        abstract = {Penelitian ini dilakukan untuk menganalisis pengaruh variasi pH larutan acid zinc
pada sistem sel volta dua kompartemen dengan elektrode Cu(Ag)-Zn terhadap nilai
karakteristik elektrik dan laju korosi yang dihasilkan. Pasangan Cu(Ag)-Zn
digunakan untuk menghasilkan tegangan dan arus dalam sel dengan elektrolit air
laut dan larutan acid zinc. Dua kompartemen dibatasi dengan jembatan garam yang
terbuat dari campuran Al2O3 (aluminium oksida) 1 mol dan NaCl (air laut) 1 mol
yang terlarut dalam semen putih Tiga Roda. Sel volta terdiri dari 5 sel yang disusun
secara seri untuk tiap variasi pH dengan nilai 4, 5 dan 6. Pada setiap sel terisi dengan
{$\pm$} 250ml air laut (bagian katoda) dan {$\pm$} 200 ml larutan acid zinc (bagian anoda). Sel
volta diukur dengan multitester setiap 1 jam sekali selama 3 hari (72 jam).
Berdasarkan penelitian yang telah dilakukan diperoleh kesimpulan bahwa dengan
penggunaan elektrolit larutan acid zinc yang memiliki nilai pH lebih rendah akan
meningkatkan nilai karakteristik elektik serta meningkatkan laju korosi yang
dihasilkan sel volta.
Kata Kunci: Jembatan garam, karakteristik elektrik, larutan acid zinc, sel volta
This research was conducted to analyze the effect of variations in pH of acid zinc
solution in a two-compartment voltaic cell system with Cu(Ag)-Zn electrodes on the
value of electrical characteristics and the resulting corrosion rate. The Cu(Ag)-Zn
pair is used to generate voltage and current in the cell with seawater electrolyte
and zinc acid solution. The two compartments are lined with salt bridge made from
mixture of 1 mole of Al2O3 (aluminum oxide) and 1 mole of NaCl (sea water)
dissolved in ?tiga roda? white cement. The voltaic cell consisted of 5 cells arranged
in series for each pH variation with values of 4, 5 and 6. Each cell is filled with {$\pm$}
250 ml of seawater (cathode part) and {$\pm$} 200 ml of acid zinc solution (anode part).
Cell voltaic was measured with a multitester every 1 hour for 3 days (72 hours).
Based on the research that has been done, it can be concluded that by using an acid
zinc electrolyte solution which has a lower pH value, it will increase the value of
the electrical characteristics and increase the corrosion rate produced by voltaic
cell.
Kata Kunci: Salt bridge, electrical characteristics, acid zinc solution, voltaic cell}
}