N2  - Telah dilakukan penelitian pengaruh variasi konsentrasi asam sitrat terhadap
karakteristik silika daun bambu dengan metode leaching. Varaisi konsentrasi asam
sitrat yang digunakan pada penelitian ini yaitu 0, 1, 3, 5, 7, dan 10% massa larutan
dengan pengkodean sampel DBAS0, DBAS1, DBAS3, DBAS5, DBAS7, dan
DBAS10. Adapun metode yang digunakan untuk mengekstraksi silika daun bambu
adalah metode leaching dan dilanjutkan dengan proses kalsinasi. Penelitian ini
bertujuan untuk mengetahui pengaruh konsentrasi asam sitrat terhadap karakteristik
silika daun bambu. Hasil analisis TGA sampel DBAS0 dan DBAS10, diperoleh
penyusutan massa sampel berturut yaitu 51,98 dan 50,05%, sedangkan analisis
DTA menunjukkan terdapat puncak endoterm masng-masing sampel pada 1027,75
oC dan 1028,57 oC yang mengindikasikan perubahan fase silika amorf. Analisis
XRF menunjukkan kemurnian tertinggi diperoleh pada sampel DBAS10 yaitu
93,94 %. Analisis XRD menunjukkan bahwa fase yang terbentuk dari semua
sampel adalah fase amorf dengan puncak lengkung pada 2? = 15 ? 30 O
. Hasil
FTIR menunjukkan gugus fungsi utama yang terbentuk adalah ?OH, Si-O-Si dan
Si-O. Hasil analisis SEM pada sampel DBAS0 dan DBAS10 menujukkan bahwa
mikrostruktur yang terbentuk dari silika daun bambu adalah gumpalan (algomerat)
dengan diameter rata-rata berturut-turut 3,048 dan 3,435 ?m.
Research has been carried out on the effect of variations in concentration citric acid
on the silica characteristics of bamboo leaves using the leaching method. Variations
of citric acid concentration used in this study were 0, 1, 3, 5, 7, and 10% by mass
with sample coding DBAS0, DBAS1, DBAS3, DBAS5, DBAS7, and DBAS10.
The method used to extract silica from bamboo leaves is the leaching method and
followed by the calcination process. This study aims to determine the effect of citric
acid concentration on the silica characteristics of bamboo leaves. The results of the
TGA analysis of samples DBAS0 and DBAS10, the sample mass shrinkage was
51.98 and 50.05%, while the DTA analysis showed that there were endothermic
peaks for each sample at 1027.75 oC and 1028.57 oC which indicated a phase change
of amorphous silica. XRF analysis showed that the highest purity was obtained in
the DBAS10 sample, which was 93.94%. XRD analysis showed that the phase
formed from all samples was an amorphous phase with a curved peak at 2? = 15 ?
30 o
. The FTIR results showed that the main functional groups formed were ?OH,
Si-O-Si and Si-O. The results of SEM analysis on samples DBAS0 and DBAS10
showed that the microstructure formed from bamboo leaf silica was an algomerate
with an average diameter of 3,048 and 3,435 m, respectively.