib.unila.ac.id/6189/8/8.%20PERSEMBAHAN.pdf document_url: http://digilib.unila.ac.id/6189/9/9.%20MOTTO.pdf document_url: http://digilib.unila.ac.id/6189/10/10.%20SANWACANA.pdf document_url: http://digilib.unila.ac.id/6189/11/11.%20DAFTAR%20ISI.pdf document_url: http://digilib.unila.ac.id/6189/12/12.%20DAFTAR%20TABEL.pdf document_url: http://digilib.unila.ac.id/6189/13/13.%20DAFTAR%20LAMPIRAN.pdf document_url: http://digilib.unila.ac.id/6189/14/14.%20DAFTAR%20GAMBAR.pdf document_url: http://digilib.unila.ac.id/6189/15/15%2C%20BAB%201.pdf document_url: http://digilib.unila.ac.id/6189/16/16.%20BAB%202.pdf document_url: http://digilib.unila.ac.id/6189/17/17.%20BAB%203.pdf document_url: http://digilib.unila.ac.id/6189/18/18.%20BAB%204.pdf document_url: http://digilib.unila.ac.id/6189/19/19.%20BAB%205.pdf document_url: http://digilib.unila.ac.id/6189/20/20.%20DAFTAR%20PUSTAKA.pdf