A1  -  SYLVIA DEWI ANGGRAENI, 1715011081
Y1  - 2022/04/21/
N2  - Self compacting concrete (SCC) adalah suatu inovasi beton yang dilakukan untuk
mengatasi permasalahan pada saat pengecoran yang tidak memerlukan pemadatan
manual meskipun pada tempat-tempat yang sulit dijangkau seperti pada tulangan
rapat. Pada penelitian ini menggunakan serat baja 3D Dramix dan kawat bendrat
sebagai campuran dalam SCC dengan volume fraksi 0%, 0,5%, 1%, 1,5%.
Penambahan serat ini bertujuan untuk mengetahui pengaruh kedua serat tersebut
pada SCC terhadap kuat tekan, kuat tarik belah dan kuat tarik lentur. Sampel
penelitian ini adalah silinder dengan diameter 150 mm dan tinggi 300 mm untuk
pengujian kuat tekan dan kuat tarik belah sedangkang kuat tarik lentur
menggunakan sampel balok dengan ukuran 100x100x400 mm. Semua sampel
benda uji ini dilakukan pengujian saat beton berumur 28 hari. Peningkatan nilai
kuat tekan, kuat tarik belah dan kuat lentur pada penambahan serat baja 1,5%
berturut-turut adalah 26,39%, 64,71% dan 111,88% terhadap beton dengan 0%
serat. Sedangkan peningkatan nilai kuat tekan, kuat tarik belah dan kuat lentur
pada penambahan kawat bendrat 1,5% berturut-turut adalah 20,31%, 60,74% dan
76,18% terhadap beton dengan 0% serat.
Kata Kunci: Self Compacting Concrete, SCC, Kawat Bendrat, Serat Baja

Self compacting concrete (SCC) is a concrete innovation that is carried out to
overcome problems during casting that does not require manual compaction even
in hard-to-reach places such as tight reinforcement. In this study, 3D Dramix
steel fibers and bendrat wire were used as a mixture in SCC with volume fractions
of 0%, 0.5%, 1%, 1.5%. The addition of this fiber aims to determine the effect of
the two fibers on SCC on compressive strength, split tensile strength and flexural
tensile strength. The sample in this study was a cylinder with a diameter of 150
mm and a height of 300 mm for testing the compressive strength and split tensile
strength while the flexural tensile strength used a beam sample with a size of
100x100x400 mm. All samples of these specimens were tested when the concrete
was 28 days old. The increase in the value of compressive strength, split tensile
strength and flexural strength at the addition of 1.5% steel fiber were 26.39%,
64.71% and 111.88% respectively for concrete with 0% fiber. While the increase
in compressive strength, split tensile strength and flexural strength with the
addition of 1.5% bendrat wire was 20.31%, 60.74% and 76.18% for concrete with
0% fiber, respectively.
Keyword:Self Compacting Concrete, SCC, Bendrat Wire, Steel Fiber
PB  - FAKULTAS TEKNIK
TI  - ANALISIS PERBANDINGAN PENGARUH CAMPURAN KAWAT
BENDRAT DAN SERAT BAJA PADA SELF COMPACTING CONCRETE
(SCC)