<> "The repository administrator has not yet configured an RDF license."^^ . <> . . "STUDI KEKUATAN ADHESI SERAT DAUN NANAS TERHADAP MATRIK\r\n\r\nPOLYESTER DENGAN PENGUJIAN DEBONDING"^^ . "Natural fibers are able to reduce sound, temperature insulation, have low density and\r\nhigh mechanical ability so they can meet industrial needs. Pineapple leaf fiber\r\ncomposite speciments wede made by chemical treatment of NaOH 0%, 3%, 5%, and\r\n7%. The fiber is 2mm in diameter, the fiber is placed in a mold which is then inserted\r\ninto the polyester resin matrix. Then the composite material was cured at 75 °C for 2\r\nhours, then the material was introduced to a lathe machine to form a v-notch. The\r\ndebonding test performed by the tensile test method where the test results showed that\r\nthe specimen with 7% NaOH fiber treatment had the highest average tensile strength\r\nof 4.96 MPa and 3% NaOH treatment had the lowest average tensile strength of 3.44\r\nMPa.\r\n\r\nKeywords: Composite, natural fiber, pineapple leaf fiber, debonding, matrix\r\ncracking, fiber pull-out, fiber breaking.\r\n\r\n1\r\n\r\nABSTRAK\r\n\r\nSTUDI KEKUATAN ADHESI SERAT DAUN NANAS TERHADAP MATRIK\r\n\r\nPOLYESTER DENGAN PENGUJIAN DEBONDING\r\n\r\nOleh\r\nM ILHAM HAMBALI\r\n\r\nSerat alam mampu meredam suara, isolasi temperatur, memiliki densitas rendah dan\r\nkemampuan mekanik tinggi sehingga dapat memenuhi kebutuhan industri. Pembuatan\r\nspesimen komposit serat daun nanas dilakukan dengan perlakuan kimia NaOH sebesar\r\n0%, 3%, 5%, dan 7%. Serat di berdiameter 2 mm, serat kemudian diletakan di cetakan\r\nyang kemudian di masukan matriks resin polyster. Material komposit di curing dengan\r\ntemperatur 75 °C selama 2 jam, dan material di bubut untuk membentuk v-notch.\r\nPengujian debonding dilakukan dengan metode uji tarik dimana hasil pengujian\r\nmenunjukan spesimen dengan perlakuan serat NaOH 7% memiliki kekuatan tarik rata\r\n– rata paling tinggi sebesar 4,96 MPa dan perlakuan NaOH 3% memiliki kekuatan tarik\r\nrata - rata terendah sebesar 3.44 MPa.\r\n\r\nKata kunci: Komposit, serat alam, komposit serat daun nanas, uji debonding\r\nkomposit."^^ . "2021-12-10" . . . . . "Fakultas Teknik"^^ . . . . . . . "1515021019"^^ . "M ILHAM HAMBALI"^^ . "1515021019 M ILHAM HAMBALI"^^ . . . . . . "STUDI KEKUATAN ADHESI SERAT DAUN NANAS TERHADAP MATRIK\r\n\r\nPOLYESTER DENGAN PENGUJIAN DEBONDING (File PDF)"^^ . . . "ABSTRACT - M ilham hambali.pdf"^^ . . . "STUDI KEKUATAN ADHESI SERAT DAUN NANAS TERHADAP MATRIK\r\n\r\nPOLYESTER DENGAN PENGUJIAN DEBONDING (File PDF)"^^ . . . "STUDI KEKUATAN ADHESI SERAT DAUN NANAS TERHADAP MATRIK\r\n\r\nPOLYESTER DENGAN PENGUJIAN DEBONDING (File PDF)"^^ . . . "FULL SKRIPSI Tanpa Lampiran Bab Pembahasan - M ilham hambali.pdf"^^ . . . "STUDI KEKUATAN ADHESI SERAT DAUN NANAS TERHADAP MATRIK\r\n\r\nPOLYESTER DENGAN PENGUJIAN DEBONDING (Other)"^^ . . . . . . "indexcodes.txt"^^ . . . "STUDI KEKUATAN ADHESI SERAT DAUN NANAS TERHADAP MATRIK\r\n\r\nPOLYESTER DENGAN PENGUJIAN DEBONDING (Other)"^^ . . . . . . "STUDI KEKUATAN ADHESI SERAT DAUN NANAS TERHADAP MATRIK\r\n\r\nPOLYESTER DENGAN PENGUJIAN DEBONDING (Other)"^^ . . . . . . "indexcodes.txt"^^ . . . "STUDI KEKUATAN ADHESI SERAT DAUN NANAS TERHADAP MATRIK\r\n\r\nPOLYESTER DENGAN PENGUJIAN DEBONDING (Other)"^^ . . . . . . "lightbox.jpg"^^ . . . "STUDI KEKUATAN ADHESI SERAT DAUN NANAS TERHADAP MATRIK\r\n\r\nPOLYESTER DENGAN PENGUJIAN DEBONDING (Other)"^^ . . . . . . "preview.jpg"^^ . . . "STUDI KEKUATAN ADHESI SERAT DAUN NANAS TERHADAP MATRIK\r\n\r\nPOLYESTER DENGAN PENGUJIAN DEBONDING (Other)"^^ . . . . . . "medium.jpg"^^ . . . "STUDI KEKUATAN ADHESI SERAT DAUN NANAS TERHADAP MATRIK\r\n\r\nPOLYESTER DENGAN PENGUJIAN DEBONDING (Other)"^^ . . . . . . "small.jpg"^^ . . . "STUDI KEKUATAN ADHESI SERAT DAUN NANAS TERHADAP MATRIK\r\n\r\nPOLYESTER DENGAN PENGUJIAN DEBONDING (Other)"^^ . . . . . . "STUDI KEKUATAN ADHESI SERAT DAUN NANAS TERHADAP MATRIK\r\n\r\nPOLYESTER DENGAN PENGUJIAN DEBONDING (Other)"^^ . . . . . . "STUDI KEKUATAN ADHESI SERAT DAUN NANAS TERHADAP MATRIK\r\n\r\nPOLYESTER DENGAN PENGUJIAN DEBONDING (Other)"^^ . . . . . . "STUDI KEKUATAN ADHESI SERAT DAUN NANAS TERHADAP MATRIK\r\n\r\nPOLYESTER DENGAN PENGUJIAN DEBONDING (Other)"^^ . . . . . . "STUDI KEKUATAN ADHESI SERAT DAUN NANAS TERHADAP MATRIK\r\n\r\nPOLYESTER DENGAN PENGUJIAN DEBONDING (Other)"^^ . . . . . . "lightbox.jpg"^^ . . . "STUDI KEKUATAN ADHESI SERAT DAUN NANAS TERHADAP MATRIK\r\n\r\nPOLYESTER DENGAN PENGUJIAN DEBONDING (Other)"^^ . . . . . . "preview.jpg"^^ . . . "STUDI KEKUATAN ADHESI SERAT DAUN NANAS TERHADAP MATRIK\r\n\r\nPOLYESTER DENGAN PENGUJIAN DEBONDING (Other)"^^ . . . . . . "medium.jpg"^^ . . . "STUDI KEKUATAN ADHESI SERAT DAUN NANAS TERHADAP MATRIK\r\n\r\nPOLYESTER DENGAN PENGUJIAN DEBONDING (Other)"^^ . . . . . . "small.jpg"^^ . . "HTML Summary of #62369 \n\nSTUDI KEKUATAN ADHESI SERAT DAUN NANAS TERHADAP MATRIK \n \nPOLYESTER DENGAN PENGUJIAN DEBONDING\n\n" . "text/html" . . . "600 Teknologi (ilmu terapan)" . . . "620 Ilmu teknik dan ilmu yang berkaitan" . .