title: PENGARUH WAKTU SINTERING TERHADAP PEMBENTUKAN FASE  SUPERKONDUKTOR BPSCCO-2212 PADA KADAR Ca = 1.10  MENGGUNAKAN METODE PENCAMPURAN BASAH
creator: Retno Asih, 1417041068
subject: 530 Fisika
description: Penelitian ini dilakukan untuk mengetahui pengaruh waktu sintering terhadap  pembentukan fase superkonduktor BPSCCO-2212 pada kadar Ca 1,10 dengan  menghitung tingkat kemurnian fase yang terbentuk dan melihat struktur mikronya.  Variasi waktu sintering yang digunakan adalah 10, 20, 30 dan 40 jam  menggunakan metode pencampuran basah. Sampel dikalsinasi pada suhu 800 °C  selama 10 jam dan disintering pada suhu 830 °C. Hasil karakterisasi XRD  menunjukkan fraksi volume tertingginya diperoleh pada sampel BPSCCO/40jam    sebesar 86,72%.. Sedangkan, fraksi volume terendah adalah BPSCCO-  2212/30jam sebesar 53,07%. Hasil uji SEM menunjukkan bahwa struktur mikro    bahan BPSCCO-2212 belum terorientasi dan masih banyak void ( ruang kosong  antar lempengan) berdasarkan hasil derajat orientasi yang dihasilkan dengan nilai  tertinggi diperoleh pada sampel BPSCCO-2212/30jam yaitu sebesar 13,59%,  sedangkan derajat orientasi terendah diperoleh pada BPSCCO-2212/20jam yaitu  sebesar 7,67.  Kata kunci: Superkonduktor BPSCCO-2212, waktu sintering, fraksi volume, dan    derajat orientasi.  This research was conducted to determined the effect of sintering time to phase  formation of superconducting BPSCCO-2212 with Ca content 1,10 by calculating  the level of purity of the phases formed and looking at the microstructure. The  variation of sintering time were 10, 20, 30 and 40 hours using wet mixing method.  The sample were calcinated with 800 °C for 10 hours and sintered at temperature  830 °C. The XRD’s characterization result showed highest volume fraction  obtainted in BPSCCO-2212/40 hours was 86,72% while, the lowest volume  fraction of BPSCCO-2212/30 hours was 53,07%. The relative high orientation  degree of BPSCCO-2212/30 hours was 13,59% and while the lowest orientation  degree of BPSCCO-2212/20 hours is 7,67%. The SEM’s characterization result  shows that all samples have not been oriented and there are still many voids  (empety space between the plates) based on the results of the degree of orientation  produced with the highest value obtained in the sample BPSCCO-2212/30hours    which is 13.59%, while the lowest degree of orientation is obtained at BPSCCO-  2212/20hours which is equal to 7.67.    Keywords: Degree of orientation, sintering time, superconductors BPSCCO-2212,  and volume fraction
publisher: FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM
date: 2021
type: Skripsi
type: NonPeerReviewed
format: text
identifier: http://digilib.unila.ac.id/62654/1/ABSTRAK%20-%20retno%20assih.pdf
format: text
identifier: http://digilib.unila.ac.id/62654/2/SKRIPSI%20FULL%20-%20retno%20assih.pdf
format: text
identifier: http://digilib.unila.ac.id/62654/3/SKRIPSI%20TANPA%20BAB%20PEMBAHASAN%20-%20retno%20assih.pdf
identifier:   Retno Asih, 1417041068  (2021) PENGARUH WAKTU SINTERING TERHADAP PEMBENTUKAN FASE SUPERKONDUKTOR BPSCCO-2212 PADA KADAR Ca = 1.10 MENGGUNAKAN METODE PENCAMPURAN BASAH.  FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM, UNIVERSITAS LAMPUNG.     
relation: http://digilib.unila.ac.id/62654/