title: KUAT TEKAN BETON MUTU TINGGI DENGAN MEMANFAATKAN FLY ASH DAN SILICA FUME SEBAGAI BAHAN PENGISI
ispublished: pub
subjects: 620
full_text_status: restricted
abstract: Mengingat limbah sisa hasil pembakaran batu bara (fly ash) meningkat setiap 
tahunnya dan dapat menyebabkan dampak lingkungan yang cukup membahayakan 
terutama pada polusi udara dalam kehidupan sekitar, maka perlu dilakukan 
pemanfaatan fly ash sebagai bahan campuran beton. Dalam penelitian ini, penulis 
akan melakukan pemanfaatan fly ash sebagai bahan pengganti sebagian semen dan 
silica fume sebagai bahan tambah untuk meningkatkan waktu setting time. Variasi 
fly ash yang digunakan adalah 0%, 5%, 10%, dan 15% dari berat total semen dan 
variasi silica fume yang digunakan adalah 5% dan 10% dengan waktu pengujian 
beton berumur 28 hari dan 60 hari serta ditambahkan superplasticizer sebesar 0,5% 
dari berat semen. Berdasarkan analisis data penelitian, didapatkan bahwa terjadi 
peningkatan kuat tekan beton antara beton yang memiliki kandungan fly ash dan 
silica fume terhadap beton tanpa kandungan fly ash dan silica fume. Kuat tekan 
beton terbesar terjadi pada penambahan fly ash sebesar 15% dan silica fume 5% 
dengan nilai kuat tekan pada umur 28 hari sebesar 41,48 MPa dan pada umur 60 
hari sebesar 47,03 MPa. Hal ini menunjukan bahwa kadar fly ash 15% dan kadar 
silica fume 5% adalah kadar optimum penambahan fly ash dan silica fume untuk 
umur beton 28 hari dan 60 hari. 
Kata Kunci : fly ash, kuat tekan, silica fume
Considering that the waste from burning coal (fly ash) increases every year and 
can cause quite dangerous environmental impacts, especially on air pollution in 
surrounding life, it is necessary to use fly ash as a concrete mixture. In this study, 
the author will use fly ash as a partial replacement for cement and silica fume as 
an added material to increase the setting time. Variations of fly ash used were 0%, 
5%, 10%, and 15% of the total weight of cement and variations of silica fume used 
were 5% and 10% with a test time of 28 days and 60 days of concrete and added a 
superplasticizer of 0, 5% by weight of cement. Based on the analysis of research 
data, it was found that there was an increase in the compressive strength of concrete 
between concrete containing fly ash and silica fume to concrete without fly ash and 
silica fume. The greatest compressive strength of concrete occurred in the addition 
of 15% fly ash and 5% silica fume with a compressive strength value of 41.48 MPa 
at the age of 28 days and 47.03 MPa at the age of 60 days. This shows that the fly 
ash content of 15% and the silica fume content of 5% are the optimum levels of 
addition of fly ash and silica fume for the concrete age of 28 days and 60 days.
Key words : fly ash, compressive strength, silica fume
date: 2022-09-05
date_type: published
publisher: FAKULTAS TEKNIK
place_of_pub: UNIVERSITAS LAMPUNG
id_number: 1815011048
citation:   Rivaldo Hartono Putra, 1815011048  (2022) KUAT TEKAN BETON MUTU TINGGI DENGAN MEMANFAATKAN FLY ASH DAN SILICA FUME SEBAGAI BAHAN PENGISI.  FAKULTAS TEKNIK, UNIVERSITAS LAMPUNG.     
document_url: http://digilib.unila.ac.id/65979/1/ABSTRAK%20%28ABSTRACT%29.pdf
document_url: http://digilib.unila.ac.id/65979/2/SKRIPSI%20FULL.pdf
document_url: http://digilib.unila.ac.id/65979/3/SKRIPSI%20TANPA%20BAB%20PEMBAHASAN.pdf