?url_ver=Z39.88-2004&rft_val_fmt=info%3Aofi%2Ffmt%3Akev%3Amtx%3Adc&rft.title=STUDI+KEKUATAN+ADHESI+SERAT+DAUN+NANAS+TERHADAP+MATRIK%0D%0A%0D%0APOLYESTER+DENGAN+PENGUJIAN+DEBONDING&rft.creator=M+ILHAM+HAMBALI%2C+1515021019&rft.subject=600+Teknologi+(ilmu+terapan)&rft.subject=620+Ilmu+teknik+dan+ilmu+yang+berkaitan&rft.description=Natural+fibers+are+able+to+reduce+sound%2C+temperature+insulation%2C+have+low+density+and%0D%0Ahigh+mechanical+ability+so+they+can+meet+industrial+needs.+Pineapple+leaf+fiber%0D%0Acomposite+speciments+wede+made+by+chemical+treatment+of+NaOH+0%25%2C+3%25%2C+5%25%2C+and%0D%0A7%25.+The+fiber+is+2mm+in+diameter%2C+the+fiber+is+placed+in+a+mold+which+is+then+inserted%0D%0Ainto+the+polyester+resin+matrix.+Then+the+composite+material+was+cured+at+75+%C2%B0C+for+2%0D%0Ahours%2C+then+the+material+was+introduced+to+a+lathe+machine+to+form+a+v-notch.+The%0D%0Adebonding+test+performed+by+the+tensile+test+method+where+the+test+results+showed+that%0D%0Athe+specimen+with+7%25+NaOH+fiber+treatment+had+the+highest+average+tensile+strength%0D%0Aof+4.96+MPa+and+3%25+NaOH+treatment+had+the+lowest+average+tensile+strength+of+3.44%0D%0AMPa.%0D%0A%0D%0AKeywords%3A+Composite%2C+natural+fiber%2C+pineapple+leaf+fiber%2C+debonding%2C+matrix%0D%0Acracking%2C+fiber+pull-out%2C+fiber+breaking.%0D%0A%0D%0A1%0D%0A%0D%0AABSTRAK%0D%0A%0D%0ASTUDI+KEKUATAN+ADHESI+SERAT+DAUN+NANAS+TERHADAP+MATRIK%0D%0A%0D%0APOLYESTER+DENGAN+PENGUJIAN+DEBONDING%0D%0A%0D%0AOleh%0D%0AM+ILHAM+HAMBALI%0D%0A%0D%0ASerat+alam+mampu+meredam+suara%2C+isolasi+temperatur%2C+memiliki+densitas+rendah+dan%0D%0Akemampuan+mekanik+tinggi+sehingga+dapat+memenuhi+kebutuhan+industri.+Pembuatan%0D%0Aspesimen+komposit+serat+daun+nanas+dilakukan+dengan+perlakuan+kimia+NaOH+sebesar%0D%0A0%25%2C+3%25%2C+5%25%2C+dan+7%25.+Serat+di+berdiameter+2+mm%2C+serat+kemudian+diletakan+di+cetakan%0D%0Ayang+kemudian+di+masukan+matriks+resin+polyster.+Material+komposit+di+curing+dengan%0D%0Atemperatur+75+%C2%B0C+selama+2+jam%2C+dan+material+di+bubut+untuk+membentuk+v-notch.%0D%0APengujian+debonding+dilakukan+dengan+metode+uji+tarik+dimana+hasil+pengujian%0D%0Amenunjukan+spesimen+dengan+perlakuan+serat+NaOH+7%25+memiliki+kekuatan+tarik+rata%0D%0A%E2%80%93+rata+paling+tinggi+sebesar+4%2C96+MPa+dan+perlakuan+NaOH+3%25+memiliki+kekuatan+tarik%0D%0Arata+-+rata+terendah+sebesar+3.44+MPa.%0D%0A%0D%0AKata+kunci%3A+Komposit%2C+serat+alam%2C+komposit+serat+daun+nanas%2C+uji+debonding%0D%0Akomposit.&rft.publisher=Fakultas+Teknik&rft.date=2021-12-10&rft.type=Skripsi&rft.type=NonPeerReviewed&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F62369%2F1%2FABSTRACT%2520-%2520M%2520ilham%2520hambali.pdf&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F62369%2F2%2FFULL%2520SKRIPSI%2520Tanpa%2520Lampiran%2520ISI%2520-%2520M%2520ilham%2520hambali.pdf&rft.format=text&rft.identifier=http%3A%2F%2Fdigilib.unila.ac.id%2F62369%2F3%2FFULL%2520SKRIPSI%2520Tanpa%2520Lampiran%2520Bab%2520Pembahasan%2520-%2520M%2520ilham%2520hambali.pdf&rft.identifier=++M+ILHAM+HAMBALI%2C+1515021019++(2021)+STUDI+KEKUATAN+ADHESI+SERAT+DAUN+NANAS+TERHADAP+MATRIK+POLYESTER+DENGAN+PENGUJIAN+DEBONDING.++Fakultas+Teknik%2C+UNIVERSITAS+LAMPUNG.+++++&rft.relation=http%3A%2F%2Fdigilib.unila.ac.id%2F62369%2F